Expendable die casting sand core
Assignee: DOEHLER-JARVIS Inc
•
Filing: 1981-08-06
•
Granted: 1983-11-08
•
Expires: 2001-08-06
Abstract
Abstract Sand cores containing an acid curable binding agent are used in the production of die castings having undercut regions because of the favorable combination of shakeout properties, resistance to washout, and resistance to surface penetration.
Inventors
- 👤 Enno H. Page
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 02:15
CPC Classifications
B; B22; B22D; B22D17/00; B22D17/20; B22D17/22; B22D17/24; B22C; B22C1/00; B22C1/16; B22C1/20; B22C1/22; B22C3/00; B22C9/00; B22C9/10
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
257 words
A method for forming a die casting having an undercut region comprising: (A) forming a die casting die having a casting surface that includes at least one expendable sand core that forms said undercut region, said sand core consisting essentially of: (a) sand, and (b) binding agent comprising from about 0.25 weight percent to about 5 weight percent of said sand, said binding agent consisting essentially of an acid curable resin and an oxidizing agent, said oxidizing agent comprising from about 20 weight percent to about 70 weight percent of said resin, (c) curing said core with sulphur dioxide, and (d) coating said cured core with a coating material consisting essentially of: (1) from about 4 weight percent to about 30 weight percent suspending agent, (2) from about 60 weight percent to about 95 weight percent particulate refractory material comprising calcium aluminate particles having an average particle size of 20 to 25 microns and having no particle size greater than 40 to about 70 microns (3) 0 to 35 weight percent liquid vehicle, and (4) from about 1 weight percent to about 10 weight percent organic binding agent selected from the group consisting of thermoplastic resins, vinyl toluene/butadiene copolymer, styrene/butadiene copolymer, vinyl toluene/acrylate copolymer, styrene/acetylene copolymer, or acrylate homopolymers; (B) injecting molten metal into said die casting die, (C) permitting said injected molten metal to solidify to form said die casting having said undercut region, and (D) removing said die casting from said die and separating said expendable core from said undercut region within said die casting.
Claim 2
Independent Claim
257 words
A method for forming a die casting having an undercut region comprising: (A) forming a die casting die having a casting surface that includes at least one expendable sand core that forms said undercut region, said sand core consisting essentially of: (a) sand, and (b) binding agent comprising from about 0.25 weight percent to about 5 weight percent of said sand, said binding agent consisting essentially of an acid curable resin and an oxidizing agent, said oxidizing agent comprising from about 20 weight percent to about 70 weight percent of said resin, (c) curing said core with sulphur dioxide, and (d) coating said cured core with a coating material consisting essentially of: (1) from about 4 weight percent to about 30 weight percent suspending agent, (2) from about 60 weight percent to about 95 weight percent particulate refractory material comprising calcium aluminate particles having an average particle size of 20 to 25 microns and having no particle size greater than 40 to about 70 microns (3) 0 to 35 weight percent liquid vehicle, and (4) from about 1 weight percent to about 10 weight percent organic binding agent selected from the group consisting of thermoplastic resins, vinyl toluene/butadiene copolymer, styrene/butadiene copolymer, vinyl toluene/acrylate copolymer, styrene/acetylene copolymer, or acrylate homopolymers; (B) injecting molten metal into said die casting die, (C) permitting said injected molten metal to solidify to form said die casting having said undercut region, and (D) removing said die casting from said die and separating said expendable core from said undercut region within said die casting.
Claim 3
Dependent Claim
13 words
A method according to claim 1 wherein said acid curable resin comprises furane.
Claim 4
Dependent Claim
15 words
A method according to claim 1 wherein said oxidizing agent comprises methyl ethyl ketone peroxide.
Claim 5
Dependent Claim
17 words
A method according to claim 1 wherein said binding agent for said said core includes a silane.
Claim 6
Dependent Claim
183 words
An expendable sand core adapted to define an undercut region in a die casting comprising: (A) a base of: (a) sand, and (b) binding agent comprising from about 0.25 weight percent to about 5 weight percent of said sand, said binding agent consisting essentially of an acid curable resin and an oxidizing agent, said oxidizing agent comprising from about 20 weight percent to about 70 weight percent of said resin, said base being cured with sulphur dioxide, and (B) a coating on said base consisting essentially of: (a) from about 4 weight percent to about 30 weight percent suspending agent, (b) from about 60 weight percent to about 95 weight percent particulate refractory material comprising calcium aluminate particles having an average particle size of 20 to 25 microns and having no particle size greater than 40 to 70 microns, (c) 0 to 35 weight percent liquid vehicle, and (d) from about 1 weight percent to about 10 weight percent organic binding agent selected from the group consisting of thermoplastic resins, vinyl toluene/butadiene copolymer, styrene/butadiene copolymer, vinyl toluene/acrylate copolymer, styrene/acetylene copolymer, or acrylate homopolymers.
Claim 7
Dependent Claim
183 words
An expendable sand core adapted to define an undercut region in a die casting comprising: (A) a base of: (a) sand, and (b) binding agent comprising from about 0.25 weight percent to about 5 weight percent of said sand, said binding agent consisting essentially of an acid curable resin and an oxidizing agent, said oxidizing agent comprising from about 20 weight percent to about 70 weight percent of said resin, said base being cured with sulphur dioxide, and (B) a coating on said base consisting essentially of: (a) from about 4 weight percent to about 30 weight percent suspending agent, (b) from about 60 weight percent to about 95 weight percent particulate refractory material comprising calcium aluminate particles having an average particle size of 20 to 25 microns and having no particle size greater than 40 to 70 microns, (c) 0 to 35 weight percent liquid vehicle, and (d) from about 1 weight percent to about 10 weight percent organic binding agent selected from the group consisting of thermoplastic resins, vinyl toluene/butadiene copolymer, styrene/butadiene copolymer, vinyl toluene/acrylate copolymer, styrene/acetylene copolymer, or acrylate homopolymers.
