Method for production of colored aluminum article
Assignee: Nippon Light Metal Co Ltd
•
Filing: 1981-03-23
•
Granted: 1983-11-08
•
Expires: 2001-03-23
Abstract
Abstract The invention comprises an improved method for producing anodized aluminum articles colored by means of optical interference effects. The method comprises the steps of subjecting an aluminum article that has been anodized by conventional process to a treatment for modifying the pore structure of the anodic film, thereafter subjecting it while connected as anode to an electrolytic treatment for modifying the barrier layer between the oxide and the metal substrate and finally coloring the article while connected as cathode in an electrolyic bath containing one or more dissolved metal salts using DC current on which is superimposed a train of positive current pulses.
Inventors
- 👤 Kohichi Yoshida
- 👤 Teruo Miyashita
- 👤 Yasuo Oka
- 👤 Takashi Kajiyama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 19:20
CPC Classifications
C; C25; C25D; C25D11/00; C25D11/02; C25D11/04; C25D11/18; C25D11/20; C25D11/22; C25D11/12; Y; Y10; Y10S; Y10S204/00; Y10S204/09
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
227 words
An improved method for the electrolytic coloring of anodized aluminum by optical interference effects, which comprises subjecting an aluminum article carrying on its surface a porous anodic oxide film including a barrier layer in sequence to (1) an electrolytic treatment for enlarging the volume of the bottom of the pores in the film, (2) a preliminary electrolytic treatment in which said article is connected as an anode to a DC current to adjust the difference in thickness of said barrier layer to obtain more uniform current distribution at all parts of said article during subsequent coloring, and (3) an electrolytic coloring treatment in which the aluminum article is connected as a cathode in an electrolytic bath containing a soluble metal salt and subjected to electrolysis with a negative DC current having superimposed positive pulses to produce a metallic electrodeposition at the enlarged bottom of said pores, wherein the frequency of the pulses is in the range of 200 to 2600 pulses per minute and the ratio (Ta/Tc) between the periods of anodic and cathodic currents, respectively, during the coloring treatment does not exceed 0.3, said coloring treatment being controlled such that the upper surface of said deposition is spaced from said barrier layer a distance in the order of the wave length of visible light, whereby the coloration of said article is determined by optical interference effects.
Claim 2
Dependent Claim
227 words
An improved method for the electrolytic coloring of anodized aluminum by optical interference effects, which comprises subjecting an aluminum article carrying on its surface a porous anodic oxide film including a barrier layer in sequence to (1) an electrolytic treatment for enlarging the volume of the bottom of the pores in the film, (2) a preliminary electrolytic treatment in which said article is connected as an anode to a DC current to adjust the difference in thickness of said barrier layer to obtain more uniform current distribution at all parts of said article during subsequent coloring, and (3) an electrolytic coloring treatment in which the aluminum article is connected as a cathode in an electrolytic bath containing a soluble metal salt and subjected to electrolysis with a negative DC current having superimposed positive pulses to produce a metallic electrodeposition at the enlarged bottom of said pores, wherein the frequency of the pulses is in the range of 200 to 2600 pulses per minute and the ratio (Ta/Tc) between the periods of anodic and cathodic currents, respectively, during the coloring treatment does not exceed 0.3, said coloring treatment being controlled such that the upper surface of said deposition is spaced from said barrier layer a distance in the order of the wave length of visible light, whereby the coloration of said article is determined by optical interference effects.
Claim 3
Dependent Claim
32 words
The method according to claim 1, wherein the treatment for enlarging of the pore-structure is effected by an electrolytic treatment with an aqueous solution consisting essentially of phosphoric acid or chromic acid.
Claim 4
Dependent Claim
28 words
The method according to claim 1, wherein the adjustment of the barrier layer is effected by an electrolytic treatment in a bath containing one or more metal salts.
Claim 5
Dependent Claim
31 words
The method according to claim 3, wherein said electrolytic bath for adjusting said barrier layer contains at least one member selected from the group consisting of nickel, cobalt, copper and tin.
Claim 6
Dependent Claim
17 words
The method according to claim 3, wherein said electrolytic bath for adjusting said barrier layer is acidic.
Claim 7
Dependent Claim
45 words
The method according to claim 3, wherein the electrolytic for adjusting said barrier layer is obtained by dissolving a metal salt in an aqueous solution of one member selected from the group consisting of boric acid, ammonium borate, ammonium tartrate, ammonium phosphate and citric acid.
Claim 8
Dependent Claim
27 words
The method according to claim 3, wherein the anodic current density applied to the article during said adjusting treatment is not more than 3 A/dm 2 .
Claim 9
Dependent Claim
23 words
The method according to claim 7, wherein said anodic current density is within the range of from 0.05 to 0.5 A/dm 2 .
Claim 10
Dependent Claim
26 words
The method according to claim 3, wherein the duration of electrolysis in said electrolytic treatment for adjusting said barrier layer is not more than 2 minutes.
Claim 11
Dependent Claim
22 words
The method according to claim 9, in which the duration of the electrolytic treatment is in the range 10 to 60 seconds.
Claim 12
Dependent Claim
33 words
The method according to claim 1, in which the metal salts contained in said coloring electrolytic bath are salts of one or more of the group consisting of nickel, cobalt, copper and tin.
Claim 13
Dependent Claim
25 words
The method according to claim 11, wherein said coloring electrolytic bath is maintained in an acidic condition by addition of sulfuric acid or boric acid.
Claim 14
Dependent Claim
26 words
The method according to claim 11, wherein said coloring electrolytic bath is maintained in an weakly acidic condition by addition of tartaric acid or citric acid.
Claim 15
Dependent Claim
38 words
The method according to claim 1, wherein the maximum cathodic current flowing through the aluminum article during said coloring treatment has a current density of not more than 1 A/dm 2 over the surface of the aluminum article.
Claim 16
Dependent Claim
21 words
The method according to claim 14, wherein the current density is in the range of 0.05 to 0.5 A/dm 2 .
Claim 17
Dependent Claim
41 words
The method accordinng to claim 1, wherein the pulses produce a maximum anodic current flowing through the aluminum article during said coloring treatment which at most equals the maximum current flowing in the opposite direction during the remainder of the cycle.
Claim 18
Dependent Claim
24 words
The method according to claim 1, wherein the frequency of the said superimposed current pulses is the range 300 to 1800 pulses per minute.
Claim 19
Dependent Claim
21 words
The method according to claim 1 in which the ratio T A /T C lies in the range 0.01 to 0.15.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-11-07 | 1987-05-09 | 1987-11-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-11-07 | 1991-05-09 | 1991-11-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-11-07 | 1995-05-09 | 1995-11-08 | $7700.00 | Window Closed / Lapsed |