Process for dyeing absorbent microbiocidal fabric and product so produced
Assignee: American Hospital Supply Corp
•
Filing: 1981-10-09
•
Granted: 1983-10-11
•
Expires: 2001-10-09
Abstract
Abstract Dyed, absorbent bioactive wettable fabrics are prepared by mixing together a wettable hydrophilic organosilicone polymer, a tinctorial amount of a compatible direct dye and a bioactive silyl quanternary amine. The mixture is applied to a non-woven cellulose-containing substrate then heated to dye the coated substrate, fix the dye and couple the microbiocide and hydrophilic coupling agent to the substrate. Fabric so produced is useful as an absorbent surgical drape or dressing to isolate a surgical incision site while providing an absorbent antimicrobial field to destroy migrating and cross-contaminating bacteria, algae and fungi.
Inventors
- 👤 A. Frank Baldwin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:23
CPC Classifications
D; D06; D06M; D06M16/00; A; A01; A01N; A01N55/00; A61; A61B; A61B42/00; A61B46/00; A61B46/40; A61F; A61F13/00; A61F13/01; A61F13/01008; A61L; A61L15/00; A61L15/16; A61L15/18; A61L15/42; A61L15/46; A61L15/52; A61L31/00; A61L31/08; A61L31/10; A61L31/14; A61L31/16; D06M15/00; D06M15/19; D06M15/37; D06M15/55; D06M15/643; D06M15/65; A61F13/15; A61F13/84; A61F13/8405; A61F2013/00089; A61F2013/00314; A61F2013/00323; A61F2013/00361; A61F2013/00727; A61F2013/00731; A61F2013/00744; A61F2013/00902; A61F2013/0091; A61F2013/15008; A61F2013/15048; A61F13/15577; A61F2013/15821; A61L2300/00; A61L2300/20; A61L2300/204; A61L2300/208; A61L2300/40; A61L2300/404
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
172 words
A process for making a dyed, absorbent, bioactive wettable medical fabric comprising the steps of: (a) mixing (1) a wettable hydrophilic coupling amount of an organosilicone terpolymer of the formula: ##STR3## wherein R is hydrogen or methyl, the sum of a+b is in the range of 5 to 200, x is 10 to 50,000, y is 1 to x and z is 1 to 0.5x provided that the sum of y+z is ≦0.75x with (2) a tinctorial amount of a compatible direct dye, and (3) bioactive amount of a bioactive silyl quaternary amine compounds have the formula: ##STR4## wherein R is an alkyl of 11 to 22 carbon atoms and R 1 is a bromine or chlorine; and (b) applying the mixture of step (a) to a non-woven cellulose-containing substrate; and (c) heating the thus coated substrate from step (b) to dry the substrate and fix the dye, microbiocide and hydrophilic coupling agent to said substrate, thereby producing a dyed, bacteriocidal substantially non-leachable and non-flammable finish which is substantive on said substrate.
Claim 2
Dependent Claim
172 words
A process for making a dyed, absorbent, bioactive wettable medical fabric comprising the steps of: (a) mixing (1) a wettable hydrophilic coupling amount of an organosilicone terpolymer of the formula: ##STR3## wherein R is hydrogen or methyl, the sum of a+b is in the range of 5 to 200, x is 10 to 50,000, y is 1 to x and z is 1 to 0.5x provided that the sum of y+z is ≦0.75x with (2) a tinctorial amount of a compatible direct dye, and (3) bioactive amount of a bioactive silyl quaternary amine compounds have the formula: ##STR4## wherein R is an alkyl of 11 to 22 carbon atoms and R 1 is a bromine or chlorine; and (b) applying the mixture of step (a) to a non-woven cellulose-containing substrate; and (c) heating the thus coated substrate from step (b) to dry the substrate and fix the dye, microbiocide and hydrophilic coupling agent to said substrate, thereby producing a dyed, bacteriocidal substantially non-leachable and non-flammable finish which is substantive on said substrate.
Claim 3
Dependent Claim
49 words
The process of claim 1 wherein the mixture of step (a) contains from about 0.5 to about 1.5 weight percent of the hydrophilic coupling agent (1), up to 1 weight percent of the direct dye (2), and from about 0.2 to 1.1 weight percent of the bioactive agent (3).
Claim 4
Dependent Claim
26 words
The process of claim 1 or 2 wherein step (c) is conducted at a temperature in the range of about 280° F. to about 360° F.
Claim 5
Dependent Claim
21 words
The process of claim 1 or 2 wherein said non-woven substrate is composed of at least about 80 weight percent cellulose.
Claim 6
Dependent Claim
30 words
The process of claim 4 wherein said non-woven substrate contains from about 80 to 85 weight percent cellulose bonded with about 15 to about 20 weight percent acrylic resin binder.
Claim 7
Dependent Claim
58 words
The process of claim 1 or 2 wherein in said hydrophilic coupling agent (1) the sum of a+b is in the range of 5 to 200, x is 50 to 300, y is 1 to 0.25x and z is 1 to 0.5x, provided that the sum of y+z is≦0.25x; and the microbiocide (3) is 3-(trimethoxysilyl)-propyloctadecyl dimethyl ammonium chloride.
References Cited (Backward Citations)
US3247280A
Cited
US3560442A
Cited
US3488217A
Cited
US3660008A
Cited
US3796686A
Cited
US3730701A
Cited
US3794736A
Cited
US3788803A
Cited
US3817739A
Cited
US4035411A
Cited
US4184004A
Cited
US4262043A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-10 | 1987-04-11 | 1987-10-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-10 | 1991-04-11 | 1991-10-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-10 | 1995-04-11 | 1995-10-11 | $7700.00 | Window Closed / Lapsed |