US4402992A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Covering solid, film cooled surfaces with a duplex thermal barrier coating
Assignee: National Aeronautics and Space Administration
•
Filing: 1981-12-07
•
Granted: 1983-09-06
•
Expires: 2001-12-07
Abstract
Abstract This invention is directed to applying thermal barrier coating systems to hardware having passageways in the walls connecting apertures in the surface to a gas supply for film cooling. An inert gas, such as argon, is discharged through the apertures during the application of the thermal barrier coating system by plasma spraying. This flow of inert gas reduces both blocking of the holes and base metal oxidation during the coating operation.
Inventors
- 👤 Curt H. Liebert
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 04:35
CPC Classifications
C; C23; C23C; C23C4/00; C23C4/02; C23C4/01; C23C4/12; C23C4/134; B; B23; B23P; B23P2700/00; B23P2700/06
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
123 words
A method of applying a thermal barrier coating system to a member having a plurality of passages therein extending from a surface thereof to a plenum chamber to accommodate an outward flow of fluid to provide film cooling in a high temperature environment comprising the steps of supplying a fluid under pressure to said plenum chamber whereby said fluid flows outward through said passages, plasma spraying a metal bond coat onto said surface having the passages therein while said fluid flows through said passages, and depositing a thermal barrier coating material on said metal bond coat while said fluid flows through said passages whereby entry of said coating material into said passages is prevented thereby inhibiting blockage thereof and reducing base metal oxidation.
Claim 2
Independent Claim
123 words
A method of applying a thermal barrier coating system to a member having a plurality of passages therein extending from a surface thereof to a plenum chamber to accommodate an outward flow of fluid to provide film cooling in a high temperature environment comprising the steps of supplying a fluid under pressure to said plenum chamber whereby said fluid flows outward through said passages, plasma spraying a metal bond coat onto said surface having the passages therein while said fluid flows through said passages, and depositing a thermal barrier coating material on said metal bond coat while said fluid flows through said passages whereby entry of said coating material into said passages is prevented thereby inhibiting blockage thereof and reducing base metal oxidation.
Claim 3
Dependent Claim
39 words
A method of applying a thermal barrier coating system as claimed in claim 1 including the step of roughening said surface of said member having the pasages therein prior to plasma spraying the metal bond coating onto said surface.
Claim 4
Dependent Claim
27 words
A method of applying a thermal barrier coating system as claimed in claim 1 wherein the fluid under pressure in the plenum chamber is an inert gas.
Claim 5
Dependent Claim
20 words
A method of applying a thermal barrier coating system as claimed in claim 3 wherein the inert gas is argon.
Claim 6
Dependent Claim
27 words
A method of applying a thermal barrier coating system as claimed in claim 4 wherein the argon gas is suppled under a pressure of about 80 psia.
Claim 7
Dependent Claim
34 words
A method of applying a thermal barrier coating system as claimed in claim 5 wherein the mass flow rate of the argon through the passages is between about 0.005 and 0.015 lb m /second.
Claim 8
Dependent Claim
29 words
A method of applying a thermal barrier coating system as claimed in claim 1 wherein the metal bond coat is selected from the group consisting of NiCrAlY and CoCrAlY.
Claim 9
Dependent Claim
52 words
A method of applying a thermal barrier coating system as claimed in claim 7 wherein the surface having the passages therein is curved and the metal bond coat is deposited on said curved surface to a thickness between about 0.002 inch and 0.004 inch while the fluid is passing through the passages.
Claim 10
Dependent Claim
28 words
A method of applying a thermal barrier coating system as claimed in claim 1 wherein a ceramic material is deposited on the metal bond coat by plasma spraying.
Claim 11
Dependent Claim
22 words
A method of applying a thermal barrier coating system as claimed in claim 9 wherein the ceramic material is yttria stabilized zirconia.
Claim 12
Dependent Claim
32 words
A method of applying a thermal barrier coating system as claimed in claim 10 whrein the yttria stabilized zirconia is plasma sprayed to a thickness between about 0.004 inch and 0.010 inch.
Claim 13
Dependent Claim
23 words
A method of applying a thermal barrier coating system as claimed in claim 11 including the step of polishing the exposed ceramic surface.
Claim 14
Dependent Claim
29 words
A method of applying a thermal barrier coating system as claimed in claim 12 wherein the ceramic surface is polished to a roughness of 1 to 3 micrometers (RMS).
References Cited (Backward Citations)
US3450558A
Cited
US3892883A
Cited
US4050133A
Cited
US4095003A
Cited
US4248940A
Cited
US4251599A
Cited
US4338360A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-09-05 | 1987-03-07 | 1987-09-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-09-05 | 1991-03-07 | 1991-09-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-09-05 | 1995-03-07 | 1995-09-06 | $7700.00 | Window Closed / Lapsed |