US4404734A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making a CdS/Cux S photovoltaic cell
Assignee: TOTAL ENERGIE DEVELOPPEMENT
•
Filing: 1982-08-02
•
Granted: 1983-09-20
•
Expires: 2002-08-02
Abstract
Abstract A photovoltaic cell is formed by combining a spray process, forming a crystalline layer containing cadmium and sulfur, and an evaporation process, depositing copper chloride for converting to CuxS. The crystals containing cadmium and sulfur are heated in an atmosphere of cadmium and chlorides to obtain crystals having at least one dimension greater than 0.5 micron and a planar layer of CuxS is formed on the large crystals. A layer of CuxS having a thickness of 0.5-1.0 micron is obtained. Electrodes are formed from evaporated gold or chromium or a metallic paste including silver or copper. ZnxCd1-xS may be substituted for CdS through at least part of the crystalline layer for improved Voc.
Inventors
- 👤 Vijay P. Singh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 06:01
CPC Classifications
H; H10; H10F; H10F71/00; H10F71/125; H10F10/00; H10F10/10; H10F10/16; H10F10/169; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/543
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
128 words
A process for forming photovoltaic cells, comprising: spraying onto a heated electrically conductive film of SnO x on a transparent vitreous substrate at least one solution effective to form a crystalline film containing cadmium and sulphur, exposing said crytalline film to a heated vapor effective to recrystallize said crystalline film to form crystals having at least one dimension greater than 0.5 microns, vacuum evaporating a copper chloride layer onto said recrystallized film, and heating to convert a portion of said recrystallized film to Cu x S to a thickness between about 0.5 to 1.0 microns, thereby forming a heterojunction and associated depletion layer with a remaining portion of said recrystallized film, said remaining portion having a thickness effective to separate said depletion layer from said electrically conductive film.
Claim 2
Dependent Claim
128 words
A process for forming photovoltaic cells, comprising: spraying onto a heated electrically conductive film of SnO x on a transparent vitreous substrate at least one solution effective to form a crystalline film containing cadmium and sulphur, exposing said crytalline film to a heated vapor effective to recrystallize said crystalline film to form crystals having at least one dimension greater than 0.5 microns, vacuum evaporating a copper chloride layer onto said recrystallized film, and heating to convert a portion of said recrystallized film to Cu x S to a thickness between about 0.5 to 1.0 microns, thereby forming a heterojunction and associated depletion layer with a remaining portion of said recrystallized film, said remaining portion having a thickness effective to separate said depletion layer from said electrically conductive film.
Claim 3
Dependent Claim
19 words
A process according to claim 1, further including: forming at least a portion of said crystalline film from CdS.
Claim 4
Dependent Claim
57 words
A process according to claim 2, further including: forming an adherent film to a thickness less than 0.3 micron adjacent said substrate film of SnO x having an aluminum content effective to adhere to said film of SnO x and said portion of said crystalline film of CdS, and forming said crystalline film over said adherent film.
Claim 5
Dependent Claim
40 words
A process according to claim 2, further including: forming a first portion of said crystalline film adjacent said substrate from CdS, and forming a second portion of said crystalline film over said first portion from Zn x Cd 1-x S.
Claim 6
Dependent Claim
22 words
A process according to claim 1, including: forming at least a portion of said crystalline film from Zn x Cd 1-x S.
Claim 7
Dependent Claim
24 words
A process according to claim 1, 2, or 5, further including: forming at least a portion of said crystalline film to include residual chlorides.
Claim 8
Dependent Claim
27 words
A process according to claim 6, wherein exposing said film to a heated vapor includes: providing an atmosphere including cadmium and chloride vapors adjacent said crystalline film.
Claim 9
Dependent Claim
44 words
A process according to claim 7, wherein providing said atmosphere includes: placing a covering plate in spaced facing relationship with said crystalline film, and heating at least said crystalline film to form said cadmium and chloride vapors from constituent portions of said crystalline film.
Claim 10
Dependent Claim
44 words
A process according to claim 7, wherein providing said atmosphere includes: placing two substrates with said crystalline films in a spaced facing relationship, and heating at least said crystalline films to form said cadmium and chloride vapors from constituent portions of said crystalline film.
Claim 11
Dependent Claim
38 words
A process according to claim 7, wherein providing said atmosphere includes: introducing said substrate having said crystalline film into a substantially sealed container, and enriching the atmosphere within said container with heated vapors containing cadmium and chloride vapors.
Claim 12
Dependent Claim
59 words
A process according to claim 1, 2, or 5, wherein converting said recrystallized film to Cu x S includes: heating said copper chloride layer and said recrystallized film to a temperature greater than about 90° C. and less than 300° C. and for a time effective to react substantially all of said copper chloride to obtain Cu x S.
Claim 13
Dependent Claim
23 words
A process according to claim 11, wherein said heating produces a substrate temperature of 190°-230° C. over a time interval of 11-20 minutes.
Claim 14
Dependent Claim
19 words
A process according to claim 11, including the step of subjecting said substrate to a vacuum during said heating.
Claim 15
Dependent Claim
26 words
A process according to claim 11, wherein said heating includes: heating said copper chloride layer and said recrystallized film in an atmosphere containing hydrogen or nitrogen.
Claim 16
Dependent Claim
19 words
A process according to claim 14, including heating to a temperature of about 185° C. for about 18 minutes.
Claim 17
Dependent Claim
26 words
A process according to claim 1, 2, or 5, further including the step of forming an electrode layer substantially covering said film of Cu x S.
Claim 18
Dependent Claim
26 words
A process according to claim 16, wherein forming said electrode layer includes vacuum evaporating a metallic material selected from the group consisting of chromium and gold.
Claim 19
Dependent Claim
29 words
A process according to claim 16, wherein forming said electrode layer includes applying a metallic paste containing a metallic material selected from the group consisting of copper or silver.
Claim 20
Dependent Claim
39 words
A process according to claim 1, 2 or 5, further including the step of forming at least a portion of said crystalline film with a dopant in an amount effective to produce a selected resistivity in said recrystallized film.
Claim 21
Dependent Claim
11 words
A process according to claim 20, wherein said dopant includes indium.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-09-19 | 1987-03-21 | 1987-09-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-09-19 | 1991-03-21 | 1991-09-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-09-19 | 1995-03-21 | 1995-09-20 | $7700.00 | Window Closed / Lapsed |