Process for molding fiber loaded rubber compound
Assignee: Goodrich Corp
•
Filing: 1981-07-13
•
Granted: 1983-06-21
•
Expires: 2001-07-13
Abstract
Abstract A process for making an elastomeric compound that has chopped fibers dispersed throughout the compound with orientation of the chopped fibers to increase the modulus and strength of the compound by milling the fiber loaded compound to break up the fibers and thereafter mold and then vulcanize the resulting product.
Inventors
- 👤 James W. Messerly
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 10:32
CPC Classifications
B; B29; B29C; B29C70/00; B29C70/04; B29C70/06; B29C70/10; B29C70/12; B29C70/14; B29K; B29K2021/00; B29L; B29L2031/00; B29L2031/709
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
103 words
A process for the molding of a fiber loaded rubber compound comprising the steps of introducing chopped fibers having lengths with a range which averages between one and two inches into a rubber compound, milling said fibers and rubber compound to break up said fibers during milling to a length that ranges between 0.3 and 0.0625 inches while orientating said fibers in a longitudinal direction to form a fiber loaded rubber compound, placing said fiber loaded rubber compound into a mold, molding said fiber loaded compound in said mold to a desired shape, and removing said molded fiber loaded compound from said mold.
Claim 2
Dependent Claim
103 words
A process for the molding of a fiber loaded rubber compound comprising the steps of introducing chopped fibers having lengths with a range which averages between one and two inches into a rubber compound, milling said fibers and rubber compound to break up said fibers during milling to a length that ranges between 0.3 and 0.0625 inches while orientating said fibers in a longitudinal direction to form a fiber loaded rubber compound, placing said fiber loaded rubber compound into a mold, molding said fiber loaded compound in said mold to a desired shape, and removing said molded fiber loaded compound from said mold.
Claim 3
Dependent Claim
28 words
A process as set forth in claim 1 wherein said milling of said fibers with said rubber compound provides orientation and entanglement of said fibers within said compound.
Claim 4
Dependent Claim
22 words
A process as set forth in claim 2 wherein said fibers have a length that is greater than one and one-fourth inches.
Claim 5
Dependent Claim
97 words
A process of molding a fiber loaded rubber compound comprising the steps of: chopping staple fibers into fibers having lengths generally greater than 1.25 inches, introducing said chopped fibers into a rubber compound, milling said fiber loaded rubber compound to disperse said fibers throughout and reduce the lengths of said fibers to a range between 0.3 to 0.062 inches, introducing said milled fiber loaded rubber compound into a mold having a predetermined shaped cavity, molding said compound in said mold wherein said molded compound is vulcanized in said mold, and removing the finished article from said mold.
Claim 6
Dependent Claim
97 words
A process of molding a fiber loaded rubber compound comprising the steps of: chopping staple fibers into fibers having lengths generally greater than 1.25 inches, introducing said chopped fibers into a rubber compound, milling said fiber loaded rubber compound to disperse said fibers throughout and reduce the lengths of said fibers to a range between 0.3 to 0.062 inches, introducing said milled fiber loaded rubber compound into a mold having a predetermined shaped cavity, molding said compound in said mold wherein said molded compound is vulcanized in said mold, and removing the finished article from said mold.
Claim 7
Dependent Claim
34 words
A process of molding a fiber loaded rubber compound as set forth in claim 4 wherein said fiber loaded compound is shaped into a v-belt product, and said product is vulcanized as a v-belt.
Claim 8
Dependent Claim
20 words
A process of molding a fiber loaded compound as set forth in claim 5 wherein said rubber compound is neoprene.
Claim 9
Dependent Claim
86 words
A process for molding a V-belt comprising the steps of introducing fibers having lengths generally greater than 1.25 inches into an elastomeric compound, milling said fiber loaded elastomeric compound to break up said fibers during milling to a length that ranges between 0.3 and 0.0625 inches and to disperse said fibers throughout said compound, shaping said milled fiber loaded compound into a belt having a V-shaped cross section, placing said V-shaped compound into a mold, and thence vulcanizing said fiber loaded compound into a belt product.
Claim 10
Dependent Claim
86 words
A process for molding a V-belt comprising the steps of introducing fibers having lengths generally greater than 1.25 inches into an elastomeric compound, milling said fiber loaded elastomeric compound to break up said fibers during milling to a length that ranges between 0.3 and 0.0625 inches and to disperse said fibers throughout said compound, shaping said milled fiber loaded compound into a belt having a V-shaped cross section, placing said V-shaped compound into a mold, and thence vulcanizing said fiber loaded compound into a belt product.
Claim 11
Dependent Claim
22 words
A process as set forth in claim 7 wherein said milling shears said fibers and provide an orientated entanglement of said fibers.
Claim 12
Dependent Claim
18 words
A process as set forth in claim 8 wherein said fibers have a diameter of approximately 11 microns.
Claim 13
Dependent Claim
22 words
A process as set forth in claim 9 wherein said mixture of fibers to elastomer is fifty parts to one hundred parts.
Claim 14
Dependent Claim
13 words
A process as set forth in claim 10 wherein said fibers are rayon.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-06-20 | 1986-12-20 | 1987-06-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-06-20 | 1990-12-20 | 1991-06-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-06-20 | 1994-12-20 | 1995-06-21 | $7700.00 | Window Closed / Lapsed |