US4414302A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making a lead storage battery and lead storage battery made according to this method
Assignee: Accumulatorenfabrik Sonnenschein GmbH
•
Filing: 1981-10-28
•
Granted: 1983-11-08
•
Expires: 2001-10-28
Abstract
Abstract This invention is related to a method of making a lead storage battery with a thixotropic gel as electrolyte consisting substantially of a sulphuric acid and a gelling agent. The object is to provide a lead storage battery which is maintenance free, leak-proof and of a long cycle life while permitting filling of the electrolyte independently of the plate dimensions including the superficial extent of the plate. To achieve this object: (a) the sulphuric acid is electrochemically bonded in the active material of the electrodes; and (b) the gel forming electrolyte is filled into the battery in the form of a gelling agent and a sulphuric acid concentration which is insufficient for the formation of a gel, but which is sufficient for initiating a charging process upon application of a charging voltage. During the charging process the sulfuric acid that is bonded to the electrodes, together with the gel forming electrolyte, will start the formation of the gel.
Inventors
- 👤 Otto Jache
- 👤 Heinz Schroeder
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 19:44
CPC Classifications
H; H01; H01M; H01M10/00; H01M10/06; H01M10/12; H01M10/08; H01M10/10; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
84 words
A method of making a lead storage battery with a thixotropic gel electrolyte consisting substantially of sulphuric acid and a gelling agent, and characterized in (a) that sulphuric acid is electrochemically bonded in the active material of the electrodes in the battery, and (b) that the battery thereafter is filled with a gelling agent and a sulphuric acid the concentration of which is insufficient for the formation of a gel, but which is sufficient for initiating a charging process upon application of a voltage.
Claim 2
Independent Claim
84 words
A method of making a lead storage battery with a thixotropic gel electrolyte consisting substantially of sulphuric acid and a gelling agent, and characterized in (a) that sulphuric acid is electrochemically bonded in the active material of the electrodes in the battery, and (b) that the battery thereafter is filled with a gelling agent and a sulphuric acid the concentration of which is insufficient for the formation of a gel, but which is sufficient for initiating a charging process upon application of a voltage.
Claim 3
Dependent Claim
72 words
A method according to claim 1, characterized in that the electrochemical bonding of sulphuric acid occurs in the pores of the active material of the battery electrodes, and is effected by discharging the lead storage battery while it is filled with a liquid sulphuric acid electrolyte, and that subsequently the residual liquid electrolyte, which is not bonded in the pores of the active material of the electrodes, is removed from the battery.
Claim 4
Dependent Claim
28 words
A method according to claim 2, characterised in that the residual electrolyte is washed from the discharged electrodes and subsequently the electrodes are dried in a non-oxidising manner.
Claim 5
Dependent Claim
37 words
A method according to claim 2, characterised in that the residual liquid electrolyte, after its removal from the battery, is mixed with a gelling agent and subsequently is returned to the battery as the gel forming electrolyte.
Claim 6
Dependent Claim
90 words
A method according to claim 4, characterised in that after the filling the battery with the gel forming electrolyte a charging voltage is applied to the electrodes so that the electrochemically bonded sulphuric acid will be released from the active material of the electrodes and together with the sulphuric acid contained in the gel forming electrolyte will result in a working electrolyte having a sulphuric acid concentration which corresponds to a predetermined working acid density, and which after being supplied with a predetermined electrical charge will progressively form a gel.
Claim 7
Independent Claim
73 words
A method according to any one of claims 1 to 3, characterised in that to the gel forming electrolyte there is added phosphoric acid, for example orthophosphoric acid in an amount of from 0.5 to 15% by weight, based on the sulphuric acid contained in the working electrolyte in its charged condition, so that about 20 to 50 mg of orthophosphoric acid will result per each gram of active material of the electrodes.
Claim 8
Dependent Claim
105 words
A lead storage battery with a thixotropic gel electrolyte, which consists substantially of sulphuric acid and a gelling agent, made in accordance with the method claimed in claim 5, characterised by (a) a partial electrochemical bonding of a liquid electrolyte in the pores of the active material of the electrodes, in which the weight ratio of the acid bonded as a sulphate in said active material, to the residual free acid remaining in the liquid electrolyte after said discharging of the battery, is between 1:1 and 50:1, and (b) said gelling agent in the finished working electrolyte amounts to about 3 to 15% by weight.
Claim 9
Dependent Claim
21 words
A lead storage battery according to claim 7, characterised in that finely dispersed silicon dioxide is used as the gelling agent.
Claim 10
Dependent Claim
48 words
A lead storage battery according to claim 8, characterized in that the silicon dioxide has a particle size of 0.002 to 0.1 μm, preferably of 0.01 to 0.02 μm, and a specific surface of 20 to 500 m 2 /g, preferably of 100 to 300 m 2 /g.
Claim 11
Dependent Claim
53 words
A lead storage battery according to any one of the claims 7 to 9, characterised in that the active material is applied to electrode substrates consisting of high-purity lead, dispersion-hardened lead, or of antimony-free lead alloys including lead-hardening substances such as selected from the group consisting of calcium, cadmium, and alkaline earth metals.
References Cited (Backward Citations)
US1634850A
Cited
US3172782A
Cited
US3457112A
Cited
US3305396A
Cited
US3556860A
Cited
US3711332A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-11-07 | 1987-05-09 | 1987-11-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-11-07 | 1991-05-09 | 1991-11-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-11-07 | 1995-05-09 | 1995-11-08 | $7700.00 | Window Closed / Lapsed |