Method for applying binding agents to fibrous webs
Assignee: Rexam Beverage Can Co
•
Filing: 1982-07-21
•
Granted: 1983-05-31
•
Expires: 2002-07-21
Abstract
Abstract A method and system for applying a foamed binding agent to a fibrous web is disclosed. The invention is characterized by the use of an extruder having an upper lip extending 1/16 to 1/4 inch beyond the lower lip, and by the drawing of a vacuum beneath the applied foam, said characteristics being critical to the formation of a uniform foam layer atop the web. A second, more substantial vacuum is then applied beneath the web to essentially completely draw the binding agent into the web thereby providing substantial inter-fiber bonding.
Inventors
- 👤 Walter L. Pauls
- 👤 Raymond A. Dunleavy, III
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 20:03
CPC Classifications
B; B05; B05D; B05D1/00; B05D1/26; B29; B29C; B29C44/00; B29C44/20; B29C44/32; B29C44/321; B29C44/34; B29C44/36; B29C44/46; B29C44/461; B29C44/50; B29C44/505; B29C48/00; B29C48/03; B29C48/07; B29C48/08; B29C48/25; B29C48/255; B29C48/2556; B29C48/30; B29C48/305; B29C48/31; B29C48/313; D; D04; D04H; D04H1/00; D04H1/40; D04H1/58; D04H1/64; D04H1/68; D21; D21H; D21H21/00; D21H21/50; D21H21/56; D21H25/00; D21H25/02; D21H5/00; D21H5/26; D21H5/265; D21H5/2657; D21H5/2664; B29L; B29L2007/00
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
168 words
A method of applying binding agent onto a second side of a fibrous web whose first side had been bonded previously, the method comprising the steps of: (a) providing said once bonded fibrous web on a moving foraminous carrier, second side facing up, (b) applying to said second side a foamed dispersion of a binding agent by extruder means, the extruder being characterized by an orifice outlet whose upper lip extends beyond its lower lip by between 1/16 and 1/4 inch, said foamed dispersion being applied at an exit velocity approximately equal to the carrier velocity, (c) drawing beneath said foraminous carrier a first vacuum just downstream of the extruder outlet orifice, said vacuum being between about 0.10 to 1.0 inch of water, whereby the foamed dispersion remains uniformly atop the web, the (d) drawing beneath the carrier a second vacuum further downstream of the extruder means, said vacuum being about between 2 and 15 inches of mercury, whereby the foamed dispersion is caused to penetrate said web.
Claim 2
Independent Claim
168 words
A method of applying binding agent onto a second side of a fibrous web whose first side had been bonded previously, the method comprising the steps of: (a) providing said once bonded fibrous web on a moving foraminous carrier, second side facing up, (b) applying to said second side a foamed dispersion of a binding agent by extruder means, the extruder being characterized by an orifice outlet whose upper lip extends beyond its lower lip by between 1/16 and 1/4 inch, said foamed dispersion being applied at an exit velocity approximately equal to the carrier velocity, (c) drawing beneath said foraminous carrier a first vacuum just downstream of the extruder outlet orifice, said vacuum being between about 0.10 to 1.0 inch of water, whereby the foamed dispersion remains uniformly atop the web, the (d) drawing beneath the carrier a second vacuum further downstream of the extruder means, said vacuum being about between 2 and 15 inches of mercury, whereby the foamed dispersion is caused to penetrate said web.
Claim 3
Dependent Claim
23 words
The method of claim 1 wherein the concentration of binding agent solids in the unfoamed emulsion is between 10 and 30% by weight.
Claim 4
Dependent Claim
35 words
The method of claim 2 wherein the amount of binding agent solids applied to the second side of the web is between 50 and 80% of the total binding agent solids applied to the web.
Claim 5
Dependent Claim
35 words
The method of claim 3 wherein the foamed dispersion has a blow ratio of between 10 and 25, blow ratio being defined as the density of the unfoamed binding agent emulsion to the foamed emulsion.
Claim 6
Dependent Claim
69 words
The method of claim 1 wherein the concentration of solids in the unfoamed emulsion is between 15 and 25% by weight, the amount of binding agent solids applied to the second side of the web is between 60 to 70% of the total solids applied to the web, the blow ratio is between 15 and 20, and the second vacuum is preferably between 5 and 10 inches of mercury.
Claim 7
Dependent Claim
49 words
The methods of claim 4 or 5 wherein the preferred upper lip member extension is 3/32 inch, the distance between the extruder outlet orifice and the web is between about 1/4 and three inches, and the angle between the orifice and the web is about 2 to about 25°.
Claim 8
Dependent Claim
16 words
The method of claim 5 wherein the binding agent is a foamed water based latex emulsion.
