Flame-retarded thermoplastic polyester compositions having improved arc resistance and process for preparing same
Assignee: General Electric Co
•
Filing: 1977-12-30
•
Granted: 1983-05-31
•
Expires: 1997-12-30
Abstract
Abstract Flame-retarded, reinforced and unreinforced thermoplastic compositions having improved arc resistance are provided comprising a high molecular weight linear polyester, such as poly(1,4-butylene terephthalate) and the like, a flame-retarding amount of a flame-retardant, such as an aromatic polycarbonate and a particulate material selected from the group consisting of finely divided mica and finely divided clay. A process for improving the arc resistance of reinforced or unreinforced flame retardant polyester compositions is also provided, the process comprising admixing finely divided mica or finely divided surface treated clay with a high molecular weight linear polyester and a flame-retardant.
Inventors
- 👤 Stuart C. Cohen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 12:50
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/34; C08K3/18; C08K3/20; C08K3/22; C08K3/40; C08K9/00; C08K9/04; C08K9/06; C08L; C08L67/00; C08L67/02; C08L69/00
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
53 words
A process for improving the electrical arc resistance of a thermoplastic composition, said process comprising admixing a particulate material selected from the group consisting of mica and surface treated clay with a high molecular weight linear polyester resin and a flame-retarding amount of a flame-retardant, thereby increasing the arc resistance of the composition.
Claim 2
Dependent Claim
53 words
A process for improving the electrical arc resistance of a thermoplastic composition, said process comprising admixing a particulate material selected from the group consisting of mica and surface treated clay with a high molecular weight linear polyester resin and a flame-retarding amount of a flame-retardant, thereby increasing the arc resistance of the composition.
Claim 3
Dependent Claim
17 words
A process as defined in claim 1 wherein a polycarbonate resin is also admixed in the composition.
Claim 4
Dependent Claim
13 words
A process as defined in claim 1 wherein the particulate material is mica.
Claim 5
Dependent Claim
15 words
A process as defined in claim 1 wherein the particulate material is surface treated clay.
Claim 6
Dependent Claim
30 words
A process as defined in claim 1 wherein the particulate material is employed in an amount of from about 5 to about 50 percent by weight of the total composition.
Claim 7
Dependent Claim
39 words
A process as defined in claim 1 wherein the said polyester has an intrinsic viscosity of at least about 0.4 deciliters per gram when measured in a solution in a 60:40 mixture of phenol and trichloroethane at 30° C.
Claim 8
Dependent Claim
102 words
A process as defined in claim 1 wherein said flame-retardant is selected from the group consisting of an aromatic carbonate homopolymer having repeating units of the formula: ##STR6## wherein R 1 and R 2 are hydrogen, lower alkyl or phenyl, X 1 and X 2 are bromo or chloro or mixtures thereof and m and r are from 1 to 4, an aromatic (copoly-) carbonate in which from 25 to 75 wt. percent of the repeating units comprise chloro or bromo-substituted dihydric phenol units and the remainder of the repeating units comprise dihydric phenol, glycol or dicarboxylic acid units, and mixtures thereof.
Claim 9
Dependent Claim
84 words
A process as defined in claim 2 wherein said polycarbonate consists essentially of recurring units of the formula: ##STR7## wherein each --R-- is selected from the group consisting of phenylene, halo-substituted phenylene and alkyl substituted phenylene, and X and Y are each selected from the group consisting of hydrogen, hydrocarbon radicals free from alipathic unsaturation and of radicals which, together and with the adjoining ##STR8## atom, form a cycloalkane radical, the total number of carbon atoms in X and Y being up to 12.
Claim 10
Dependent Claim
25 words
A process as defined in claim 1 wherein said flame-retardant is an aromatic (copoly-) carbonate of a 50:50 mole ratio of bisphenol and tetrabromobisphenol A.
Claim 11
Dependent Claim
13 words
A process as defined in claim 1 wherein said polyester is poly(1,4-butylene terephthalate).
Claim 12
Dependent Claim
15 words
A process as defined in claim 8 wherein said polycarbonate has the repeating units ##STR9##
Claim 13
Dependent Claim
19 words
A process as defined in claim 11 wherein the polycarbonate resin consists of from 20 to 400 repeating units.
Claim 14
Dependent Claim
14 words
A process as defined in claim 11 wherein said reinforcing agent is glass fibers.
References Cited (Backward Citations)
US3290165A
Cited
US3855277A
Cited
US3953394A
Cited
US3953394B1
Cited
US3824209A
Cited
US4064098A
Cited
US4122061A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-05-30 | 1986-11-29 | 1987-05-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-05-30 | 1990-11-29 | 1991-05-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-05-30 | 1994-11-29 | 1995-05-31 | $7700.00 | Window Closed / Lapsed |