Papermaking
Assignee: Nouryon Pulp and Performance Chemicals LLC
•
Filing: 1981-02-26
•
Granted: 1983-05-31
•
Expires: 2001-02-26
Abstract
Abstract A papermaking process in which an aqueous papermaking stock containing a cellulosic pulp is formed and dried. The stock includes a binder comprising colloidal silicic acid, and cationic starch which is added to the stock before the sheet is formed. The manner of addition involves first adding and intermixing in the stock a portion of the colloidal silicic acid and then the cationic starch and, after an agglomerate has formed, adding and intermixing the remainder of the colloidal silicic acid prior to the formation of the sheet. The method results in improved sheet properties and improved retention of filler and fines on the wire.
Inventors
- 👤 Per J. Svending
- 👤 Per G. Batelson
- 👤 Hans E. Johansson
- 👤 Hans M. Larsson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 04:52
CPC Classifications
D; D21; D21H; D21H17/00; D21H17/63; D21H17/67; D21H17/68; D21F; D21F1/00; D21F1/66; D21F1/82; D21H17/20; D21H17/21; D21H17/24; D21H17/28; D21H17/29; D21H21/00; D21H21/50; D21H21/52; D21H23/00; D21H23/76; D21H23/765
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
152 words
In a papermaking process in which an aqueous papermaking stock containing a cellulosic pulp is formed into a sheet and dried, said sheet comprising over 50% cellulosic fiber, the stock including a binder comprising colloidal silicic acid having an average particle size of less than 20 nm, and cationic starch having a degree of substitution of between 0.01 and 0.05, the weight ratio of cationic starch to SiO 2 being between 1:1 and 25:1, the weight of solids in the binder being between 0.1-15% by weight of said pulp the improvement which comprises intermixing in the stock first a portion of the colloidal silicic acid and then the cationic starch and after an agglomerate has formed, adding and intermixing the remainder of the colloidal silicic acid in the stock prior to the formation of the sheet, said first portion of colloidal silicic acid comprising 20-90% of the total colloidal silicic acid added.
Claim 2
Dependent Claim
152 words
In a papermaking process in which an aqueous papermaking stock containing a cellulosic pulp is formed into a sheet and dried, said sheet comprising over 50% cellulosic fiber, the stock including a binder comprising colloidal silicic acid having an average particle size of less than 20 nm, and cationic starch having a degree of substitution of between 0.01 and 0.05, the weight ratio of cationic starch to SiO 2 being between 1:1 and 25:1, the weight of solids in the binder being between 0.1-15% by weight of said pulp the improvement which comprises intermixing in the stock first a portion of the colloidal silicic acid and then the cationic starch and after an agglomerate has formed, adding and intermixing the remainder of the colloidal silicic acid in the stock prior to the formation of the sheet, said first portion of colloidal silicic acid comprising 20-90% of the total colloidal silicic acid added.
Claim 3
Dependent Claim
164 words
In a papermaking process in which an aqueous papermaking stock containing a cellulosic pulp is formed into a sheet and dried, said sheet comprising over 50% cellulosic fiber, the stock including a binder comprising a colloidal silicic acid sol having silica particles having a surface area of from about 50 to 1000 m 2 /g and cationic starch having a degree of substitution of between 0.02 and 0.04, the weight ratio of cationic starch to SiO 2 being between 1.5:1 and 10:1, the weight of solids in the binder being between about 0.1-15% of the weight of the pulp, the improvement which comprises intermixing in the stock first a portion of the colloidal silicic acid and then the cationic starch and, after an agglomerate has formed, adding and intermixing the remainder of the colloidal silicic acid in the stock prior to the formation of the sheet said first portion of colloidal silicic acid sol comprising 20-90% of the total colloidal silicic acid sol added.
Claim 4
Dependent Claim
164 words
In a papermaking process in which an aqueous papermaking stock containing a cellulosic pulp is formed into a sheet and dried, said sheet comprising over 50% cellulosic fiber, the stock including a binder comprising a colloidal silicic acid sol having silica particles having a surface area of from about 50 to 1000 m 2 /g and cationic starch having a degree of substitution of between 0.02 and 0.04, the weight ratio of cationic starch to SiO 2 being between 1.5:1 and 10:1, the weight of solids in the binder being between about 0.1-15% of the weight of the pulp, the improvement which comprises intermixing in the stock first a portion of the colloidal silicic acid and then the cationic starch and, after an agglomerate has formed, adding and intermixing the remainder of the colloidal silicic acid in the stock prior to the formation of the sheet said first portion of colloidal silicic acid sol comprising 20-90% of the total colloidal silicic acid sol added.
