Process of preparing copolymer of lower carboxylic acid and ester thereof

Claim 2

A one-pot process for preparing an alcoholic solution of a copolymer of an unsaturated monocarboxylic acid and an ester thereof, said copolymer having the structure ##STR3## wherein, R 1 represents hydrogen and methyl; R 2 represents methyl, ethyl, propyl, and butyl; x represents from 2 to 50 weight percent (wt %) based on the combined weight of x and y; y represents from 50 to 98 wt % based on the combined weight of x and y; and, the sum of the numerical values of x+y is always 100 and the groups x and y are present in an heterogenous relative order, said process comprising, (a) reacting a reaction mixture comprising (meth)acrylic acid, and optionally ester(s) thereof, and a lower aliphatic monohydric alcohol R 2 OH, wherein R 2 has the same meaning as above in the presence of an acid esterification catalyst and a polymerization initiator, at the reflux temperature of said reaction mixture, (b) removing the water formed from the reaction, and (c) recovering an alcoholic solution of said copolymer.

Claim 3

The process of claim 1 comprising, after removing said water, neutralizing said esterification catalyst in said reaction mixture, and removing a desired portion of said lower aliphatic alcohol by azeotropic distillation.

Claim 4

The process of claim 2 wherein neutralizing said esterification catalyst in said reaction mixture is effected with a neutralizing agent selected from the group consisting of ammonia, hydrazine, a low boiling primary aliphatic amine, a low boiling secondary aliphatic amine, and a low boiling tertiary aliphatic amine.

Claim 5

The method of claim 3 wherein said lower aliphatic alcohol is isopropanol and said neutralizing agent is ammonia.

Claim 6

The method of claim 3 wherein said lower aliphatic alcohol is 1-butanol and said neutralizing agent is ammonia.

Claim 7

A one-pot process for preparing an alcoholic solution of a copolymer of an unsaturated monocarboxylic acid and an ester thereof, said copolymer having the structure ##STR4## wherein, R 1 represents hydrogen and methyl; R 2 represents methyl, ethyl, propyl, and butyl; x represents from 2 to 50 weight percent (wt %) based on the combined weight of x and y; y represents from 50 to 98 wt % based on the combined weight of x and y; and, the sum of the numerical values of x+y is always 100 and the groups x and y are present in a heterogenous relative order, said process comprising, (a) esterifying by heating to reflux a mixture comprising (meth)acrylic acid and a lower aliphatic monohydric alcohol R 2 OH, wherein R 2 has the same meaning as above, in the presence of an esterification catalyst to form an ester, (b) removing the water formed from the esterification reaction, thereafter (c) adding polymerization initiator and optionally (meth)acrylate to form a reaction mixture and reacting said reaction mixture at the reflux temperature of said reaction mixture, and (d) recovering an alcoholic solution of said copolymer.

Claim 8

A one-pot process for preparing an alcoholic solution of a copolymer of an unsaturated monocarboxylic acid and an ester thereof, said copolymer having the structure ##STR4## wherein, R 1 represents hydrogen and methyl; R 2 represents methyl, ethyl, propyl, and butyl; x represents from 2 to 50 weight percent (wt %) based on the combined weight of x and y; y represents from 50 to 98 wt % based on the combined weight of x and y; and, the sum of the numerical values of x+y is always 100 and the groups x and y are present in a heterogenous relative order, said process comprising, (a) esterifying by heating to reflux a mixture comprising (meth)acrylic acid and a lower aliphatic monohydric alcohol R 2 OH, wherein R 2 has the same meaning as above, in the presence of an esterification catalyst to form an ester, (b) removing the water formed from the esterification reaction, thereafter (c) adding polymerization initiator and optionally (meth)acrylate to form a reaction mixture and reacting said reaction mixture at the reflux temperature of said reaction mixture, and (d) recovering an alcoholic solution of said copolymer.

Claim 9

The process of claim 6 comprising, after removing said water, neutralizing said esterification catalyst in said reaction mixture with a neutralizing agent selected from the group consisting of ammonia, hydrazine, a low boiling primary aliphatic amine, a low boiling secondary aliphatic amine, and a low boiling tertiary aliphatic amine.

Claim 10

A one-pot process for preparing an alcoholic solution of a copolymer of an unsaturated monocarboxylic acid and an ester thereof, said copolymer having the structure ##STR5## wherein, R 1 and R 1 ' represent hydrogen and methyl; R 2 and R 2 ' represent methyl, ethyl, propyl, and butyl; x represents from 2 to 50 weight percent (wt %) based on the combined weight of x, y 1 and y 2 ; y 1 and y 2 together represent from 50 to 98 wt % based on the combined weight of x, y 1 and y 2 ; and, the sum of the numerical values of x+y 1 +y 2 is always 100 and the groups x, y 1 and y 2 are present in a heterogenous relative order, said process comprising, (a) reacting a reaction mixture comprising (meth)acrylic acid, a lower aliphatic monohydric alcohol R 2 OH, wherein R 2 has the same meaning as above, and an additional ester CH 2 ═C(R' 1 )-COOR' 2 , wherein R' 1 and R' 2 have the said meaning as above in the presence of an acid esterification catalyst and a polymerization initiator, at the reflux temperature of said reaction mixture, (b) removing the water formed from the reaction, and (c) recovering an alcoholic solution of said copolymer.

Claim 11

A one-pot process for preparing an alcoholic solution of a copolymer of an unsaturated monocarboxylic acid and an ester thereof, said copolymer having the structure ##STR5## wherein, R 1 and R 1 ' represent hydrogen and methyl; R 2 and R 2 ' represent methyl, ethyl, propyl, and butyl; x represents from 2 to 50 weight percent (wt %) based on the combined weight of x, y 1 and y 2 ; y 1 and y 2 together represent from 50 to 98 wt % based on the combined weight of x, y 1 and y 2 ; and, the sum of the numerical values of x+y 1 +y 2 is always 100 and the groups x, y 1 and y 2 are present in a heterogenous relative order, said process comprising, (a) reacting a reaction mixture comprising (meth)acrylic acid, a lower aliphatic monohydric alcohol R 2 OH, wherein R 2 has the same meaning as above, and an additional ester CH 2 ═C(R' 1 )-COOR' 2 , wherein R' 1 and R' 2 have the said meaning as above in the presence of an acid esterification catalyst and a polymerization initiator, at the reflux temperature of said reaction mixture, (b) removing the water formed from the reaction, and (c) recovering an alcoholic solution of said copolymer.

Claim 12

The process of claim 8 comprising, after removing said water, neutralizing said esterification catalyst in said reaction mixture with a neutralizing agent selected from the group consisting of ammonia, hydrazine, a low boiling primary aliphatic amine, a low boiling secondary aliphatic amine, and a low boiling tertiary aliphatic amine.

Claim 13

The process of claim 9 wherein said lower aliphatic alcohol is ethanol, said (meth)acrylic acid is acrylic acid, said additional ester is methylmethacrylate and said neutralizing agent is ammonia.