Claim 9
Independent Claim
193 words
A method of applying binding agent to each side of a loose fibrous web, the method comprising the steps of: (a) providing said fibrous web on a first moving foraminous carrier, first side facing up, (b) applying to said first side a binding agent emulsion, (c) at least partially drying said once bonded web, (d) transferring said web to a second moving foraminous carrier, the web being inverted thereby, (e) applying to said second side a foamed dispersion of a binding agent by extruder means, the extruder characterized by an orifice outlet whose upper lip extends beyond its lower lip by between 1/16 and 1/4 inch, said foamed dispersion being applied at an exit velocity approximately equal to the carrier velocity, (f) drawing beneath said foraminous carrier a first vacuum just downstream of the extruder outlet orifice, said vacuum being between about 0.10 to 1.0 inch of water, whereby the foamed dispersion remains uniformly atop the web, and (g) drawing beneath the carrier a second vacuum further downstream of the extruder means, said vacuum being about between 2 and 15 inches of mercury, whereby the foamed dispersion is caused to penetrate said web.
Claim 10
Independent Claim
193 words
A method of applying binding agent to each side of a loose fibrous web, the method comprising the steps of: (a) providing said fibrous web on a first moving foraminous carrier, first side facing up, (b) applying to said first side a binding agent emulsion, (c) at least partially drying said once bonded web, (d) transferring said web to a second moving foraminous carrier, the web being inverted thereby, (e) applying to said second side a foamed dispersion of a binding agent by extruder means, the extruder characterized by an orifice outlet whose upper lip extends beyond its lower lip by between 1/16 and 1/4 inch, said foamed dispersion being applied at an exit velocity approximately equal to the carrier velocity, (f) drawing beneath said foraminous carrier a first vacuum just downstream of the extruder outlet orifice, said vacuum being between about 0.10 to 1.0 inch of water, whereby the foamed dispersion remains uniformly atop the web, and (g) drawing beneath the carrier a second vacuum further downstream of the extruder means, said vacuum being about between 2 and 15 inches of mercury, whereby the foamed dispersion is caused to penetrate said web.
Claim 11
Dependent Claim
20 words
The method of claim 8 wherein binding agent is applied to the first side of the web by spray means.
Claim 12
Dependent Claim
29 words
The method of claim 9 wherein a vacuum is drawn below the first carrier essentially beneath the spray means, said vacuum being about 0.1 to 1.0 inch of water.
Claim 13
Dependent Claim
27 words
The method of claim 10 wherein the concentration of the binding agent solids in the emulsion applied by spray means is between 15 to 20% by weight.
Claim 14
Dependent Claim
105 words
The method of claim 8 wherein the binding agent emulsion applied to the first side is a foamed dispersion, said foam being applied thereto by extruder means, the extruder characterized by an orifice outlet whose upper lip extends beyond its lower lip by between 1/16 and 1/4 inch, said foamed dispersion being applied at an exit velocity approximately equal to the first carrier velocity, and further comprising the step of drawing beneath said foraminous carrier a first vacuum just downstream of the extruder outlet orifice, said vacuum being between about 0.10 to 1.0 inch of water, whereby the foamed dispersion remains uniformly atop the web.
Claim 15
Dependent Claim
23 words
The methods of claim 10 or 12 wherein said vacuum drawn beneath the first carrier is preferably less than 0.5 inches of water.
Claim 16
Dependent Claim
29 words
The methods of claim 13 wherein the vacuum drawn through the second carrier and just downstream of the extruder outlet orifice is preferably less than 0.5 inches of water.
Claim 17
Dependent Claim
29 words
The method of claim 12 wherein the concentration of the binding agent solids on an unfoamed basis applied to the first side is about 15 to 20% by weight.
Claim 18
Dependent Claim
30 words
The methods of claim 11 or 15, wherein the concentration of binding agent solids on an unfoamed basis applied to the second side is about 10 to 30% by weight.
Claim 19
Dependent Claim
31 words
The methods of claim 16 wherein the amount of binding agent solids applied to the second side is about 50 to 80% of all binding agent solids contained in the web.
Claim 20
Dependent Claim
28 words
The method of claim 17 wherein the concentration of binding agent solids on an unfoamed basis applied to the second side is about 15 to 25% by weight.
Claim 21
Dependent Claim
19 words
The methods of claim 18 wherein the blow ratio of foamed binding agent dispersion is between 10 and 25.
Claim 22
Dependent Claim
18 words
The methods of claim 19 wherein the binding agent is a water based latex emulsion, foamed where applicable.
Claim 23
Dependent Claim
49 words
The methods of claim 8 or 12 wherein the preferred upper lip member extension is 3/32 inch, the distance between the extruder outlet orifice and the web is between about 1/4 to three inches, and the angle between the orifice and the web is about 2° to about 25°.
References Cited (Backward Citations)
US3043738A
Cited
US3042573A
Cited
US3348989A
Cited
US3331728A
Cited
US3600750A
Cited
US3609810A
Cited
US4159355A
Cited
US4332756A
Cited
US4292271A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-05-30 | 1986-11-29 | 1987-05-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-05-30 | 1990-11-29 | 1991-05-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-05-30 | 1994-11-29 | 1995-05-31 | $7700.00 | Window Closed / Lapsed |