Claim 5
Dependent Claim
164 words
In a papermaking process in which an aqueous papermaking stock containing a cellulosic pulp is formed into a sheet and dried, said sheet comprising over 50% cellulosic fiber, the stock including a binder comprising a colloidal silicic acid sol having silica particles having a surface area of from about 300 to 700 m 2 /g and cationic starch having a degree of substitution of between 0.02 and 0.04, the weight ratio of cationic starch to SiO 2 being between 1.5:1 and 10:1, the weight of solids in the binder being between about 1.0-15% of the weight of the pulp, the improvement which comprises intermixing in the stock first a portion of the colloidal silicic acid and then the cationic starch and, after an agglomerate has formed, adding and intermixing the remainder of the colloidal silicic acid in the stock prior to the formation of the sheet said first portion of colloidal silicic acid sol comprising 20-90% of the total colloidal silicic acid sol added.
Claim 6
Dependent Claim
164 words
In a papermaking process in which an aqueous papermaking stock containing a cellulosic pulp is formed into a sheet and dried, said sheet comprising over 50% cellulosic fiber, the stock including a binder comprising a colloidal silicic acid sol having silica particles having a surface area of from about 300 to 700 m 2 /g and cationic starch having a degree of substitution of between 0.02 and 0.04, the weight ratio of cationic starch to SiO 2 being between 1.5:1 and 10:1, the weight of solids in the binder being between about 1.0-15% of the weight of the pulp, the improvement which comprises intermixing in the stock first a portion of the colloidal silicic acid and then the cationic starch and, after an agglomerate has formed, adding and intermixing the remainder of the colloidal silicic acid in the stock prior to the formation of the sheet said first portion of colloidal silicic acid sol comprising 20-90% of the total colloidal silicic acid sol added.
Claim 7
Dependent Claim
164 words
In a papermaking process in which an aqueous papermaking stock containing a cellulosic pulp is formed into a sheet and dried, said sheet comprising over 50% cellulosic fiber, the stock including a binder comprising a colloidal silicic acid sol having silica particles having a surface area of from about 300 to 700 m 2 /g and cationic starch having a degree of substitution of between 0.02 and 0.04, the weight ratio of cationic starch to SiO 2 being between 1.5:1 and 4.5:1, the weight of solids in the binder being between about 1.0-15% of the weight of the pulp, the improvement which comprises intermixing in the stock first a portion of the colloidal silicic acid and then the cationic starch and, after an agglomerate has formed, adding and intermixing the remainder of the colloidal silicic acid in the stock prior to the formation of the sheet said first portion of colloidal silicic acid sol comprising 20-90% of the total colloidal silicic acid sol added.
Claim 8
Dependent Claim
164 words
In a papermaking process in which an aqueous papermaking stock containing a cellulosic pulp is formed into a sheet and dried, said sheet comprising over 50% cellulosic fiber, the stock including a binder comprising a colloidal silicic acid sol having silica particles having a surface area of from about 300 to 700 m 2 /g and cationic starch having a degree of substitution of between 0.02 and 0.04, the weight ratio of cationic starch to SiO 2 being between 1.5:1 and 4.5:1, the weight of solids in the binder being between about 1.0-15% of the weight of the pulp, the improvement which comprises intermixing in the stock first a portion of the colloidal silicic acid and then the cationic starch and, after an agglomerate has formed, adding and intermixing the remainder of the colloidal silicic acid in the stock prior to the formation of the sheet said first portion of colloidal silicic acid sol comprising 20-90% of the total colloidal silicic acid sol added.
Claim 9
Dependent Claim
51 words
The process of any one of claims 1, 2, 3, and 4 wherein between about 30 and about 80 percent of the colloidal silic acid is added to the stock to form an agglomerate and the remaining portion of the colloidal silicic acid is added after the formation of the agglomerate.
References Cited (Backward Citations)
US2647158A
Cited
US2865743A
Cited
US3224927A
Cited
US3227607A
Cited
US3737370A
Cited
US3721575A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-05-30 | 1986-11-29 | 1987-05-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-05-30 | 1990-11-29 | 1991-05-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-05-30 | 1994-11-29 | 1995-05-31 | $7700.00 | Window Closed / Lapsed |