Abstract
Abstract A storable cement product is a dry mixture of magnesium oxide (MgO) and aluminum phosphate, or a product containing MgO and, separated therefrom, an aqueous aluminum phosphate solution, some or all of an inert aggregate component optionally being present in either product. In 45-kg samples, the mortar formed when the MgO, phosphate, water, and aggregate are combined attains an exotherm in the range of about 40°-90° C. after an interval of 10 minutes. The mortar hardens quickly thereafter, and is uniquely suited for patching roads under varying conditions of application and use. The reaction exotherm is controlled by a unique combination of the concentrations of the four critical components, and the surface area and particle size of the MgO.
Inventors
- 👤 Ernst A. Tomic
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 17:08
CPC Classifications
C; C04; C04B; C04B40/00; C04B40/06; C04B40/0641; C04B40/065; C04B2111/00; C04B2111/00474; C04B2111/0075
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
175 words
A storable cement product containing (a) magnesium oxide in the form of particles which have a surface area of less than about 1 square meter per gram, and up to 90 percent of which pass through a 200-mesh screen and 10 percent of which are held on a 170-mesh or coarser screen; and (b) aluminum phosphate; components (a) and (b) being adapted to be combined with water and an inert aggregate of mixed particle sizes in amounts such as to form a mixture therewith comprising, by weight, about from 3 to 25 percent of component (a), about from 10 to 15 percent of component (b), about from 5 to 10 percent water, and about from 50 to 82 percent aggregate, and thereupon to undergo a reaction which raises the temperature of a 45-kilogram sample of the mixture to a peak temperature in the range of about from 40° to 90° C. at a rate such that said peak temperature is reached after the elapse of at least 10 minutes after the formation of said mixture.
Claim 2
Dependent Claim
175 words
A storable cement product containing (a) magnesium oxide in the form of particles which have a surface area of less than about 1 square meter per gram, and up to 90 percent of which pass through a 200-mesh screen and 10 percent of which are held on a 170-mesh or coarser screen; and (b) aluminum phosphate; components (a) and (b) being adapted to be combined with water and an inert aggregate of mixed particle sizes in amounts such as to form a mixture therewith comprising, by weight, about from 3 to 25 percent of component (a), about from 10 to 15 percent of component (b), about from 5 to 10 percent water, and about from 50 to 82 percent aggregate, and thereupon to undergo a reaction which raises the temperature of a 45-kilogram sample of the mixture to a peak temperature in the range of about from 40° to 90° C. at a rate such that said peak temperature is reached after the elapse of at least 10 minutes after the formation of said mixture.
Claim 3
Dependent Claim
52 words
A cement product of claim 1 wherein up to about 50 percent of said magnesium oxide particles pass through a 200-mesh screen and 10 percent are held on a 35-mesh or coarser screen, and said mixture comprises, by weight, up to about 10 percent magnesium oxide and at least 60 percent aggregate.
Claim 4
Dependent Claim
40 words
A cement product of claim 1 in the form of a dry mix of magnesium oxide and aluminum phosphate, said reaction between components (a) and (b) being adapted to occur when said product is combined with said aggregate and water.
Claim 5
Dependent Claim
34 words
A cement product of claim 3 consisting essentially of about from 24 to 63 percent by weight of said magnesium oxide and about from 37 to 76 percent by weight of said aluminum phosphate.
Claim 6
Dependent Claim
43 words
A mortar comprising the cement product of claim 3 freshly combined with water and an inert aggregate of mixed particle sizes in amounts such as to form said mixture therewith, a 45-kilogram sample of said mortar being workable for at least 10 minutes.
Claim 7
Dependent Claim
40 words
A cement product of claim 1 in the form of a dry mix of magnesium oxide, aluminum phosphate, and inert aggregate, said reaction between components (a) and (b) being adapted to occur when said product is combined with said water.
Claim 8
Dependent Claim
36 words
A cement product of claim 6 consisting essentially of about from 3 to 27 percent magnesium oxide, about from 11 to 16 percent aluminum phosphate, and about from 58 to 86 percent aggregate, all by weight.
Claim 9
Dependent Claim
54 words
A cement product of claim 6 consisting essentially of about from 4 to 37 percent magnesium oxide, about from 15 to 22 percent aluminum phosphate, and about from 54 to 81 percent sand, all by weight, said reaction between components (a) and (b) being adapted to occur when said product is combined with gravel.
Claim 10
Dependent Claim
36 words
A mortar comprising the cement product of claim 6 freshly combined with water in an amount such as to form said mixture therewith, a 45-kilogram sample of said mortar being workable for at least 10 minutes.
Claim 11
Dependent Claim
71 words
A cement product of claim 3 or claim 6 wherein up to about 20 percent of said magnesium oxide particles pass through a 200-mesh screen and 10 percent are held on an 18-mesh or coarser screen, and the magnesium oxide content, by weight, of said water- and aggregate-containing mixture is about from 10 to 25 percent, components (a) and (b) being adapted to react at ambient temperatures above about 20° C.
Claim 12
Dependent Claim
75 words
A cement product of claim 3 or claim 6 wherein up to about 40 percent of said magnesium oxide particles pass through a 200-mesh screen and 10 percent are held on a 20-mesh or coarser screen, and the magnesium oxide content, by weight, of said water- and aggregate-containing mixture is about from 3 to 10 percent, components (a) and (b) being adapted to react at ambient temperatures of about from 10° C. to 20° C.
Claim 13
Dependent Claim
69 words
A cement product of claim 3 or claim 6 wherein up to about 60 percent of said magnesium oxide particles pass through a 200-mesh screen and 10 percent are held on a 35-mesh screen, and the magnesium oxide content, by weight, of said water- and aggregate-containing mixture is about from 3 to 10 percent, components (a) and (b) being adapted to react at ambient temperatures below about 10° C.
Claim 14
Dependent Claim
37 words
A cement product of claim 1 containing said water as a component which is separated from said magnesium oxide, said reaction between components (a) and (b) being adapted to occur when they are combined with said water.
Claim 15
Dependent Claim
15 words
A cement product of claim 13 wherein said aluminum phosphate is present in aqueous solution.
Claim 16
Dependent Claim
42 words
A cement product of claim 14 consisting essentially of, by weight, about from 3 to 10 percent magnesium oxide, about from 10 to 15 percent aluminum phosphate, about from 50 to 82 percent aggregate, and about from 5 to 10 percent water.
Claim 17
Dependent Claim
18 words
A cement product of claim 14 wherein said magnesium oxide and said aluminum phosphate solution are separately packaged.
Claim 18
Dependent Claim
38 words
A mortar comprising the cement product of claim 13 freshly mixed so as to combine said water with the remainder thereof to form said mixture, a 45-kilogram sample of said mortar being workable for at least 10 minutes.
Claim 19
Dependent Claim
53 words
A cement product of claim 14 wherein up to about 90 percent of said magnesium oxide particles pass through a 200-mesh screen and 10 percent are held on a 170-mesh or coarser screen, and the magnesium oxide content, by weight, of said water- and aggregate-containing mixture is about from 3 to 10 percent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-07-18 | 1987-01-17 | 1987-07-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-07-18 | 1991-01-17 | 1991-07-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-07-18 | 1995-01-17 | 1995-07-19 | $7700.00 | Window Closed / Lapsed |