Claim 2

A coated fabric comprising a fabric of continuous multifilament threads, the fabric having a density ranging between 26% and 60%, a first coating applied to the fabric and a second coating applied over the first coating, the first and second coating each comprising a mix of a dispersable elastic and/or thermoplastic substance with a highly crosslinked duroplastic substance, the proportion of the elastic and/or thermoplastic substance to highly crosslinked duroplastic substance in each mix varying from the first coating to the second coating.

Claim 3

A coated fabric according to claim 1, wherein the amount of elastic and/or thermoplastic substance in the mix of the first coating is one to four parts by weight per one part by weight of highly crosslinked duroplastic substance, and the amount of elastic and/or thermoplastic substance in the mix of the second coating is less than one part by weight per one part by weight of highly crosslinked duroplastic substance.

Claim 4

A plastic coated fabric according to claim 1, characterized in that the elastic and/or thermoplastic substance is 1.5 to 2 parts by weight of the highly crosslinked duroplastic substance.

Claim 5

A coated fabric according to claims 1 or 2, wherein the fabric has a density that ranges between 32% to 42%.

Claim 6

A coated fabric according to claims 1 or 2, wherein the fabric has a modulus <4% and 8%, respectively, when measured at 55 daN/5 cm and 90 daN/5 cm, respectively.

Claim 7

A coated fabric according to claim 5, wherein the modulus of the fabric when measured at 55 daN/5 cm and 90 daN/5 cm is less than 2% and 4%, respectively.

Claim 8

A coated fabric according to claim 6, wherein the modulus of the fabric when measured at 55 daNa/5 cm and 90 daN/5 cm is less than 1% and 2%, respectively.

Claim 9

A coated fabric according to claim 1, wherein the fabric consists of polyester threads having surfaces activated and roughened by an alkaline reaction promoter.

Claim 10

A coated fabric according to claim 1, wherein the fabric is composed of aramid threads.

Claim 11

A coated fabric according to claim 1, wherein the highly crosslinked duroplastic substance is a phenol-formaldehyde resin and the elastic and/or thermoplastic substance is an acrylic resin.

Claim 12

A coated fabric according to claim 1, further comprising a layer of abrasives bonded to said second coating.

Claim 13

A coated fabric according to claim 1, wherein said mix of the first coating contains 1.05 to 10 times as much of the elastic and/or thermoplastic substance as the second coating.

Claim 14

A coated fabric according to claim 1, wherein said highly crosslinked duroplastic substance is a duroplast selected from the group consisting of polyimide resin, phenolic resin, unsaturated by saturated polyester resin, epoxy resin, and acrylic resin.

Claim 15

A coated fabric according to claim 10, wherein said fabric is comprised of polyethylene terephthalate.

Claim 16

A coated fabric according to claim 14, wherein the mix for forming the first coating also contains a chemical reaction promoter for activating and roughing the surface of a multifilament thread of the fabric to improve adhesion.

Claim 17

A coated fabric according to claim 1, wherein at least the mix of the first coating contains a chemical reaction promotor for activating and roughening the surface of the multifilament threads in order to improve adhesion and said mix of the first coating containing a larger proportion of the reaction promotor than the mix of the second coating, based in each base on the total quantity of each mix.

Claim 18

A coated fabric according to claim 1, wherein the mix for forming the first coating also contains a chemical reaction promotor for activating and roughening the surface of a multifilament spread of the fabric to improve adhesion.

Claim 19

A coated fabric according to claim 1, wherein the content of the elastic and/or thermoplastic substance in the mix of the first coating is from one to four parts by weight per one part by weight of the highly crosslinked duroplastic substance and at least the mix of the first coating contains a chemical reaction promotor for activating and roughening the surface of the multicomponent threads of the fabric in order to improve adhesion, the mix of the first coating containing a larger proportion of the chemical reaction promotor than the mix of the second coating, based in each case on the total quantity of each mix.

Claim 20

A process for the manufacture of a polymer coated fabric which comprises applying two different coatings of a mix of dispersable elastic and/or thermoplastic substance with a highly crosslinked duroplastic substance in succession to the front and/or back side of the fabric, said fabric being formed of continuous multifilament threads and having a fabric density ranging between 26% and 60%, at least the mix for the first coating, in which the content of the elastic and/or thermoplastic substance is from one to four parts by weight per one part by weight of the highly crosslinked duroplastic substance, having been admixed with a reaction promoter for activating and roughening the surface of the multifilament threads in order to improve adhesion, and the mix for the first coating containing a larger proportion of the chemical reaction promoter than the mix for the second coating, based in each case on the total quantity of each mix.

Claim 21

A process for the manufacture of a polymer coated fabric which comprises applying two different coatings of a mix of dispersable elastic and/or thermoplastic substance with a highly crosslinked duroplastic substance in succession to the front and/or back side of the fabric, said fabric being formed of continuous multifilament threads and having a fabric density ranging between 26% and 60%, at least the mix for the first coating, in which the content of the elastic and/or thermoplastic substance is from one to four parts by weight per one part by weight of the highly crosslinked duroplastic substance, having been admixed with a reaction promoter for activating and roughening the surface of the multifilament threads in order to improve adhesion, and the mix for the first coating containing a larger proportion of the chemical reaction promoter than the mix for the second coating, based in each case on the total quantity of each mix.

Claim 22

A process according to claim 19, wherein the fabric is a fabric of polyester threads and the mix for the first coating is adjusted to a pH range between 8 and 14 and the mix for the second coating is adjusted to a pH range between 7 and 14.

Claim 23

A process according to claim 19, wherein the mix of the first coating is adjusted to a pH range between 10 and 14 and the mix for the second coating is adjusted to a pH range between 8 and 12.

Claim 24

A process according to claim 19, wherein the mix for the first coating is adjusted to a pH range between 12 and 13, and the mix for the second coating is adjusted by a pH range between 9 and 11.