US4414124A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of producing barium-ferrite series powder
Assignee: Toshiba Corp
•
Filing: 1981-04-03
•
Granted: 1983-11-08
•
Expires: 2001-04-03
Abstract
Abstract Barium-ferrite series powders are prepared from an alkaline aqueous solution containing a prescribed ratio of ions of the metals equal to those contained in the powder. In the first stage, the alkaline aqueous solution is heated at a constant volume at 150° to 300° C. to precipitate a precursor of the barium-ferrite series powder. Then, the precursor is baked at 700° to 1,000° C. to crystallize the precursor.
Inventors
- 👤 Hiroshi Endo
- 👤 Masashi Awa
- 👤 Shigeo Iiri
- 👤 Toshihiko Oguchi
- 👤 Isao Suzuki
- 👤 Naoyuki Hirate
- 👤 Masaru Hayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 13:34
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/032; H01F1/10; H01F1/11; C; C01; C01G; C01G49/00; C01G49/0018; C01G49/0036; C01G49/0063; C01G49/0072; C01G49/009; C04; C04B; C04B35/00; C04B35/01; C04B35/26; C04B35/2683; C01P; C01P2002/00; C01P2002/50; C01P2002/52; C01P2004/00; C01P2004/01; C01P2004/03; C01P2004/20; C01P2004/22; C01P2004/51; C01P2004/54; C01P2004/60; C01P2004/62; C01P2006/00; C01P2006/42
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
195 words
A method of producing barium-ferrite series microcrystalline powders having a general formula: BaO.n(Fe.sub.1-m M.sub.m).sub.2 O.sub.3 where M is at least one substituent component selected from the group consisting of Co, Ti, Ni, Mn, Cu, Zn, In, Ge and Nb, m is 0 to 0.2, and n is 5.4 to 6.0, comprising: providing an alkaline aqueous solution having an alkalinity of at least 0.01 N and containing barium ions, iron (III) ions and, optionally ions of the substituent component M dissolved therein in amounts sufficient to provide a molar ratio of 1:2n(1-m):2nm in the crystalline powder of said formula by adding a first aqueous solution to a second aqueous solution of an alkali, said first aqueous solution being prepared in advance by dissolving the water-soluble compounds of barium, iron (III) and optionally substituent component M in water; heating said alkaline aqueous solution at 150° to 300° C. at a constant volume, thereby precipitating a precursor of said crystalline powder, said precursor substantially bearing regular hexagonal plate-shaped crystal contour; and baking said precursor at 700° to 1,000° C. to completely crystallize the precursor, thereby obtaining the crystalline powder having a particle size of 0.5 μm or less.
Claim 2
Independent Claim
195 words
A method of producing barium-ferrite series microcrystalline powders having a general formula: BaO.n(Fe.sub.1-m M.sub.m).sub.2 O.sub.3 where M is at least one substituent component selected from the group consisting of Co, Ti, Ni, Mn, Cu, Zn, In, Ge and Nb, m is 0 to 0.2, and n is 5.4 to 6.0, comprising: providing an alkaline aqueous solution having an alkalinity of at least 0.01 N and containing barium ions, iron (III) ions and, optionally ions of the substituent component M dissolved therein in amounts sufficient to provide a molar ratio of 1:2n(1-m):2nm in the crystalline powder of said formula by adding a first aqueous solution to a second aqueous solution of an alkali, said first aqueous solution being prepared in advance by dissolving the water-soluble compounds of barium, iron (III) and optionally substituent component M in water; heating said alkaline aqueous solution at 150° to 300° C. at a constant volume, thereby precipitating a precursor of said crystalline powder, said precursor substantially bearing regular hexagonal plate-shaped crystal contour; and baking said precursor at 700° to 1,000° C. to completely crystallize the precursor, thereby obtaining the crystalline powder having a particle size of 0.5 μm or less.
Claim 3
Dependent Claim
33 words
The method according to claim 1, wherein the barium ions, iron (III) ions and ions of the substituent component M are provided by water-soluble compounds of barium, iron (III) and substituent component M.
Claim 4
Dependent Claim
25 words
The method according to claim 2, wherein the water-soluble compounds are selected from the group consisting of nitrates, perchlorates, chlorates, chlorides, fluorides, acetates and sulfates.
Claim 5
Dependent Claim
19 words
The method according to claim 1, wherein the alkalinity of the aqueous solution is provided by a strong alkali.
Claim 6
Dependent Claim
24 words
The method according to claim 4, wherein the strong alkali is selected from the group consisting of sodium hydroxide, potassium hydroxide and lithium hydroxide.
Claim 7
Dependent Claim
28 words
The method according to claim 1, wherein the first aqueous solution is cooled to 20° C. or less and, then, added to the aqueous solution of the alkali.
Claim 8
Dependent Claim
22 words
The method according to claim 1, 4 or 6, wherein the alkaline aqueous solution has an alkalinity of 1 to 6 N.
Claim 9
Dependent Claim
15 words
The method according to claim 7, wherein the normality N ranges between 3 and 6.
Claim 10
Dependent Claim
25 words
The method according to claim 1, wherein the heating of the alkaline aqueous solution falls within the range of between 180° C. and 250° C.
Claim 11
Dependent Claim
18 words
The method according to claim 1 or 9, wherein the alkaline aqueous solution is heated in an autoclave.
Claim 12
Dependent Claim
21 words
The method according to claim 1, wherein the baking temperature is within the range of between 850° C. and 950° C.
Claim 13
Dependent Claim
19 words
The method according to claim 1 or 11, wherein the precursor particles are kept floated in the baking step.
Claim 14
Dependent Claim
22 words
The method according to claim 12, wherein the precursor is baked in a rotary kiln or baking furnace of fluidized bed type.
References Cited (Backward Citations)
US3634254A
Cited
US4025449A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-11-07 | 1987-05-09 | 1987-11-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-11-07 | 1991-05-09 | 1991-11-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-11-07 | 1995-05-09 | 1995-11-08 | $7700.00 | Window Closed / Lapsed |