Abstract A composition is disclosed for use in forming ceramic articles having improved color, density, bonding strength and mechanical strength. Ceramic particles are slurried with a composition that tends to minimize inclusion of bubbles of gas, e.g., air, and also minimize interstitial voids between the ceramic particles. In a preferred mode, the ceramic particles are slurred with an aqueous solution of sodium hydroxide having, for example, a sodium hydroxide concentration, by weight, in the order of about 0.02% to about 0.03%. The aqueous solution of the sodium hydroxide is added to a powered ceramic until a workable past or slurry is obtained. Articles are formed using the paste or slurry or the paste or slurry is built-up on a support and the ceramic is then fired to fuse the particles.
A ceramic composition consisting essentially of a particulate dental porcelain precursor and an amount of a transient binder sufficient for providing a paste for building up a green porcelain precursor layer on a dental appliance to be jacketed with dental porcelain said transient binder consisting essentially of an aqueous solution of about 0.02% to about 0.03% by weight of sodium hydroxide.
Claim 2
Dependent Claim
61 words
A ceramic composition consisting essentially of a particulate dental porcelain precursor and an amount of a transient binder sufficient for providing a paste for building up a green porcelain precursor layer on a dental appliance to be jacketed with dental porcelain said transient binder consisting essentially of an aqueous solution of about 0.02% to about 0.03% by weight of sodium hydroxide.
Claim 3
Dependent Claim
91 words
In the method of making fired dental porcelain articles comprising the steps of preparing an aqueous suspension of a particulate dental porcelain precursor, forming the suspension, and firing the formed suspension to fuse the precursor to form a dental porcelain article the improvement comprising said aqueous suspension being prepared by forming a paste of said particulate dental porcelain precursor and an aqueous solution of about 0.02% to about 0.03% by weight of sodium hydroxide wherein upon firing a dental porcelain article of improved density, color hue and minimized shrinkage is produced.
Claim 4
Dependent Claim
91 words
In the method of making fired dental porcelain articles comprising the steps of preparing an aqueous suspension of a particulate dental porcelain precursor, forming the suspension, and firing the formed suspension to fuse the precursor to form a dental porcelain article the improvement comprising said aqueous suspension being prepared by forming a paste of said particulate dental porcelain precursor and an aqueous solution of about 0.02% to about 0.03% by weight of sodium hydroxide wherein upon firing a dental porcelain article of improved density, color hue and minimized shrinkage is produced.