Assignee: SCHMELZBASALTWERK AKLENBORN DR ING MAURITZ KG
•
Filing: 1980-09-02
•
Granted: 1983-07-05
•
Expires: 2000-09-02
Abstract
Abstract A process for fixing wear-resistant armoring tiles to cement mortar. In accordance with the process, the back sides of the tiles are coated with a mixture of polyester epoxy resin composition including sand and quartz or sand powder, with a curing agent. A material having an affinity for the cement mortar (like quartz sand or lavalite) is dusted and rolled into the coated back side of the tiles, so as to thoroughly be mixed up with the resin mixture coating. After the hardening of the coating including the material having affinity to cement mortar, the tiles are embedded in the cement mortar. Accordingly, this process substantially eliminates the well known poor adhesive properties of such tiles with respect to cement mortar.
Inventors
- 👤 Wilhelm Kramer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 16:09
CPC Classifications
B; B65; B65G; B65G11/00; B65G11/16; B65G11/166; C; C04; C04B; C04B26/00; C04B26/02; C04B26/10; C04B2111/00; C04B2111/00474; C04B2111/00482; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1089; Y10T156/1092; Y10T428/00; Y10T428/16; Y10T428/163; Y10T428/164; Y10T428/166; Y10T428/31504; Y10T428/31511; Y10T428/31515; Y10T428/31522
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
261 words
A process for fixing in position on a cement mortar coated supporting structure wear-resistant lining tiles of ceramic, fused mineral and metallic material for highly abrasive bulk material such as coal ores and rock, said process comprising: cleaning the back side to be coated of each of said tiles, applying an epoxy-containing coating to the cleaned back side of said tiles, said epoxy-containing coating having a thickness of 1.5-2 mm and consisting of a resin mixture and a curing agent mixed at a ratio of 100 to 17, the curing temperature for said epoxy-containing coating being in the range of 290-310 K.°, the resin mixture consisting of 36.9 parts by weight epoxy resin, 25.2 parts by weight of fine sand, 34.9 parts by weight of quartz sand powder, 1.0 parts by weight of thixotropic agent, and 2.0 parts by weight of conducting carbon stock, dusting and rolling in the epoxy-containing coated back side of said tiles a layer of material having an affinity for cement mortar, the material being selected from the group consisting of quartz sand, lavalite and broken expanded clay, with a grain size of 1-3 mm, said material being rolled into the epoxy-containing coated back side of said tiles at a pressure of 1 to 2 N/square mm, and following the rolling in of said material, hardening said epoxy-containing coating, placing and fixing in position said coated tiles on the cement mortar coated supporting structure and filling up the spaces between said tiles by a pointing compound, so as to produce a high shear strength in said tiles.
Claim 2
Dependent Claim
261 words
A process for fixing in position on a cement mortar coated supporting structure wear-resistant lining tiles of ceramic, fused mineral and metallic material for highly abrasive bulk material such as coal ores and rock, said process comprising: cleaning the back side to be coated of each of said tiles, applying an epoxy-containing coating to the cleaned back side of said tiles, said epoxy-containing coating having a thickness of 1.5-2 mm and consisting of a resin mixture and a curing agent mixed at a ratio of 100 to 17, the curing temperature for said epoxy-containing coating being in the range of 290-310 K.°, the resin mixture consisting of 36.9 parts by weight epoxy resin, 25.2 parts by weight of fine sand, 34.9 parts by weight of quartz sand powder, 1.0 parts by weight of thixotropic agent, and 2.0 parts by weight of conducting carbon stock, dusting and rolling in the epoxy-containing coated back side of said tiles a layer of material having an affinity for cement mortar, the material being selected from the group consisting of quartz sand, lavalite and broken expanded clay, with a grain size of 1-3 mm, said material being rolled into the epoxy-containing coated back side of said tiles at a pressure of 1 to 2 N/square mm, and following the rolling in of said material, hardening said epoxy-containing coating, placing and fixing in position said coated tiles on the cement mortar coated supporting structure and filling up the spaces between said tiles by a pointing compound, so as to produce a high shear strength in said tiles.
Claim 3
Dependent Claim
36 words
The process as claimed in claim 1, further comprising applying a conducting epoxy-containing coating and working the coating into any small pores in the back side of the tiles so as to completely coat the same.
Claim 4
Dependent Claim
63 words
The process as claimed in claim 1, in which, within a time period of 20 minutes after applying the epoxy-containing coating to the back side of said tiles, dusting and rolling into the coated back side of said tiles, round-grained quartz sand having a grain size of 2 to 3 mm, and using more material than is needed for fully covering said tiles.
Claim 5
Dependent Claim
61 words
The process as claimed in claim 1, in which, within a time period of 20 minutes after applying the epoxy-containing coating to the back side of said tiles, dusting and rolling into the coated back side of said tiles, lavalite with a grain size of 2 to 3 mm, and using more material than is needed for fully covering said tiles.
Claim 6
Dependent Claim
34 words
The process as claimed in claim 1, in which said tiles are fixed to a cement mortar composition having plastic material additives that increase water retention, strength and adhesive properties of the mortar composition.
Claim 7
Dependent Claim
33 words
The process as claimed in claim 1, in which said epoxy-containing coating is conductive and said material is thoroughly mixed with said epoxy-containing coating, but without inactivating the surface of said epoxy-containing coating.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-07-04 | 1987-01-03 | 1987-07-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-07-04 | 1991-01-03 | 1991-07-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-07-04 | 1995-01-03 | 1995-07-05 | $7700.00 | Window Closed / Lapsed |