Diffusion bonding of dissimilar ceramics
Assignee: International Business Machines Corp
•
Filing: 1982-05-03
•
Granted: 1983-09-27
•
Expires: 2002-05-03
Abstract
Abstract Diffusion bonding of dissimilar ceramics can be accomplished by the application of pressure only while the ceramics are at a temperature at which their expansion rates are the same. A process for manufacturing magnetic head cores is disclosed where a magnetic ferrite is diffusion bonded to a non-magnetic ceramic by heating the core pieces to the expansion rate crossover temperature and then applying the diffusion bonding pressure. The pressure is removed either before or after the bonded pieces are cooled.
Inventors
- 👤 William W. Chow
- 👤 Eugene B. Rigby
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 05:41
CPC Classifications
C; C04; C04B; C04B37/00; C04B37/001; C04B35/00; C04B35/01; C04B35/46; C04B35/462; C04B35/465; C04B35/468; C04B35/4686; C04B35/622; C04B35/64; C04B35/645; C04B37/003; C04B37/005; G; G11; G11B; G11B5/00; G11B5/127; G11B5/133; G11B5/1335; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/32; C04B2235/3231; C04B2235/3232; C04B2235/3244; C04B2235/34; C04B2235/3418; C04B2235/65; C04B2235/656; C04B2235/6562; C04B2235/6565; C04B2235/6567; C04B2235/70; C04B2235/80; C04B2235/96; C04B2235/9607; C04B2237/00; C04B2237/02; C04B2237/10; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/341; C04B2237/343; C04B2237/345; C04B2237/346; C04B2237/348; C04B2237/36; C04B2237/50; C04B2237/52; C04B2237/62; C04B2237/78; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/4902; Y10T29/49021; Y10T29/49032; Y10T29/49055
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
98 words
A process for diffusion bonding of ceramic pieces respectively consisting of dissimilar ceramic materials having expansion curves with a certain temperature range where the respective thermal expansion curves of each ceramic material intersect, said process comprising the steps of: obtaining the ceramic pieces; placing the obtained ceramic pieces adjacent each other for bonding; heating the placed ceramic pieces to the certain temperature range; applying pressure to the heated ceramic pieces to effect a diffusion bond while maintaining the ceramic pieces at the certain temperature range; removing the applied pressure; and cooling the bonded ceramic pieces to ambient temperature.
Claim 2
Dependent Claim
98 words
A process for diffusion bonding of ceramic pieces respectively consisting of dissimilar ceramic materials having expansion curves with a certain temperature range where the respective thermal expansion curves of each ceramic material intersect, said process comprising the steps of: obtaining the ceramic pieces; placing the obtained ceramic pieces adjacent each other for bonding; heating the placed ceramic pieces to the certain temperature range; applying pressure to the heated ceramic pieces to effect a diffusion bond while maintaining the ceramic pieces at the certain temperature range; removing the applied pressure; and cooling the bonded ceramic pieces to ambient temperature.
Claim 3
Dependent Claim
25 words
A process for diffusion bonding as defined in claim 1 wherein the step of removing the applied pressure is performed before the step of cooling.
Claim 4
Dependent Claim
25 words
A process for diffusion bonding as defined in claim 1 wherein the step of removing the applied pressure is performed after the step of cooling.
Claim 5
Dependent Claim
35 words
A process for diffusion bonding as defined in claim 1 wherein one of said ceramic pieces consists of a non-magnetic ceramic material and a second of said ceramic pieces consists of a magnetic ferrite material.
Claim 6
Dependent Claim
38 words
A process for diffusion bonding ceramic pieces as defined in claim 4 wherein the magnetic ferrite material is manganese-zinc and the non-magnetic ceramic material is taken from the class consisting of magnesium aluminate, zirconia, titania, and barium titanate.
Claim 7
Dependent Claim
29 words
A process for bonding ceramic pieces as defined in claim 5 wherein the bonded ceramic pieces are further bonded to other ceramic pieces to form a magnetic head structure.
Claim 8
Dependent Claim
37 words
A process for diffusion bonding of ceramic pieces as defined in claim 5 wherein the magnetic ferrite material is manganese-zinc and the non-magnetic ceramic material is titania and the certain temperature range is approximately 1000 degrees centigrade.
Claim 9
Dependent Claim
43 words
A process for diffusion bonding of ceramic pieces as defined in claim 5 wherein the magnetic ferrite material is manganese-zinc and the non-magnetic ceramic material is zirconia and the ceramic materials are heated to the certain temperature range of approximately 800 degrees centigrade.
Claim 10
Dependent Claim
45 words
A process for diffusion bonding of ceramic pieces as defined in claim 5 wherein the magnetic ferrite material is manganese-zinc and the non-magnetic ceramic material is magnesium aluminate and wherein the ceramic pieces are heated to the certain temperature range of approximately 1400 degrees centigrade.
Claim 11
Dependent Claim
133 words
A process for making parts of a head core for a magnetic head by the diffusion bonding of a formed magnetic ceramic block to a formed non-magnetic ceramic block with the dissimilar ceramic materials having expansion curves with a certain temperature range where the respective thermal expansion curves of each ceramic material intersect, said process comprising the steps of: obtaining the formed magnetic ceramic block; obtaining the formed non-magnetic ceramic block; placing the obtained ceramic blocks adjacent each other in the bonding configuration; heating the placed ceramic blocks to the certain temperature range; applying pressure for a time period to the heated ceramic blocks to effect a diffusion bond while maintaining the ceramic pieces at the certain temperature range; and removing the applied pressure while cooling the bonded ceramic pieces to ambient temperature.
Claim 12
Dependent Claim
133 words
A process for making parts of a head core for a magnetic head by the diffusion bonding of a formed magnetic ceramic block to a formed non-magnetic ceramic block with the dissimilar ceramic materials having expansion curves with a certain temperature range where the respective thermal expansion curves of each ceramic material intersect, said process comprising the steps of: obtaining the formed magnetic ceramic block; obtaining the formed non-magnetic ceramic block; placing the obtained ceramic blocks adjacent each other in the bonding configuration; heating the placed ceramic blocks to the certain temperature range; applying pressure for a time period to the heated ceramic blocks to effect a diffusion bond while maintaining the ceramic pieces at the certain temperature range; and removing the applied pressure while cooling the bonded ceramic pieces to ambient temperature.
Claim 13
Dependent Claim
39 words
A process for diffusion bonding dissimilar ceramic blocks to form a part of a head core as defined in claim 10 wherein the magnetic ceramic piece is manganese-zinc ferrite and the non-magnetic ceramic block is a barium titanate ceramic.
Claim 14
Dependent Claim
42 words
A process for diffusion bonding of dissimilar ceramic blocks to form a head core as defined in claim 11 wherein the certain temperature range is approximately 900° C. and the pressure applied is 3000 psi for a time period of one hour.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-09-26 | 1987-03-28 | 1987-09-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-09-26 | 1991-03-28 | 1991-09-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-09-26 | 1995-03-28 | 1995-09-27 | $7700.00 | Window Closed / Lapsed |