Assignee: Mobil Oil AS
•
Filing: 1982-05-27
•
Granted: 1983-11-15
•
Expires: 2002-05-27
Abstract
Abstract A method is provided for effectively tailoring the catalytic activity of porous crystalline zeolites. The method involves loading all channels of a cationic form of the porous zeolite with molten wax, contacting the wax-loaded zeolite with hydrogen fluoride solution in a controlled manner, and calcining the hydrogen fluoride solution contacted zeolite.
Inventors
- 👤 George T. Kokotailo
- 👤 Albert C. Rohrman, Jr.
- 👤 Stephen Sawruk
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 13:18
CPC Classifications
B; B01; B01J; B01J29/00; B01J29/04; B01J29/06; B01J29/40; B01J2229/00; B01J2229/30; B01J2229/40; B01J2229/42; Y; Y10; Y10S; Y10S423/00; Y10S423/22; Y10S423/23; Y10S423/29; Y10S423/33
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
109 words
A method for altering catalytic activity of the cationic form of a porous crystalline zeolite which comprises the sequential steps of loading all pores and channels of said zeolite with a paraffinic wax, contacting the wax loaded zeolite with an aqueous hydrogen fluoride solution of from about 0.005 Normal to about 0.5 Normal at a temperature of from about 20° C. to about 35° C. and a pressure of from about atmospheric to about 40 psig for a contact time of from about 1 hour to about 10 hours, and calcining the hydrogen fluoride solution contacted zeolite at a temperature of from about 200° C. to about 600° C.
Claim 2
Independent Claim
109 words
A method for altering catalytic activity of the cationic form of a porous crystalline zeolite which comprises the sequential steps of loading all pores and channels of said zeolite with a paraffinic wax, contacting the wax loaded zeolite with an aqueous hydrogen fluoride solution of from about 0.005 Normal to about 0.5 Normal at a temperature of from about 20° C. to about 35° C. and a pressure of from about atmospheric to about 40 psig for a contact time of from about 1 hour to about 10 hours, and calcining the hydrogen fluoride solution contacted zeolite at a temperature of from about 200° C. to about 600° C.
Claim 3
Dependent Claim
61 words
The method of claim 1 wherein said wax loading is accomplished by contacting said zeolite with molten paraffinic wax under conditions sufficient to maintain the wax in the molten state and to effectively block all pores and channels of said zeolite, and then cooling said wax loaded zeolite sufficiently to solidify the wax within all pores and channels of said zeolite.
Claim 4
Dependent Claim
20 words
The method of claim 1 wherein said crystalline zeolite is characterized by a silica/alumina mole ratio of at least 12.
Claim 5
Dependent Claim
24 words
The method of claim 3 wherein said cystalline zeolite is selected from the group consisting of ZSM-5, ZSM-11, ZSM-12, ZSM-23 ZSM-35, ZSM-38 and ZSM-48.
Claim 6
Dependent Claim
11 words
The method of claim 4 wherein said crystalline zeolite is ZSM-5.
Claim 7
Dependent Claim
23 words
The method of claim 1 wherein said wax is a paraffinic hydrocarbon of from about 20 carbon atoms to about 35 carbon atoms.
Claim 8
Dependent Claim
39 words
The method of claim 1 which includes the further steps of ion exchanging the calcined hydrogen fluoride solution contacted zeolite and thereafter calcining the ion exchanged zeolite at a temperature of from about 200° C. to about 600° C.
Claim 9
Independent Claim
156 words
A method for altering catalytic activity of the cationic form of a porous crystalline zeolite characterized as having a structure which provides constrained access to and egress from the intracrystalline free space by virtue of having a pore dimension greater than about 5 Angstroms and pore windows of about a size such as would be provided by 10-membered rings of oxygen atoms, which comprises the sequential steps of loading the pores and channels of said zeolite with a paraffinic wax, contacting the wax loaded zeolite with an aqueous hydrogen fluoride solution of from about 0.005 Normal to about 0.5 Normal at a temperature of from about 20° C. to about 35° C. and a pressure of from about atmospheric to about 40 psig for a contact time of from about 1 hour to about 10 hours, and calcining the hydrogen fluoride solution contacted zeolite at a temperature of from about 200° C. to about 600° C.
Claim 10
Independent Claim
156 words
A method for altering catalytic activity of the cationic form of a porous crystalline zeolite characterized as having a structure which provides constrained access to and egress from the intracrystalline free space by virtue of having a pore dimension greater than about 5 Angstroms and pore windows of about a size such as would be provided by 10-membered rings of oxygen atoms, which comprises the sequential steps of loading the pores and channels of said zeolite with a paraffinic wax, contacting the wax loaded zeolite with an aqueous hydrogen fluoride solution of from about 0.005 Normal to about 0.5 Normal at a temperature of from about 20° C. to about 35° C. and a pressure of from about atmospheric to about 40 psig for a contact time of from about 1 hour to about 10 hours, and calcining the hydrogen fluoride solution contacted zeolite at a temperature of from about 200° C. to about 600° C.
Claim 11
Independent Claim
130 words
A method for altering catalytic activity of the cationic form of a porous crystalline zeolite characterized by a Constraint Index of from about 1 to about 12 and a silica/alumina mole ratio of at least 12, whch comprises the sequential steps of loading the pores and channels of said zeolite with a paraffinic wax, contacting the wax loaded zeolite with an aqueous hydrogen fluoride solution of from about 0.005 Normal to about 0.5 Normal at a temperature of from about 20° C. to about 35° C. and a pressure of from about atmospheric to about 40 psig for a contact time of from about 1 hour to about 10 hours, and calcining the hydrogen fluoride solution contacted zeolite at a temperature of from about 200° C. to about 600° C.
Claim 12
Independent Claim
130 words
A method for altering catalytic activity of the cationic form of a porous crystalline zeolite characterized by a Constraint Index of from about 1 to about 12 and a silica/alumina mole ratio of at least 12, whch comprises the sequential steps of loading the pores and channels of said zeolite with a paraffinic wax, contacting the wax loaded zeolite with an aqueous hydrogen fluoride solution of from about 0.005 Normal to about 0.5 Normal at a temperature of from about 20° C. to about 35° C. and a pressure of from about atmospheric to about 40 psig for a contact time of from about 1 hour to about 10 hours, and calcining the hydrogen fluoride solution contacted zeolite at a temperature of from about 200° C. to about 600° C.
References Cited (Backward Citations)
US3437587A
Cited
US3630965A
Cited
US3702886A
Cited
US3702312A
Cited
US4054511A
Cited
US4088605A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-11-14 | 1987-05-16 | 1987-11-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-11-14 | 1991-05-16 | 1991-11-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-11-14 | 1995-05-16 | 1995-11-15 | $7700.00 | Window Closed / Lapsed |