Abstract A process for producing a crosslinked polyethylene insulated cable having an outer semiconductive layer which comprises providing an internal semiconductive layer, and an electrically insulating layer on an electrical conductor in conventional manner, coating by extrusion a resin composition comprising 100 parts by weight of an ethylene/vinyl acetate copolymer having a vinyl acetate content of at least about 55% by weight and about 5 to about 100 parts by weight of carbon black and a crosslinking effective amount of a crosslinking agent on said electrically insulating layer and heating said coated composition to at least about 230 DEG C. to crosslink said resin composition is disclosed. This process assures high production speed. When the ethylene/vinyl acetate copolymer used has a vinyl acetate content of at least about 80% by weight the outer semiconductive layer can easily be peeled off by hand.
A process for producing a crosslinked polyethylene insulated cable having an outer semiconductive layer which comprises providing an internal semiconductive layer, and an electrically insulating layer on an electrical conductor in conventional manner, coating by extrusion a resin composition comprising 100 parts by weight of an ethylene/vinyl acetate copolymer having a vinyl acetate content of at least about 55% by weight and about 5 to about 100 parts by weight of carbon black and a crosslinking effective amount of a crosslinking agent on said electrically insulating layer and heating said coated composition to at least about 250° C. in a nitrogen atmosphere to crosslink said resin composition.
Claim 2
Dependent Claim
107 words
A process for producing a crosslinked polyethylene insulated cable having an outer semiconductive layer which comprises providing an internal semiconductive layer, and an electrically insulating layer on an electrical conductor in conventional manner, coating by extrusion a resin composition comprising 100 parts by weight of an ethylene/vinyl acetate copolymer having a vinyl acetate content of at least about 55% by weight and about 5 to about 100 parts by weight of carbon black and a crosslinking effective amount of a crosslinking agent on said electrically insulating layer and heating said coated composition to at least about 250° C. in a nitrogen atmosphere to crosslink said resin composition.
Claim 3
Dependent Claim
21 words
The process of claim 1, wherein said ethylene/vinyl acetate copolymer has a vinyl content of at least about 80% by weight.
Claim 4
Dependent Claim
12 words
A crosslinked polyethylene insulated cable produced by the process of claim 1.
Claim 5
Dependent Claim
12 words
A crosslinked polyethylene insulated cable produced by the process of claim 2.
Claim 6
Dependent Claim
26 words
The process of claim 1, wherein from about 0.3 to about 2 wt% of said crosslinking agent is present, based on the weight of the resin.
Claim 7
Dependent Claim
17 words
The process of claim 1, wherein said crosslinking is conducted at a temperature up to 290° C.
Claim 8
Dependent Claim
13 words
The process of claim 1, wherein said temperature is at least 270° C.
Claim 9
Dependent Claim
13 words
The process of claim 7, wherein said temperature is up to 290° C.