Video disc processing

Claim 2

In the manufacture of a conductive, high density information disc having video and audio information in the form of geometric variations in an information track which can be reconstituted in electrical signal form with a playback stylus, wherein a conductive plastic is molded to form said high density information disc, the improvement which comprises treating the surfaces of said high density information disc with an ammonium salt selected from the group consisting of ammonium chloride, tetramethyl ammonium chloride, tetramethyl ammonium bromide and ammonium bromide to render the playback quality of said high density information disc substantially resistant to and stable under conditions of high relative humidity.

Claim 3

A process in accordance with claim 1, wherein said ammonium salt is employed in an aqueous solution, said solution containing from about 2 up to about 12 percent by weight of ammonium salt based on the total weight of the treating solution.

Claim 4

A process in accordance with claim 1, wherein said ammonium salt is employed as an aqueous solution of ammonium chloride, said solution containing from about 2 up to about 5 percent by weight of ammonium chloride based on the total weight of the treating solution.

Claim 5

A process in accordance with claim 1, wherein a lubricant is applied to the treated surfaces of said high density information disc.

Claim 6

A process in accordance with claim 4, wherein said lubricant has the formula: ##STR2## wherein x is an integer of about 2-4.

Claim 7

In a method of fabricating a high density information disc replica which comprises dry blending a polyvinylchloride resin with additives including conductive particles, stabilizers, lubricants, and flow modifiers, molding the resultant blend to form a high density information disc replica, and applying a thin lubricant layer to the surfaces of the disc replica, the improvement which comprises treating the surfaces of said high density information disc replica with an ammonium salt selected from the group consisting of ammonium chloride, tetramethyl ammonium chloride, tetramethyl ammonium bromide and ammonium bromide to render the playback quality of said high density information disc replica substantially resistant to, and stable under, conditions of high relative humidity, prior to applying the lubricant layer.

Claim 8

In a method of fabricating a high density information disc replica which comprises dry blending a polyvinylchloride resin with additives including conductive particles, stabilizers, lubricants, and flow modifiers, molding the resultant blend to form a high density information disc replica, and applying a thin lubricant layer to the surfaces of the disc replica, the improvement which comprises treating the surfaces of said high density information disc replica with an ammonium salt selected from the group consisting of ammonium chloride, tetramethyl ammonium chloride, tetramethyl ammonium bromide and ammonium bromide to render the playback quality of said high density information disc replica substantially resistant to, and stable under, conditions of high relative humidity, prior to applying the lubricant layer.

Claim 9

A method in accordance with claim 6, wherein said treating is carried out by employing an aqueous solution of said ammonium salt, said solution containing from about 2 up to about 12 percent by weight of said ammonium salt based on the total weight of the treating solution.

Claim 10

A method in accordance with claim 6, wherein said treating is carried out by employing an aqueous solution of ammonium chloride, said solution containing from about 2 up to about 5 percent by weight of ammonium chloride based on the total weight of said aqueous solution.

Claim 11

A method in accordance with claim 6, wherein said lubricant layer consists essentially of a siloxane of the formula: ##STR3## wherein x is an integer of about 2-4.

Claim 12

A method in accordance with claim 6, wherein said additives include at least 12 percent by weight of the molding composition of conductive carbon black particles.