Process for coating optical fibers
Assignee: Applied Science Group Inc
•
Filing: 1981-03-20
•
Granted: 1983-09-06
•
Expires: 2001-03-20
Abstract
Abstract Vitreous optical fibers provided with hermetically sealed coatings applied by method and apparatus comprising; drawing a fiber directly from a fiber extruder into and through an elongated chamber having inert gas air locks at its opposite ends. Between the air locks, the optical fiber passes successively through a series of evacuated chamber sections comprising: first, a plasma-ion milling zone wherein fiber surface contaminants are removed and microscopic surface defects are diminished; second, a carbon film depositing zone wherein elemental carbon, propelled in plasma-ion form, coats the surface of fiber with a diamond-like elemental carbon film of submicron thickness; third, an elemental metal film depositing zone wherein a selected metal such as indium, tin, aluminum or gold is plasma deposited onto the fiber to form a coating of less than micron thickness; and finally a second metal depositing zone wherein a coating, in the order of microns in thickness, of such a selective metal is applied by immersing and passing the fiber through a more condensed molecular form of the metal.
Inventors
- 👤 Sol Aisenberg
- 👤 Martin L. Stein
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:21
CPC Classifications
C; C03; C03C; C03C25/00; C03C25/10; C03C25/104
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
127 words
A process for the application of at least one imprevious film of elemental coating material continuously about the outer surface of a moving vitreous optical fiber, which process comprises the steps of: (a) substantially evacuating the ambient oxygen from the surrounding inert gas about said moving fiber; (b) plasma ion milling the outer surface of said moving fiber while said fiber is in the substantial vacuum caused by said evacuation step; and (c) thereafter, depositing a film of between about five to less than one thousand Angstroms in thickness of elemental material evenly about the outer surface of said fiber while maintaining said reduced atmospheric pressure, said film depositing step through high energy plasma transfer of ions of said elemental material in said substantially oxygen-free created vacuum.
Claim 2
Dependent Claim
127 words
A process for the application of at least one imprevious film of elemental coating material continuously about the outer surface of a moving vitreous optical fiber, which process comprises the steps of: (a) substantially evacuating the ambient oxygen from the surrounding inert gas about said moving fiber; (b) plasma ion milling the outer surface of said moving fiber while said fiber is in the substantial vacuum caused by said evacuation step; and (c) thereafter, depositing a film of between about five to less than one thousand Angstroms in thickness of elemental material evenly about the outer surface of said fiber while maintaining said reduced atmospheric pressure, said film depositing step through high energy plasma transfer of ions of said elemental material in said substantially oxygen-free created vacuum.
Claim 3
Dependent Claim
16 words
The process of claim 1, wherein at least the first elemental material is a non-metallic element.
Claim 4
Dependent Claim
18 words
A process as defined in claim 2 wherein said non-metallic elemental film is a crystalline form of carbon.
Claim 5
Dependent Claim
47 words
A process as defined in claim 2 including the additional step of: (e) passing said fiber through an energetic beam of plasma ions of a metal after said first elemental film is plasma deposited and before said fiber is passed through said liquid supply of molten metal.
Claim 6
Dependent Claim
21 words
The method as defined in claim 4 wherein said metallic plasma ions are of the same metal as said molten liquid.
Claim 7
Dependent Claim
14 words
The process of claim 1, wherein at least one elemental material is a metal.
Claim 8
Dependent Claim
24 words
The process of claim 1, wherein at least one elemental material is a metal selected from the group consisting of indium, tin and aluminum.
Claim 9
Dependent Claim
40 words
A process as defined in claim 7 including the additional step of: (d) passing said moving fiber through a liquid supply of molten metal whereby said molten metal forms a final metal coating over said earlier plasma deposited metallic film.
Claim 10
Dependent Claim
24 words
A process as defined in claim 8 wherein said molten metal is a metal selected from the group consisting of indium, tin and aluminum.