Claim 8
Dependent Claim
14 words
A sand core according to claim 5 wherein said acid curable resin comprises furane.
Claim 9
Dependent Claim
16 words
A sand core according to claim 5 wherein said oxidizing agent comprises methyl ethyl ketone peroxide.
Claim 10
Dependent Claim
18 words
A sand core according to claim 5 wherein said binding agent for said sand core includes a silane.
Claim 11
Dependent Claim
111 words
A coating material for cured cores useful in die casting of molten metals, consisting essentially of: (a) from about 4 weight percent to about 30 weight percent suspending agent, (b) from about 60 weight percent to about 95 weight percent particulate refractory material comprising calcium aluminate particles having an average particle size of 20 to 25 microns and having no particle size greater than 40 to about 70 microns, (c) 0 to 35 weight percent liquid vehicle, and (d) from about 1 weight percent to about 10 weight percent organic binding agent selected from the group consisting of vinyl toluene/butadiene copolymer, styrene/butadiene copolymer, vinyl toluene/acrylate copolymer, styrene/acetylene copolymer, or acrylate homopolymers.
Claim 12
Dependent Claim
111 words
A coating material for cured cores useful in die casting of molten metals, consisting essentially of: (a) from about 4 weight percent to about 30 weight percent suspending agent, (b) from about 60 weight percent to about 95 weight percent particulate refractory material comprising calcium aluminate particles having an average particle size of 20 to 25 microns and having no particle size greater than 40 to about 70 microns, (c) 0 to 35 weight percent liquid vehicle, and (d) from about 1 weight percent to about 10 weight percent organic binding agent selected from the group consisting of vinyl toluene/butadiene copolymer, styrene/butadiene copolymer, vinyl toluene/acrylate copolymer, styrene/acetylene copolymer, or acrylate homopolymers.
Claim 13
Independent Claim
255 words
A method of forming a die casting having an undercut region from a die casting die having a casting surface that includes at least one expendable sand core that forms said undercut region, (A) said core consisting essentially of: (a) sand, and (b) binding agent comprising from about 0.25 weight percent to about 5 weight percent of said sand, said binding agent consisting essentially of an acid curable resin and an oxidizing agent, said oxidizing agent comprising from about 20 weight percent to about 70 weight percent of said resin, said core being cured with sulphur dioxide, and (c) coating said cured core with a material consisting essentially of: (1) from about 4 weight percent to about 30 weight percent suspending agent, (2) from about 60 weight percent to about 95 weight percent particulate refractory material comprising calcium aluminate particles having an average particle size of 20 to 25 microns and having no particle size greater than 40 to about 70 microns, (3) 0 to 35 weight percent liquid vehicle, and (4) from about 1 weight percent to about 10 weight percent organic binding agent selected from the group consisting of thermoplastic resins, vinyl toluene/butadiene copolymer, styrene/butadiene copolymer, vinyl toluene/acrylate copolymer, styrene/acetylene copolymer, or acrylate homopolymers; and (B) injecting molten metal into said die casting die; (C) permitting said injected molten metal to solidify to form said die casting having said undercut region; (D) removing said die casting from said die; and (E) separating said expendable core from said undercut region within said die casting.
Claim 14
Independent Claim
255 words
A method of forming a die casting having an undercut region from a die casting die having a casting surface that includes at least one expendable sand core that forms said undercut region, (A) said core consisting essentially of: (a) sand, and (b) binding agent comprising from about 0.25 weight percent to about 5 weight percent of said sand, said binding agent consisting essentially of an acid curable resin and an oxidizing agent, said oxidizing agent comprising from about 20 weight percent to about 70 weight percent of said resin, said core being cured with sulphur dioxide, and (c) coating said cured core with a material consisting essentially of: (1) from about 4 weight percent to about 30 weight percent suspending agent, (2) from about 60 weight percent to about 95 weight percent particulate refractory material comprising calcium aluminate particles having an average particle size of 20 to 25 microns and having no particle size greater than 40 to about 70 microns, (3) 0 to 35 weight percent liquid vehicle, and (4) from about 1 weight percent to about 10 weight percent organic binding agent selected from the group consisting of thermoplastic resins, vinyl toluene/butadiene copolymer, styrene/butadiene copolymer, vinyl toluene/acrylate copolymer, styrene/acetylene copolymer, or acrylate homopolymers; and (B) injecting molten metal into said die casting die; (C) permitting said injected molten metal to solidify to form said die casting having said undercut region; (D) removing said die casting from said die; and (E) separating said expendable core from said undercut region within said die casting.
Claim 15
Dependent Claim
13 words
A method according to claim 10 wherein said acid curable resin comprises furane.
Claim 16
Dependent Claim
15 words
A method according to claim 10 wherein said oxidizing agent comprises methyl ethyl ketone peroxide.
Claim 17
Dependent Claim
17 words
A method according to claim 10 wherein said binding agent for said sand core includes a silane.
References Cited (Backward Citations)
US3401735A
Cited
JPS46942Y1
Cited
US3639654A
Cited
US3879339A
Cited
US3922245A
Cited
US4001468A
Cited
US4127157A
Cited
US4096293A
Cited
US4194915A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-11-07 | 1987-05-09 | 1987-11-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-11-07 | 1991-05-09 | 1991-11-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-11-07 | 1995-05-09 | 1995-11-08 | $7700.00 | Window Closed / Lapsed |