Method of impregnating spheres of activated alumina for use in catalyst support with cerium

Assignee: Nissan Motor Co Ltd
•
Filing: 1982-05-26
•
Granted: 1983-10-04
•
Expires: 2002-05-26
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract A method of impregnating spheres of activated alumina with cerium in an oxidized state. The cerium-impregnated alumina spheres are for use in catalyst supports for three-way catalysts for purification of exhaust gases of automotive engines. The method has the steps of wetting spheres of activated alumina with an aqueous solution of a cerium salt, drying the wet spheres and calcining the dried spheres in an oxidizing atmosphere. The drying is performed so as to complete the removal of water from the spheres by evaporation in a time period not longer than 10 min, preferably by subjecting the wet spheres to microwave heating and most preferably by performing the microwave heating with a forced draft. By quickly completing the drying the distribution of cerium in the individual spheres becomes very uniform, and this has the effect of improving the efficiency of three-way catalysts produced by using the cerium-impregnated spheres of activated alumina.

Inventors

  • 👤 Keiichi Sawamura

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-10-30 13:16
CPC Classifications
B; B01; B01J; B01J37/00; B01J37/34; B01J37/341; B01J37/343; B01D; B01D53/00; B01D53/34; B01D53/74; B01D53/86; B01J23/00; B01J23/10; B01J37/02; B01J37/0201; B01J37/08

Claims Analysis

Total Claims: 9
Claim 1
Independent Claim 85 words
In a method of impregnating spheres of activated alumina for use in catalyst supports with cerium in an oxidized state, the method having the steps of wetting spheres of activated alumina with an aqueous solution of a cerium salt, drying the wet spheres and calcining the dried spheres in an oxidizing atmosphere, the improvement comprising performing the step of drying the wet spheres so as to complete the removal of water from the spheres by evaporation in a time period not longer than 10 minutes.
Claim 2
Dependent Claim 85 words
In a method of impregnating spheres of activated alumina for use in catalyst supports with cerium in an oxidized state, the method having the steps of wetting spheres of activated alumina with an aqueous solution of a cerium salt, drying the wet spheres and calcining the dried spheres in an oxidizing atmosphere, the improvement comprising performing the step of drying the wet spheres so as to complete the removal of water from the spheres by evaporation in a time period not longer than 10 minutes.
Claim 3
Dependent Claim 23 words
A method according to claim 1, wherein the step of drying the wet spheres is performed by exposing the wet spheres to microwaves.
Claim 4
Dependent Claim 21 words
A method according to claim 2, wherein the wet spheres are placed in a current of air during the drying step.
Claim 5
Dependent Claim 26 words
A method according to claim 3, wherein the temperature of said current of air is in the range from about 30° C. to about 120° C.
Claim 6
Dependent Claim 18 words
A method according to claim 1 or 3, wherein said oxidizing atmosphere at the calcining step is air.
Claim 7
Dependent Claim 28 words
A method according to claim 1 or 3, wherein the dried spheres are calcined at a temperature in the range from about 500° C. to about 650° C.
Claim 8
Dependent Claim 70 words
A method according to claim 1 or 3, wherein the concentration of said cerium salt in said aqueous solution and the quantity of said aqueous solution relative to the quantity of the spheres of activated alumina are controlled such that the content of cerium in the spheres after the calcining step is in the range from 2 to 15% of the total weight of the spheres after the calcining step.
Claim 9
Dependent Claim 15 words
A method according to claim 1 or 3, wherein said cerium salt is cerium nitrate.

References Cited (Backward Citations)

DE2412230A1 Cited
US4206087A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1986-10-03 1987-04-04 1987-10-04 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1990-10-03 1991-04-04 1991-10-04 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1994-10-03 1995-04-04 1995-10-04 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag