Abstract A dielectric ceramic material composed of primary and secondary ingredients forming in combination a polycrystalline ceramic proper, and of insulating substances diffused throughout the intergranular boundaries of the ceramic proper for an increase in apparent relative dielectric constant. The primary ingredients comprise, in relative proportions, 90.68-99.88 wt. % SrTiO 3 , 0.07-5.32 wt. % Nb 2 O 5 , and 0.05-4.00 wt. % GeO 2 . The secondary ingredients comprise 0.02-0.10 wt. part SiO 2 and 0.01-0.03 wt. part Al 2 O 3 with respect to 100 wt. parts of the primary ingredients, with the weight ratio of SiO 2 to Al 2 O 3 being from 1.5 to 5.0. The insulating substances comprise 0.03-2.90 wt. % PbO, 0.11-4.34 wt. % Bi 2 O 3 , and 0.001-0.18 wt. % B 2 O 3 with respect to the total weight of the primary and the secondary ingredients. In the fabrication of bodies of the ceramic the mixture of the insulating substances is coated or otherwise layered on polycrystalline ceramic bodies prepared from the primary and secondary ingredients. The coated ceramic bodies are then heated to cause diffusion of the insulating substances throughout their intergranular boundaries.
An insulated boundary layer ceramic having primary and secondary ingredients forming in combination a polycrystalline ceramic proper, and insulating substances dispersed throughout the intergranular boundaries of the ceramic proper, the primary ingredients consisting essentially of, in relative proportions, from about 90.68 to about 99.88 percent by weight SrTiO 3 , from about 0.07 to about 5.32 percent by weight of Nb 2 O 5 , and from about 0.05 to about 4.00 percent by weight GeO 2 , the secondary ingredients consisting essentially of from about 0.02 to about 0.10 part by weight SiO 2 and from about 0.01 to about 0.03 part by weight Al 2 O 3 with respect to 100 parts by weight of the primary ingredients, the ratio in weight of SiO 2 to Al 2 O 3 being from about 1.5 to about 5.0, and the insulating substances consisting essentially of from about 0.03 to about 2.90 percent by weight PbO, from about 0.11 to about 4.34 percent by weight Bi 2 O 3 , and from about 0.001 to about 0.18 percent by weight B 2 O 3 , the percentages of the insulating substances being all with respect to the total weight of the primary and the seconary ingredients.
Claim 2
Dependent Claim
206 words
An insulated boundary layer ceramic having primary and secondary ingredients forming in combination a polycrystalline ceramic proper, and insulating substances dispersed throughout the intergranular boundaries of the ceramic proper, the primary ingredients consisting essentially of, in relative proportions, from about 90.68 to about 99.88 percent by weight SrTiO 3 , from about 0.07 to about 5.32 percent by weight of Nb 2 O 5 , and from about 0.05 to about 4.00 percent by weight GeO 2 , the secondary ingredients consisting essentially of from about 0.02 to about 0.10 part by weight SiO 2 and from about 0.01 to about 0.03 part by weight Al 2 O 3 with respect to 100 parts by weight of the primary ingredients, the ratio in weight of SiO 2 to Al 2 O 3 being from about 1.5 to about 5.0, and the insulating substances consisting essentially of from about 0.03 to about 2.90 percent by weight PbO, from about 0.11 to about 4.34 percent by weight Bi 2 O 3 , and from about 0.001 to about 0.18 percent by weight B 2 O 3 , the percentages of the insulating substances being all with respect to the total weight of the primary and the seconary ingredients.