Homogeneous liquid barium carbonate-barium alkyl phenate-cadmium carboxylate stabilizer systems for rigid polyvinyl chloride resins
Assignee: Argus Chemical Corp
•
Filing: 1981-12-31
•
Granted: 1983-08-30
•
Expires: 2001-12-31
Abstract
Abstract Homogeneous liquid stabilizer systems imparting to polyvinyl chloride resins a heat and light stability comparable to or exceeding organotin stabilizers are provided which are substantially solvent-free and have a low viscosity and a minimum flash point of 96° C., containing as the essential and only stabilizers a liquid barium carbonate-barium alkyl phenate and a cadmium salt of a branched chain aliphatic carboxylic acid having from about eight to about ten carbon atoms, optionally as a mixture of at least 85% cadmium salt of a branched chain aliphatic carboxylic acid with up to about 15% of a cadmium salt of an aromatic carboxylic acid having from about seven to about eleven carbon atoms, and/or of a saturated or unsaturated straight chain aliphatic carboxylic acid having from about nine to about twenty-two carbon atoms, the total weight percent of barium and cadmium in the stabilizer system being at least 18%, and the ratio of the weight percent of cadmium to the weight percent of barium being within the range from about 0.4:1 to about 1.2:1.
Inventors
- 👤 Kook J. Bae
- 👤 Lawrence R. Brecker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 10:29
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/18; C08K3/24; C08K3/26; C08K5/00; C08K5/04; C08K5/09; C08K5/098; C08K5/13; C08K5/138
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
183 words
A homogeneous liquid stabilizer system imparting heat and light stability to polyvinyl chloride resins and which is substantially solvent-free and has a low viscosity and a minimum flash point of 96° C., consisting as the essential and only stabilizers of (1) a liquid barium carbonate-barium alkyl phenate and (2) a cadmium salt of a carboxylic acid selected from the group consisting of branched chain aliphatic carboxylic acids having from about eight to about ten carbon atoms, and mixtures thereof in an amount of at least about 85% with up to about 15% of one or more cadmium salts of aromatic carboxylic acids having from about seven to about eleven carbon atoms, and saturated and unsaturated straight chain aliphatic carboxylic acids having from about twelve to about twenty-two carbon atoms, the total weight preferred of barium and cadmium in the stabilizer system being at least 18%, and the ratio of the weight percent of cadmium to the weight percent of barium being within the range from about 0.4:1 to about 1.2:1, the barium and cadmium salts being in amounts to form a homogeneous liquid.
Claim 2
Dependent Claim
183 words
A homogeneous liquid stabilizer system imparting heat and light stability to polyvinyl chloride resins and which is substantially solvent-free and has a low viscosity and a minimum flash point of 96° C., consisting as the essential and only stabilizers of (1) a liquid barium carbonate-barium alkyl phenate and (2) a cadmium salt of a carboxylic acid selected from the group consisting of branched chain aliphatic carboxylic acids having from about eight to about ten carbon atoms, and mixtures thereof in an amount of at least about 85% with up to about 15% of one or more cadmium salts of aromatic carboxylic acids having from about seven to about eleven carbon atoms, and saturated and unsaturated straight chain aliphatic carboxylic acids having from about twelve to about twenty-two carbon atoms, the total weight preferred of barium and cadmium in the stabilizer system being at least 18%, and the ratio of the weight percent of cadmium to the weight percent of barium being within the range from about 0.4:1 to about 1.2:1, the barium and cadmium salts being in amounts to form a homogeneous liquid.
Claim 3
Dependent Claim
23 words
A stabilizer system according to claim 1 in which the cadmium salt is a salt of a mixture of aliphatic and aromatic acids.
Claim 4
Dependent Claim
22 words
A stabilizer system according to claim 2 in which the aliphatic acid is 2-ethylhexoic acid and the aromatic acid is benzoic acid.
Claim 5
Dependent Claim
27 words
A stabilizer system according to claim 1 in which the cadmium salt is a salt of a mixture of aliphatic branched chain and aliphatic straight chain acids.
Claim 6
Dependent Claim
22 words
A stabilizer system according to claim 4 in which the branched chain acid is 2-ethylhexoic and the straight chain acid is oleic.
Claim 7
Dependent Claim
22 words
A stabilizer system according to claim 4 in which the branched chain acid is 2-ethylhexoic and the straight chain acid is stearic.
Claim 8
Dependent Claim
22 words
A stabilizer system according to claim 4 in which the branched chain acid is 2-ethylhexoic and the straight chain acid is isostearic.
