Plating resist with improved resistance to extraneous plating

Claim 2

A photohardenable resist composition comprising polymerizable organic binder, a photoinitiator capable of initiating polymerization of said binder upon exposure to actinic radiation, and an effective amount, greater than 1% by weight, of aluminum oxide microparticles dispersed throughout said binder, said aluminum oxide microparticles being made by the flame hydrolysis of anhydrous aluminum halide.

Claim 3

A composition according to claim 1 wherein said aluminum oxide is about 1 to 30% by weight of the total weight of said composition.

Claim 4

A composition according to claim 1 wherein said aluminum oxide is about 10 to 30% by weight of the total weight of said composition.

Claim 5

A composition according to claim 1 wherein said binder comprises epoxide.

Claim 6

A composition according to claim 1 wherein said binder comprises acrylate monomer.

Claim 7

A composition according to claim 1 wherein said binder comprises vinyl prepolymer.

Claim 8

A composition according to claim 1 wherein said binder comprises an epoxide, said photoinitiator comprises triarylsulfonium hexafluoroantimonate, and said aluminum oxide is about 10 to 20% by weight of the total weight of said composition.

Claim 9

A composition according to claim 1 further comprising an amount of fumed silica sufficient to impart to said composition a shear thinning index number greater than about 1.25.

Claim 10

A composition according to claim 1 wherein said aluminum oxide microparticles are made by the flame hydrolysis of anhydrous aluminum chloride and have a primary particle size less than about 0.1 micrometer in diameter.

Claim 11

A photohardenable resist composition comprising epoxide, triarylsulfonium hexafluoroantimonate, and about 10 to 20% by weight of fumed aluminum oxide microparticles made by the flame hydrolysis of anhydrous aluminum chloride.

Claim 12

A photohardenable resist composition comprising epoxide, triarylsulfonium hexafluoroantimonate, and about 10 to 20% by weight of fumed aluminum oxide microparticles made by the flame hydrolysis of anhydrous aluminum chloride.

Claim 13

A dry film negative photoresist composition comprising (1) carrier film and (2) a photosensitive layer carried on said film that is adherable to a printed circuit board substrate, reacts when exposed to an imagewise pattern of light to provide imagewise differential removability from said substrate, and comprises (a) photopolymerizable organic binder, (b) a catalytic amount of photoinitiator for initiating imagewise reaction of said binder upon imagewise exposure of said photosensitive layer to light, and (c) an effective amount, greater than 1% by weight, of aluminum oxide microparticles dispersed throughout said binder, said aluminum oxide microparticles being made by the flame hydrolysis of anhydrous aluminum halide.

Claim 14

A dry film negative photoresist composition comprising (1) carrier film and (2) a photosensitive layer carried on said film that is adherable to a printed circuit board substrate, reacts when exposed to an imagewise pattern of light to provide imagewise differential removability from said substrate, and comprises (a) photopolymerizable organic binder, (b) a catalytic amount of photoinitiator for initiating imagewise reaction of said binder upon imagewise exposure of said photosensitive layer to light, and (c) an effective amount, greater than 1% by weight, of aluminum oxide microparticles dispersed throughout said binder, said aluminum oxide microparticles being made by the flame hydrolysis of anhydrous aluminum halide.

Claim 15

A composition according to claim 11 wherein said aluminum oxide is about 1 to 30% by weight of the total weight of said composition.

Claim 16

A composition according to claim 12 wherein said aluminum oxide microparticles are made by the flame hydrolysis of anhydrous aluminum chloride and have a primary particle size less than about 0.1 micrometer in diameter.

Claim 17

A dry film positive photoresist composition comprising (1) carrier film and (2) a photosensitive layer carried on said film that is adherable to a printed circuit board substrate, reacts when exposed to an imagewise pattern of light to provide imagewise differential removability from said substrate, and comprises (a) photosolubilizable organic binder, (b) a catalytic amount of photoinitiator for initiating imagewise reaction of said binder upon imagewise exposure of said photosensitive layer to light, and (c) an effective amount, greater than 1% by weight, of aluminum oxide microparticles dispersed throughout said binder, said aluminum oxide microparticles being made by the flame hydrolysis of anhydrous aluminum halide.

Claim 18

A dry film positive photoresist composition comprising (1) carrier film and (2) a photosensitive layer carried on said film that is adherable to a printed circuit board substrate, reacts when exposed to an imagewise pattern of light to provide imagewise differential removability from said substrate, and comprises (a) photosolubilizable organic binder, (b) a catalytic amount of photoinitiator for initiating imagewise reaction of said binder upon imagewise exposure of said photosensitive layer to light, and (c) an effective amount, greater than 1% by weight, of aluminum oxide microparticles dispersed throughout said binder, said aluminum oxide microparticles being made by the flame hydrolysis of anhydrous aluminum halide.

Claim 19

A composition according to claim 10 wherein said aluminum oxide is about 1 to 30% by weight of the total weight of said composition.

Claim 20

A composition according to claim 15 wherein said aluminum oxide microparticles are made by the flame hydrolysis of anhydrous aluminum chloride and have a primary particle size less than about 0.1 micrometer in diameter.

Claim 21

A hardenable resist composition comprising an organic binder and from about 4 to 14% weight of the total weight of said composition of aluminum oxide microparticles dispersed throughout said binder, said aluminum oxide microparticles being made by the flame hydrolysis of anhydrous aluminum halide.

Claim 22

A hardenable resist composition comprising an organic binder and from about 4 to 14% weight of the total weight of said composition of aluminum oxide microparticles dispersed throughout said binder, said aluminum oxide microparticles being made by the flame hydrolysis of anhydrous aluminum halide.

Claim 23

A printed circuit board having a plating resist pattern comprising a hardenable resist composition comprising an organic binder and an effective amount, greater than 1% by weight, of aluminum oxide microparticles dispersed throughout said binder, said aluminum oxide microparticles being made by the flame hydrolysis of anhydrous aluminum halide.

Claim 24

A printed circuit board having a plating resist pattern comprising a hardenable resist composition comprising an organic binder and an effective amount, greater than 1% by weight, of aluminum oxide microparticles dispersed throughout said binder, said aluminum oxide microparticles being made by the flame hydrolysis of anhydrous aluminum halide.

Claim 25

A printed circuit board in accordance with claim 18, wherein said plating resist pattern is hardened.

Claim 26

A printed circuit board having a plating resist pattern comprising a photohardenable resist composition according to claim 1.

Claim 27

A printed circuit board in accordance with claim 20, wherein said plating resist pattern is hardened.

Claim 28

A printed circuit board having a plating resist pattern comprising a photohardenable resist composition according to claim 10.

Claim 29

A printed circuit board in accordance with claim 22, wherein said plating resist pattern is hardened.