Preparation of electrically conductive polymers
Assignee: BASF SE
•
Filing: 1982-04-29
•
Granted: 1983-11-01
•
Expires: 2002-04-29
Abstract
Abstract A process for the preparation of stable electrically conductive polymers, having conductivities greater than 10 -2 S/cm, wherein a polyacetylene is reacted with from 1 to 100, preferably from 10 to 33, % by weight of tosylmethyl isocyanide and from 0.1 to 70, preferably from 5 to 35, % by weight of an alkali metal or its amide, or of a Lewis acid. The polymers obtained can be used in electrical engineering for the production of solar cells, for the conversion and fixing of radiation and for the production of electrical and magnetic switches and electrical storage devices, and can also be used for the antistatic treatment of plastics.
Inventors
- 👤 Herbert Naarmann
- 👤 Klaus Penzien
- 👤 Johannes Schlag
- 👤 Petr Simak
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 10:13
CPC Classifications
H; H01; H01B; H01B1/00; H01B1/06; H01B1/12; H01B1/124; H01B1/125; C; C08; C08F; C08F8/00; C08F8/42; H10; H10K; H10K85/00; H10K85/10; H10K85/141; H10K85/143; H10K30/00; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/549
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
77 words
A process for the preparation of a stable electrically conductive polymer from a polyacetylene, the polymer having an electrical conductivity greater than 10 -2 S/cm, which process consists essentially of treating the polyacetylene with from 1 to 100% by weight of tosylmethyl isocyanide and from 0.1 to 70% by weight of a dopant selected from the group consisting of an alkali metal, an alkali metal amide or a Lewis acid, the percentages being based on the polyacetylene.
Claim 2
Dependent Claim
77 words
A process for the preparation of a stable electrically conductive polymer from a polyacetylene, the polymer having an electrical conductivity greater than 10 -2 S/cm, which process consists essentially of treating the polyacetylene with from 1 to 100% by weight of tosylmethyl isocyanide and from 0.1 to 70% by weight of a dopant selected from the group consisting of an alkali metal, an alkali metal amide or a Lewis acid, the percentages being based on the polyacetylene.
Claim 3
Dependent Claim
43 words
A process as defined in claim 1, wherein the reaction is carried out using from 10 to 30% by weight of tosylmethyl isocyanide and from 5 to 35% by weight of an alkali metal or of its amide, or of a Lewis acid.
Claim 4
Dependent Claim
51 words
A process as defined in claim 1, wherein the reaction is first carried out with tosylmethyl isocyanide to give a polymer containing structural units of the formula (I): ##STR4## where n is 5-200, and this product is then reacted with an alkali metal or its amide, or with a Lewis acid.
Claim 5
Dependent Claim
43 words
A process as defined in claim 1, wherein a Lewis acid is used as the dopant and wherein the Lewis acid is a halogen derivative of an element of group III, IV, V, VI, VII or VIII of the periodic table of elements.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-31 | 1987-05-02 | 1987-11-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-31 | 1991-05-02 | 1991-11-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-31 | 1995-05-02 | 1995-11-01 | $7700.00 | Window Closed / Lapsed |