Opacifying polymeric particle and uses

Claim 2

A latex coating composition of improved opacity and film characteristics, said coating composition comprising discrete capsules comprising a solid polymeric core surrounded by a solid polymeric shell having a Tg less than about 45° C., wherein the weight ratio of said shell to the total weight of said capsule ranges from 0.25:1 to 0.5:1.

Claim 3

An aqueous latex dispersion paint composition which forms at ambient temperatures into a hardened paint film, said latex paint having about 40% to 70% by weight total solids comprising on a dry solids weight basis: a. 10-25% of a film forming latex binder; b. 2-25% of an opacifying organic particle comprising discrete capsules comprising a solid polymeric core surrounded by a solid polymeric shell having a Tg less than about 45° C., wherein the weight ratio of said shell to the total weight of particle ranges from 0.25:1 to 0.5:1; c. 15 to 40% opacifying pigment having a refractive index of at least about 1.8; d. 0 to 70% of extender pigment having refractive index below about 1.5.

Claim 4

An aqueous latex dispersion paint composition which forms at ambient temperatures into a hardened paint film, said latex paint having about 40% to 70% by weight total solids comprising on a dry solids weight basis: a. 10-25% of a film forming latex binder; b. 2-25% of an opacifying organic particle comprising discrete capsules comprising a solid polymeric core surrounded by a solid polymeric shell having a Tg less than about 45° C., wherein the weight ratio of said shell to the total weight of particle ranges from 0.25:1 to 0.5:1; c. 15 to 40% opacifying pigment having a refractive index of at least about 1.8; d. 0 to 70% of extender pigment having refractive index below about 1.5.

Claim 5

An aqueous latex dispersion paint composition which forms at ambient temperatures into a hardened paint film, said paint film having opacity and film characteristics substantially equivalent to a first film formed from a first composition containing pigment and binder wherein x is weight in pounds of said pigment in said first composition, y is weight in pounds of said binder in said first composition, said paint composition containing pigment, binder and an opacifying organic particle comprising discrete capsules comprising a solid polymeric core surrounded by a solid polymeric shell having a Tg less than about 45° C., the weight ratio of said shell to the total weight of said capsule ranges from 0.25:1 to 0.5:1, wherein x' is the weight difference in pounds of the pigment between said first composition and said paint composition, y' is the weight difference in pounds of the binder between said first composition and said paint composition and z is the weight in pounds of said particles in said paint composition, x' ranges from about 0.1x to about 0.5x; y' ranges from about 0.1y to about 0.6y; and z ranges from about 0.3(x'+y') to about 0.9(x'+y').

Claim 6

An aqueous latex dispersion paint composition which forms at ambient temperatures into a hardened paint film, said paint film having opacity and film characteristics substantially equivalent to a first film formed from a first composition containing pigment and binder wherein x is weight in pounds of said pigment in said first composition, y is weight in pounds of said binder in said first composition, said paint composition containing pigment, binder and an opacifying organic particle comprising discrete capsules comprising a solid polymeric core surrounded by a solid polymeric shell having a Tg less than about 45° C., the weight ratio of said shell to the total weight of said capsule ranges from 0.25:1 to 0.5:1, wherein x' is the weight difference in pounds of the pigment between said first composition and said paint composition, y' is the weight difference in pounds of the binder between said first composition and said paint composition and z is the weight in pounds of said particles in said paint composition, x' ranges from about 0.1x to about 0.5x; y' ranges from about 0.1y to about 0.6y; and z ranges from about 0.3(x'+y') to about 0.9(x'+y').

Claim 7

The composition of claim 1, 2 or 3 wherein said cores range in diameter from about 0.3 to about 1.0 micron.

Claim 8

The composition of claim 4 wherein said cores range in diameter from about 0.4 to about 0.8 micron.

Claim 9

The composition of claim 5 wherein said shell to said capsule weight ratio ranges from 0.4:1 to 0.45:1.

Claim 10

The composition of claim 1, 2 or 3 wherein said core is formed of polymeric material having a T g greater than about 80° C. and said shell is formed of a uncrosslinked polymeric material having a T g less than 45° C.

Claim 11

The composition of claim 7 wherein the T g material of said core ranges from 80° C. to about 120° C.

Claim 12

The composition of claim 7 wherein the material of said shell has a T g ranging from -45° C. to +30° C.

Claim 13

The composition of claim 1, 2 or 3 wherein said material of said core is selected from a group consisting of methyl methacrylate, vinyl chloride, acrylonitrile and polystyrene.

Claim 14

The composition of claim 10 wherein said material of said core comprises polystyrene.

Claim 15

The composition of claim 1, 2 or 3 wherein the material in said shell is selected from a group consisting of copolymers of acrylate, methyl acrylate, styrene and vinyl acetate.

Claim 16

The composition of claim 1, 2 or 3 wherein the particles are monodisperse.

Claim 17

The composition of claim 1, 2 or 3 wherein said composition forms a film upon drying, said film contains voids and said voids ranges from about 0.2 to about 0.5 micron in diameter.

Claim 18

The composition of claim 1, 2 or 3 wherein said core is formed of a crosslinked polymeric material having a T g greater than about 70° C.

Claim 19

The composition of claim 3 wherein said x' ranges from about 0.2x to about 0.4x, y' ranges from 0.2y to about 0.4y, and z is about 0.5(x'+y').