US4412577A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Control of seed melt-back during directional solidification of metals
Assignee: RTX Corp
•
Filing: 1982-01-27
•
Granted: 1983-11-01
•
Expires: 2002-01-27
Abstract
Abstract In the manufacture of a single crystal article, by the directional solidification of a metal in a ceramic mold the melt-back of a seed crystal is controlled to provide high casting yield. The melt-back, measured as a fraction of the original length of the seed, is preferably between 25-75%, more preferably between 33-67%. Diametrical clearance between the seed and mold is also closely controlled, between 0.06-0.25 mm, to eliminate extraneous grain nucleation.
Inventors
- 👤 Richard W. Salkeld
- 👤 Neal P. Anderson
- 👤 Anthony F. Giamei
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 23:36
CPC Classifications
B; B22; B22D; B22D27/00; B22D27/04; B22D27/045; C; C30; C30B; C30B11/00; C30B11/14; C30B29/00; C30B29/10; C30B29/52
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
166 words
The process of directional solidification from molten metal of an article having a structure which is epitaxial with a seed which comprises forming a mold, placing an original seed within the mold, heating the mold, melting a portion of the seed by contacting a seed surface with molten metal placed in the mold, and epitaxially solidifying the molten metal, characterized by melting a portion of the seed length which is at least 25% of the original seed length, the melted portion of the seed length being measured from the original molten metal contacting surface before melting to the location of the liquidus interface after melting, the melting being sufficient to cause physical disruption of surface films on the surface of the seed where it is contacted by molten metal to be epitaxially solidified, and insufficient to raise above the metal solidus temperature the portion of the seed which is most distant from the region where it is contacted by the molten metal to be epitaxially solidified.
Claim 2
Dependent Claim
166 words
The process of directional solidification from molten metal of an article having a structure which is epitaxial with a seed which comprises forming a mold, placing an original seed within the mold, heating the mold, melting a portion of the seed by contacting a seed surface with molten metal placed in the mold, and epitaxially solidifying the molten metal, characterized by melting a portion of the seed length which is at least 25% of the original seed length, the melted portion of the seed length being measured from the original molten metal contacting surface before melting to the location of the liquidus interface after melting, the melting being sufficient to cause physical disruption of surface films on the surface of the seed where it is contacted by molten metal to be epitaxially solidified, and insufficient to raise above the metal solidus temperature the portion of the seed which is most distant from the region where it is contacted by the molten metal to be epitaxially solidified.
Claim 3
Dependent Claim
26 words
The process of claim 1 characterized by melting a portion which is more than 25 percent but less than 75 percent of the original seed length.
Claim 4
Dependent Claim
26 words
The process of claim 2 characterized by melting a portion which is more than 33 percent but less than 67 percent of the original seed length.
Claim 5
Dependent Claim
14 words
The process of claims 1 or 2 wherein the seed is a nickel superalloy.
Claim 6
Dependent Claim
12 words
The process of claim 4 wherein the seed is a single crystal.
Claim 7
Dependent Claim
84 words
The process of claim 4 wherein the mold is a ceramic investment shell mold, having a starter section shaped to encompass a seed, a selector section connected to the starter section to provide a reduced cross section solidification growth path, and an article section connected to the selector section to define the shape of the article, characterized by providing a lateral clearance space of between 0.06-0.25 mm, as measured diametrically between the seed and the starter section of the mold which surrounds the seed.
References Cited (Backward Citations)
US3260505A
Cited
US3494709A
Cited
US3763926A
Cited
US3857436A
Cited
US4015657A
Cited
US4209348A
Cited
US4190094A
Cited
US4289570A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-31 | 1987-05-02 | 1987-11-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-31 | 1991-05-02 | 1991-11-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-31 | 1995-05-02 | 1995-11-01 | $7700.00 | Window Closed / Lapsed |