Claim 9
Dependent Claim
22 words
A stabilizer system according to claim 4 in which the branched chain acid is 2-ethylhexoic and the straight chain acid is lauric.
Claim 10
Dependent Claim
39 words
A stabilizer system according to claim 1 in which the liquid barium carbonate-alkyl phenate comprises barium carbonate combined with at least one barium alkyl phenate in a monvolatile organic liquid which acts as a liquefying agent for the carbonate.
Claim 11
Dependent Claim
27 words
A stabilizer system according to claim 9 in which the organic liquid is selected from the group consisting of hydrocarbon oils, plasticizers, epoxy esters, and mixtures thereof.
Claim 12
Dependent Claim
29 words
A stabilizer system according to claim 1 in which the metal ratio of barium carbonate to barium alkyl phenate is a number within the range from 2 to 20.
Claim 13
Dependent Claim
30 words
A stabilizer system according to claim 1 in which the alkyl phenate residue of the barium alkyl phenate has at least ten up to about one hundred fifty carbon atoms.
Claim 14
Dependent Claim
36 words
A stabilizer system according to claim 1 in which the ratio of total barium to the organic moiety in the barium carbonate-barium alkyl phenate is greater than the stoichiometric ratio of the neutral barium alkyl phenate.
Claim 15
Dependent Claim
25 words
A stabilizer system according to claim 13 in which the barium carbonate-barium alkyl phenate is barium carbonate-barium dodecyl phenate containing from 23 to 29% Ba.
Claim 16
Dependent Claim
16 words
A stabilizer system according to claim 1 in which the cadmium carboxylate salt is a liquid.
Claim 17
Dependent Claim
22 words
A stabilizer system according to claim 15 in which the cadmium salt is a salt of 2-ethyl hexoic acid and benzoic acid.
Claim 18
Dependent Claim
73 words
A stabilizer system according to claim 1 in which the cadmium carboxylate salt is liquefied in course of preparation, by carrying out the formation of the salt in the presence of a high-boiling organic solvent for the resulting cadmium carboxylate, this solvent accompanying the salt in the stabilizer system in an amount not exceeding 12% solvent by weight of the stabilizer system, after combination of the liquefied cadmium carboxylate with the other components.
Claim 19
Dependent Claim
42 words
A stabilizer system according to claim 17 in which the solvent is selected from the group consisting of aliphatic, cycloaliphatic and aromatic hydrocarbons; and aliphatic, cycloaliphatic and aromatic alcohols, ether alcohols, and ether alcohol esters; and esters of organic and inorganic acids.
Claim 20
Dependent Claim
66 words
A polyvinyl chloride resin composition having improved resistance to deterioration when heated at 350° F., comprising a polyvinyl chloride resin formed at least in part of the recurring group: ##STR2## and having a chlorine content in excess of 40%, where X is either hydrogen or chlorine; and an amount to enhance the resistance to deterioration of the resin of a stabilizer composition according to claim 1.
Claim 21
Dependent Claim
20 words
A polyvinyl chloride resin composition in accordance with claim 19 in which the polyvinyl chloride resin is polyvinyl chloride homopolymer.
Claim 22
Dependent Claim
25 words
A polyvinyl chloride resin composition in accordance with claim 19 in which the polyvinyl chloride resin is a copolymer of vinyl chloride and vinyl acetate.
Claim 23
Dependent Claim
66 words
A polyvinyl chloride resin composition having improved resistance to deterioration when heated at 350° F., comprising a polyvinyl chloride resin formed at least in part of the recurring group: ##STR3## and having a chlorine content in excess of 40%, where X is either hydrogen or chlorine; and an amount to enhance the resistance to deterioration of the resin of a stabilizer composition according to claim 2.
Claim 24
Dependent Claim
66 words
A polyvinyl chloride resin composition having improved resistance to deterioration when heated at 350° F., comprising a polyvinyl chloride resin formed at least in part of the recurring group: ##STR4## and having a chlorine content in excess of 40%, where X is either hydrogen or chlorine; and an amount to enhance the resistance to deterioration of the resin of a stabilizer composition according to claim 4.
Claim 25
Dependent Claim
28 words
A polyvinyl chloride resin composition according to claim 19 which is formulated as a rigid polyvinyl chloride resin to withstand a processing temperature of at least 375° F.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-08-29 | 1987-02-28 | 1987-08-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-08-29 | 1991-02-28 | 1991-08-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-08-29 | 1995-02-28 | 1995-08-30 | $7700.00 | Window Closed / Lapsed |