Claim 11
Dependent Claim
152 words
The process of rendering the surface of a moving vitreous optical fiber impervious to atmospheric attack, which process comprises the steps of: (a) evacuating ambient oxygen from gases about said fiber surface to create an inert gas volume of reduced pressure through which said fiber is passed; (b) plasma ion milling the surface of said fibers in said inert reduced atmosphere to remove loosely bound contaminants from said surface; (c) directing a high energy carbon ion plasma in said inert reduced atmosphere toward said moving fiber to deposit first on said fiber surface a non-metallic elemental diamond-like carbon film, said film holding deposited atoms in an evenly distributed, tightly bound lattice with film thickness of from more than about five to less than one thousand Angstroms; and, (d) thereafter depositing at least on enveloping coating of elemental metal about said film while said film is moving through said inert reduced pressure atomsphere.
Claim 12
Dependent Claim
152 words
The process of rendering the surface of a moving vitreous optical fiber impervious to atmospheric attack, which process comprises the steps of: (a) evacuating ambient oxygen from gases about said fiber surface to create an inert gas volume of reduced pressure through which said fiber is passed; (b) plasma ion milling the surface of said fibers in said inert reduced atmosphere to remove loosely bound contaminants from said surface; (c) directing a high energy carbon ion plasma in said inert reduced atmosphere toward said moving fiber to deposit first on said fiber surface a non-metallic elemental diamond-like carbon film, said film holding deposited atoms in an evenly distributed, tightly bound lattice with film thickness of from more than about five to less than one thousand Angstroms; and, (d) thereafter depositing at least on enveloping coating of elemental metal about said film while said film is moving through said inert reduced pressure atomsphere.
Claim 13
Dependent Claim
24 words
The process as defined in claim 10, wherein the elemental metal coating deposited is selected from the group consisting of indium, tin and aluminum.
Claim 14
Dependent Claim
209 words
A process for continuous production of a vitreous optical fiber of substantially cylindrical cross-section whose surface has been rendered impervious to attack, which process comprises the steps of: (a) feeding a vitreous fiber of indeterminate length through a vacuum lock into an inert gas environment having a pressure of less than about 1×10 -6 atmospheres; (b) while said fiber is progressing through said vacuum environment, plasma milling the surface of said fiber with plasma created ions propelled under high energy excitation against the milled surface of said moving fiber; (c) subjecting said milled surface of said moving fiber to an additional ionic plasma environment containing carbon ions thereby depositing a first surface coating film of diamond-like crystalline carbon on said moving milled surface of said fiber, (d) depositing a second continuous film of metal in elemental form about said carbon film by exposure of said fiber to a second high energy plasma metal-ion procedure; (e) exposing said plasma deposited metal film on said moving fiber to a further vacuum-vapor deposition of a compatible metal; and, (f) thereafter, depositing a third coating on said vitreous fiber by running said moving fiber through a molten mass of said compatible metal thereby to increase the thickness of the earlier deposited metallic film.
Claim 15
Dependent Claim
209 words
A process for continuous production of a vitreous optical fiber of substantially cylindrical cross-section whose surface has been rendered impervious to attack, which process comprises the steps of: (a) feeding a vitreous fiber of indeterminate length through a vacuum lock into an inert gas environment having a pressure of less than about 1×10 -6 atmospheres; (b) while said fiber is progressing through said vacuum environment, plasma milling the surface of said fiber with plasma created ions propelled under high energy excitation against the milled surface of said moving fiber; (c) subjecting said milled surface of said moving fiber to an additional ionic plasma environment containing carbon ions thereby depositing a first surface coating film of diamond-like crystalline carbon on said moving milled surface of said fiber, (d) depositing a second continuous film of metal in elemental form about said carbon film by exposure of said fiber to a second high energy plasma metal-ion procedure; (e) exposing said plasma deposited metal film on said moving fiber to a further vacuum-vapor deposition of a compatible metal; and, (f) thereafter, depositing a third coating on said vitreous fiber by running said moving fiber through a molten mass of said compatible metal thereby to increase the thickness of the earlier deposited metallic film.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-09-05 | 1987-03-07 | 1987-09-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-09-05 | 1991-03-07 | 1991-09-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-09-05 | 1995-03-07 | 1995-09-06 | $7700.00 | Window Closed / Lapsed |