Dibenzylidene sorbitol composition and process for preparation thereof
Assignee: Ec Chemical Ind Co Ltd
•
Filing: 1981-07-13
•
Granted: 1983-06-14
•
Expires: 2001-07-13
Abstract
Abstract A composition consisting essentially of solid powdery dibenzylidene sorbitol and a higher fatty acid, the surface of the dibenzylidene sorbitol being coated with the higher fatty acid; and a process for producing dibenzylidene sorbitol powder having a coating of a higher fatty acid on its surface, which comprises a step of forming an aqueous emulsion of the higher fatty acid by adding an alkali to an organic solvent solution or hot molten mass of the higher fatty acid partially saponify the higher fatty acid and dispersing the resulting mixture of the higher fatty acid and its saponification product in water, a step of coating the surface of dibenzylidene sorbitol powder with the higher fatty acid by adding the dibenzylidene sorbitol to the resulting emulsion, and a step of separating the solid from the mixture, drying the solid and recovering the dried product. The transparency and rigidity of a polyolefin resin is improved by addition of aforesaid dibenzylidene sorbitol composition.
Inventors
- 👤 Hiroshi Uchiyama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:39
CPC Classifications
C; C08; C08K; C08K9/00; C08K9/04
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
76 words
A composition consisting essentially of 95 to 50 parts by weight of solid powdery dibenzylidene sorbitol and 5 to 50 parts by weight of at least one higher fatty acid of the formula CH 3 (CH 2 ) n COOH in which n is an integer of from 14 to 20, the total weight of said two components being 100 parts by weight, the surface of the dibenzylidene sorbitol being coated with the higher fatty acid.
Claim 2
Dependent Claim
76 words
A composition consisting essentially of 95 to 50 parts by weight of solid powdery dibenzylidene sorbitol and 5 to 50 parts by weight of at least one higher fatty acid of the formula CH 3 (CH 2 ) n COOH in which n is an integer of from 14 to 20, the total weight of said two components being 100 parts by weight, the surface of the dibenzylidene sorbitol being coated with the higher fatty acid.
Claim 3
Dependent Claim
18 words
The composition of claim 1 wherein the higher fatty acid is behenic acid, stearic acid or palmitic acid.
Claim 4
Dependent Claim
21 words
The composition of claim 1 wherein the maximum particle size distribution of the dibenzylidene sorbitol powder is 100 to 200 mesh.
Claim 5
Dependent Claim
177 words
A process for producing dibenzylidene sorbitol powder having a coating of a higher fatty acid on its surface, which comprises: a step of forming an aqueous emulsion of at least one higher fatty acid of the formula CH 3 (CH 2 ) n COOH, in which n is an integer of from 14 to 20, by adding an alkali or an organic amine to an organic solvent solution or hot molten mass of the higher fatty acid to partially saponify the higher fatty acid, and dispersing the resulting mixture of the higher fatty acid and its saponification product in water, a step of coating the surface of 95 to 50 parts by weight of dibenzylidene sorbitol powder with 5 to 50 parts by weight of the higher fatty acid by adding the dibenzylidene sorbitol powder to the resulting aqueous emulsion, the total weight of the dibenzylidene sorbitol powder and the higher fatty acid being 100 parts by weight, and a step of separating the resultant solid from the mixture, drying the solid and recovering the dried product.
Claim 6
Dependent Claim
177 words
A process for producing dibenzylidene sorbitol powder having a coating of a higher fatty acid on its surface, which comprises: a step of forming an aqueous emulsion of at least one higher fatty acid of the formula CH 3 (CH 2 ) n COOH, in which n is an integer of from 14 to 20, by adding an alkali or an organic amine to an organic solvent solution or hot molten mass of the higher fatty acid to partially saponify the higher fatty acid, and dispersing the resulting mixture of the higher fatty acid and its saponification product in water, a step of coating the surface of 95 to 50 parts by weight of dibenzylidene sorbitol powder with 5 to 50 parts by weight of the higher fatty acid by adding the dibenzylidene sorbitol powder to the resulting aqueous emulsion, the total weight of the dibenzylidene sorbitol powder and the higher fatty acid being 100 parts by weight, and a step of separating the resultant solid from the mixture, drying the solid and recovering the dried product.
Claim 7
Dependent Claim
24 words
The process of claim 4 wherein the concentration of the higher fatty acid in the organic solvent solution is 5 to 50% by weight.
Claim 8
Dependent Claim
33 words
The process of claim 4 wherein the alkali or organic amine is used in an amount of 5 to 15 parts by weight per 100 parts by weight of the higher fatty acid.
Claim 9
Dependent Claim
101 words
An additive for improving the transparency of a polyolefin resin, said additive comprising (A) a dibenzylidene sorbitol composition consisting essentially of 95 to 50 parts by weight of solid powdery dibenzylidene sorbitol and 5 to 50 parts by weight of at least one higher fatty acid of the formula CH 3 (CH 2 ) n COOH in which n is an integer of from 14 to 20, the total weight of said two components being 100 parts by weight, the surface of the dibenzylidene sorbitol being coated with the higher fatty acid, and (B) a conventional additive for a polyolefin resin.
Claim 10
Dependent Claim
101 words
An additive for improving the transparency of a polyolefin resin, said additive comprising (A) a dibenzylidene sorbitol composition consisting essentially of 95 to 50 parts by weight of solid powdery dibenzylidene sorbitol and 5 to 50 parts by weight of at least one higher fatty acid of the formula CH 3 (CH 2 ) n COOH in which n is an integer of from 14 to 20, the total weight of said two components being 100 parts by weight, the surface of the dibenzylidene sorbitol being coated with the higher fatty acid, and (B) a conventional additive for a polyolefin resin.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-06-13 | 1986-12-13 | 1987-06-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-06-13 | 1990-12-13 | 1991-06-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-06-13 | 1994-12-13 | 1995-06-14 | $7700.00 | Window Closed / Lapsed |