Abstract
Abstract The invention disclosed is a novel method of making an improved carbon dioxide absorbing material. A primary carbon dioxide absorbent is employed, specifically a group IA and IIA metal hydroxide, and various combinations of additives which modify the properties of the primary absorbent, in the form of an aqueous solution, and sprayed onto the surface of the primary absorbent.
Inventors
- 👤 Clive D. R. MacGregor
- 👤 William G. Forsyth
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 15:13
CPC Classifications
B; B01; B01D; B01D53/00; B01D53/02; B01J; B01J20/00; B01J20/02; B01J20/04; B01J20/041; B01J20/046; B01J20/30; B01J20/3021; B01J20/32; B01J20/3202; B01J20/3204; B01J20/3231; B01J20/3234; B01J20/3236; B01J20/3291; B01J20/3293; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
119 words
In a method for making a carbon dioxide absorbent material, said absorbent material comprising about 75 to about 85%/w of a compound selected from the group consisting of group IA and IIA metal hydroxides, about 15 to about 20%/w of water and about 3 to about 5%/w of an additive, the improvement comprising (1) providing said additive in solution in water wherein said additive solution comprises about 15 to about 20%/w of water, about 2 to about 3% of NaOH, about 1 to about 2%/w of KOH and about 0.1 to about 1%/w of CaCl 2 , and (2) spraying said addition solution onto said compound to provide a substantially even coating of said addition solution on said compound.
Claim 2
Dependent Claim
119 words
In a method for making a carbon dioxide absorbent material, said absorbent material comprising about 75 to about 85%/w of a compound selected from the group consisting of group IA and IIA metal hydroxides, about 15 to about 20%/w of water and about 3 to about 5%/w of an additive, the improvement comprising (1) providing said additive in solution in water wherein said additive solution comprises about 15 to about 20%/w of water, about 2 to about 3% of NaOH, about 1 to about 2%/w of KOH and about 0.1 to about 1%/w of CaCl 2 , and (2) spraying said addition solution onto said compound to provide a substantially even coating of said addition solution on said compound.
Claim 3
Dependent Claim
46 words
A method according to claim 1, including the additional step of transferring the coated compound to an air-tight enclosure and storing for about two days prior to use at about 4°-20° C. in order to permit stabilization of the activity of the CO 2 absorbent material.
Claim 4
Dependent Claim
31 words
A method according to claim 1 or 2, wherein the CO 2 absorbent material consists essentially of ______________________________________
H.sub.2 O 16.7%/w
NaOH 2.7%/w
KOH 1.4%/w
CaCl.sub.2 0.1%/w
Ca(OH).sub.2 79.1%/w
100.0%/w
______________________________________
Claim 5
Independent Claim
144 words
A method for making a carbon dioxide absorbent material, which comprises (a) providing substantially pure Ca(OH) 2 in an amount of about 75 to about 85%/w; (b) adding 60-70% by weight H 2 O; (c) mixing thoroughly until a paste of substantially uniform consistency is achieved; (d) drying in air to remove substantially all of the water; (e) grinding and screening the dried material to provide granular Ca(OH) 2 of average diameter of 5-8 mesh; (f) providing an additive solution comprising about 15 to about 20%/w of water, about 2 to about 3%/w of NaOH, about 1 to about 2%/w of KOH and about 0.1 to about 1%/w of CaCl 2 ; and (g) spraying said additive solution onto the granular Ca(OH) 2 from step (e) while stirring gently to provide a substantially even coating of said additive solution of the Ca(OH) 2 .
Claim 6
Independent Claim
144 words
A method for making a carbon dioxide absorbent material, which comprises (a) providing substantially pure Ca(OH) 2 in an amount of about 75 to about 85%/w; (b) adding 60-70% by weight H 2 O; (c) mixing thoroughly until a paste of substantially uniform consistency is achieved; (d) drying in air to remove substantially all of the water; (e) grinding and screening the dried material to provide granular Ca(OH) 2 of average diameter of 5-8 mesh; (f) providing an additive solution comprising about 15 to about 20%/w of water, about 2 to about 3%/w of NaOH, about 1 to about 2%/w of KOH and about 0.1 to about 1%/w of CaCl 2 ; and (g) spraying said additive solution onto the granular Ca(OH) 2 from step (e) while stirring gently to provide a substantially even coating of said additive solution of the Ca(OH) 2 .
Claim 7
Dependent Claim
21 words
A method according to claim 4, including the additional step of extruding the paste from step (c) to increase bulk density.
Claim 8
Dependent Claim
21 words
A method according to claim 4, wherein step (d) the drying is effected at about 140° C. for about 12 hours.
Claim 9
Dependent Claim
17 words
A method according to claim 4, wherein step (b) about 70% by weight of water is added.
Claim 10
Dependent Claim
46 words
A method according to claim 4, including the additional step of transferring the coated compound to an air tight enclosure and storing for about two days prior to use at about 4°-20° C. in order to permit stabilization of the activity of the Ca(OH) 2 .
Claim 11
Dependent Claim
52 words
A method according to claim 4, 5 or 8, wherein the CO 2 absorbent material consists essentially of 79.1%/w of granular Ca(OH) 2 of mesh size 5-8 from step (e) and an additive solution consisting essentially of 16.7%/w of water, 2.7%/w of NaOH, 1.4%/w of KOH and 0.1%/w of CaCl 2 .
Claim 12
Dependent Claim
12 words
The carbon dioxide absorbent material produced by the process of claim 2.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-03 | 1987-04-04 | 1987-10-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-03 | 1991-04-04 | 1991-10-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-03 | 1995-04-04 | 1995-10-04 | $7700.00 | Window Closed / Lapsed |