Aircraft stringer material and method for producing the same
Assignee: Sumitomo Light Metal Industries Ltd
•
Filing: 1980-07-30
•
Granted: 1983-10-18
•
Expires: 2000-07-30
Abstract
Abstract An aircraft stringer material having high strength, small grain size, good resistance to stress corrosion cracking and a very high degree of workability is produced from an aluminum base alloy consisting essentially of 5.1 to 8.1 wt. % Zn, 1.8 to 3.4 wt. % Mg, 1.2 to 2.6 wt. % Cu, up to 0.20 wt. % Ti and at least one of 0.18 to 0.35 wt. % Cr and 0.05 to 0.25 wt. % Zr, the balance being aluminum and impurities, by a production method characterized by a special annealing step including rapid heating to a temperature of 320 DEG to 500 DEG C. at a heating rate exceeding 11 DEG C./min. Further, a corrosion-resistant stringer material is produced in a manner very similar to the above production method, using the above aluminum alloy as a core and AA7072 alloy as cladding.
Inventors
- 👤 Yoshio Baba
- 👤 Teruo Uno
- 👤 Hideo Yoshida
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 09:49
CPC Classifications
B; B32; B32B; B32B15/00; B32B15/01; B32B15/016; B64; B64C; B64C1/00; B64C1/06; B64C1/064; C; C22; C22F; C22F1/00; C22F1/04; C22F1/053
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
181 words
A method for producing an aluminum alloy product having a grain size not exceeding 100 μm and useful as an aircraft stringer material, comprising the steps of: homogenizing an aluminum alloy consisting essentially of 5.1 to 8.1 wt. % zinc, 1.8 to 3.4 wt. % magnesium, 1.2 to 2.6 wt. % copper, at least one of 0.18 to 0.35 wt. % chromium and 0.05 to 0.25 wt. % zirconium, up to 0.20 wt. % titanium, up to 0.50 wt. % iron, up to 0.40 wt. % silicon, up to 0.70 wt. % manganese, and the balance being aluminum and incidental impurities wherein said impurities do not include any of the components named above, thereby to produce an homogenized alloy; then hot rolling said homogenized alloy to provide a shaped object; then cold rolling said shaped object to provide a plate having a selected thickness; then rapidly heating said plate at an average heating rate exceeding 11° C./min. to a temperature of 320° to 500° C. and thereby annealing said plate and effecting recrystallization to form a uniformly fine recrystallized grain structure.
Claim 2
Independent Claim
181 words
A method for producing an aluminum alloy product having a grain size not exceeding 100 μm and useful as an aircraft stringer material, comprising the steps of: homogenizing an aluminum alloy consisting essentially of 5.1 to 8.1 wt. % zinc, 1.8 to 3.4 wt. % magnesium, 1.2 to 2.6 wt. % copper, at least one of 0.18 to 0.35 wt. % chromium and 0.05 to 0.25 wt. % zirconium, up to 0.20 wt. % titanium, up to 0.50 wt. % iron, up to 0.40 wt. % silicon, up to 0.70 wt. % manganese, and the balance being aluminum and incidental impurities wherein said impurities do not include any of the components named above, thereby to produce an homogenized alloy; then hot rolling said homogenized alloy to provide a shaped object; then cold rolling said shaped object to provide a plate having a selected thickness; then rapidly heating said plate at an average heating rate exceeding 11° C./min. to a temperature of 320° to 500° C. and thereby annealing said plate and effecting recrystallization to form a uniformly fine recrystallized grain structure.
Claim 3
Dependent Claim
37 words
A method as claimed in claim 1, including the additional steps of cold working said annealed plate and then subjecting same to solution heat treatment to obtain a plate having a grain size not exceeding 100 μm.
Claim 4
Dependent Claim
32 words
The method as claimed in claim 1 or claim 2 in which after said rapid heating step, the annealed plate is cooled at an average cooling rate of less than 30° C./hr.
Claim 5
Dependent Claim
61 words
The method as claimed in claim 1 or claim 2 in which after said rapid heating step, the annealed plate is cooled at an average cooling rate of 30° C./hr. or higher, then said plate is reheated to a temperature of 200° to 500° C. and then said plate is cooled at an average cooling rate of 30° C./hr. or less.
Claim 6
Dependent Claim
54 words
The method as claimed in claim 1 or claim 2 in which after said rapid heating step, the annealed plate is cooled at an average cooling rate of 30° C./hr. or higher, then said plate is reheated to a temperature of 200° to less than 350° C. and then said plate is air cooled.
Claim 7
Dependent Claim
27 words
The method as claimed in claim 2 in which in said cold working step, said annealed plate is cold rolled up to a maximum reduction of 90%.
Claim 8
Dependent Claim
49 words
The method as claimed in claim 1 in which said homogenizing step is performed by heating said aluminum alloy at a temperature of 400° to 490° C. for from 2 to 48 hours and said hot rolling step is performed at a starting temperature of 350° to 470° C.
Claim 9
Dependent Claim
49 words
The method as claimed in claim 7 in which after said hot rolling step and before said cold rolling step, said shaped object is heated at a temperature of 300° to 460° C. to anneal same and then it is cooled at a cooling rate not exceeding 30° C./hr.
Claim 10
Dependent Claim
84 words
The method as claimed in claim 1 or claim 2 in which said aluminum alloy consists essentially of 5.1 to 8.1 wt.% zinc, 1.8 to 3.4 wt.% magnesium, 1.2 to 2.6 wt. % copper, 0.18 to 0.35 wt. % chromium, up to 0.20 wt. % titanium, up to 0.50 wt. % iron, up to 0.40 wt. % silicon, up to 0.70 wt. % manganese, and the balance being aluminum and incidental impurities wherein said impurities do not include any of the components named above.
Claim 11
Independent Claim
199 words
A method for producing a clad aluminum alloy product having a core grain size not exceeding 100 μm and useful as an aircraft stringer material, comprising the steps of: homogenizing an aluminum core alloy consisting essentially of 5.1 to 8.1 wt. % zinc, 1.8 to 3.4 wt. % magnesium, 1.2 to 2.6 wt. % copper, at least one of 0.18 to 0.35 wt. % chromium and 0.05 to 0.25 wt. % zirconium, up to 0.20 wt. % titanium, up to 0.50 wt. % iron, up to 0.40 wt. % silicon, up to 0.70 wt. % manganese, and the balance being aluminum and incidental impurities wherein said impurities do not include any of the components named above, thereby to produce an homogenized alloy; then hot clad rolling a cladding layer consisting of AA7072 alloy on at least one side of said homogenized core alloy to provide a shaped object; then cold rolling said shaped object to provide a plate having a selected thickness; then rapidly heating said plate at an average heating rate exceeding 11° C./min. to a temperature of 320° to 500° C. and thereby annealing said plate and effecting recrystallization to form a uniformly fine recrystallized grain structure.
Claim 12
Independent Claim
199 words
A method for producing a clad aluminum alloy product having a core grain size not exceeding 100 μm and useful as an aircraft stringer material, comprising the steps of: homogenizing an aluminum core alloy consisting essentially of 5.1 to 8.1 wt. % zinc, 1.8 to 3.4 wt. % magnesium, 1.2 to 2.6 wt. % copper, at least one of 0.18 to 0.35 wt. % chromium and 0.05 to 0.25 wt. % zirconium, up to 0.20 wt. % titanium, up to 0.50 wt. % iron, up to 0.40 wt. % silicon, up to 0.70 wt. % manganese, and the balance being aluminum and incidental impurities wherein said impurities do not include any of the components named above, thereby to produce an homogenized alloy; then hot clad rolling a cladding layer consisting of AA7072 alloy on at least one side of said homogenized core alloy to provide a shaped object; then cold rolling said shaped object to provide a plate having a selected thickness; then rapidly heating said plate at an average heating rate exceeding 11° C./min. to a temperature of 320° to 500° C. and thereby annealing said plate and effecting recrystallization to form a uniformly fine recrystallized grain structure.
Claim 13
Dependent Claim
41 words
A method as claimed in claim 10, including the additional steps of cold working said annealed plate and then subjecting same to solution heat treatment to obtain a plate in which the core has a grain size not exceeding 100 μm.
Claim 14
Dependent Claim
32 words
The method as claimed in claim 10 or claim 11 in which after said rapid heating step, the annealed plate is cooled at an average cooling rate of less than 30° C./hr.
Claim 15
Dependent Claim
61 words
The methd as claimed in claim 10 or claim 11 in which after said rapid heating step, the annealed plate is cooled at an average cooling rate of 30° C./hr. or higher, then said plate is reheated to a temperature of 200° to 500° C. and then said plate is cooled at an average cooling rate of 30° C./hr. or less.
Claim 16
Dependent Claim
54 words
The method as claimed in claim 10 or claim 11 in which after said rapid heating step, the annealed plate is cooled at an average cooling rate of 30° C./hr. or higher, then said plate is reheated to a temperature of 200° to less than 350° C. and then said plate is air cooled.
Claim 17
Dependent Claim
27 words
The method as claimed in claim 11 in which in said cold working step, said annealed plate is cold rolled up to a maximum reduction of 90%.
Claim 18
Dependent Claim
71 words
The method as claimed in claim 10 in which said homogenizing step is performed by heating said aluminum alloy at a temperature of 400° to 490° C. for from 2 to 48 hours, said AA7072 alloy is homogenized at 400° to 560° C. for 2 to 48 hours prior to said hot clad rolling step, and said hot rolling step is performed at a starting temperature of 350° to 470° C.
Claim 19
Dependent Claim
49 words
The method as claimed in claim 16 in which after said hot rolling step and before said cold rolling step, said shaped object is heated at a temperature of 300° to 460° C. to anneal same and then it is cooled at a cooling rate not exceeding 30° C./hr.
Claim 20
Dependent Claim
86 words
The method as claimed in claim 10 or claim 11 in which said aluminum alloy consists essentially of 5.1 to 8.1 wt. % zinc, 1.8 to 3.4 wt. % magnesium, 1.2 to 2.6 wt. % copper, 0.18 to 0.35 wt. % chromium, up to 0.20 wt. % titanium, up to 0.50 wt. % iron, up to 0.40 wt. % silicon, up to 0.70 wt. % manganese, and the balance being aluminum and incidental impurities wherein said impurities do not include any of the components named above.
Claim 21
Dependent Claim
34 words
The method as claimed in claim 1, claim 2 or claim 6, in which after said rapid heating step, the annealed plate is cooled at an average cooling rate of 30° C./hr. or higher.
Claim 22
Dependent Claim
34 words
The method as claimed in claim 10, claim 11 or claim 15, in which after said rapid heating step, the annealed plate is cooled at an average cooling rate of 30° C./hr. or higher.
References Cited (Backward Citations)
US4305763A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-17 | 1987-04-18 | 1987-10-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-17 | 1991-04-18 | 1991-10-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-17 | 1995-04-18 | 1995-10-18 | $7700.00 | Window Closed / Lapsed |