US4384083A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Thermoplastic adhesive
Assignee: MCCABE ENTERPRISES Inc A CORP OF FL
•
Filing: 1981-07-22
•
Granted: 1983-05-17
•
Expires: 2001-07-22
Abstract
Abstract A thermoplastic adhesive composition that is particularly suitable for use as a hot melt adhesive is disclosed that comprises at least about 10% by weight of a polyether-based thermoplastic polyurethane and another component selected from the group consisting of: (A) a polyamide formed by the condensation of a compound of the formula YN<Z>NH where Z is selected from the group consisting of ##STR1## where R is selected from the group consisting of hydrogen and alkyl groups having from 1 to 6 carbon atoms and R 1 is a divalent aliphatic hydrocarbon group having at least 1 carbon atom, Y is selected from the group consisting of hydrogen, R'NH 2 and R'OH where R' is a divalent alkylene radical having from 1 to 6 carbon atoms, with an amide forming derivative of a polymeric fat acid; (b) a thermoplastic copolyester made from the polyesterification reaction between terephthalic acid, cyclohexanedimethanol, a diol in addition to cyclohexanedimethanol and a dibasic acid in addition to terephthalic acid; or (C) a polyester-polyamide formed by heating a mixture of about 50 to about 99% by weight of component (A) with about 1 to about 50% by weight of component (B) at a temperature above the melting point of components (A) and (B) for a sufficient period to effect ester interchange.
Inventors
- 👤 Richard L. Baker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 22:17
CPC Classifications
C; C09; C09J; C09J177/00; C09J177/06; C09J177/08; C08; C08L; C08L77/00; C09J175/00; C09J175/04; C09J175/08; C09J177/12; C08L2666/00; C08L2666/02; C08L2666/14; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31551; Y10T428/31562; Y10T428/31565; Y10T428/31573; Y10T428/3158; Y10T428/31587
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
197 words
An adhesive comprising at least about 10% by weight of a polyether-based thermoplastic polyurethane and another component selected from the group consisting of: (A) a polyamide formed by the condensation of a compound of the formula YN<Z>NH where Z is selected from the group consisting of ##STR4## where R is selected from the group consisting of hydrogen and alkyl groups having from 1 to 6 carbon atoms and R 1 is a divalent aliphatic hydrocarbon group having at least one carbon atom, Y is selected from the group consisting of hydrogen, R'NH 2 and R'OH where R' is a divalent alkylene radical having from 1 to 6 carbon atoms, with an amide forming derivative of a polymeric fat acid; (B) a thermoplastic copolyester made from the polyesterification reaction between terephthalic acid, cyclohexanedimethanol, a diol in addition to cyclohexanedimethanol and a dibasic acid in addition to terephthalic acid; or (C) a polyester-polyamide formed by heating a mixture of about 50 to about 99% by weight of component (A) with about 1 to about 50% by weight of component (B) at a temperature above the melting points of components (A) and (B) for a sufficient period to effect ester-interchange.
Claim 2
Dependent Claim
197 words
An adhesive comprising at least about 10% by weight of a polyether-based thermoplastic polyurethane and another component selected from the group consisting of: (A) a polyamide formed by the condensation of a compound of the formula YN<Z>NH where Z is selected from the group consisting of ##STR4## where R is selected from the group consisting of hydrogen and alkyl groups having from 1 to 6 carbon atoms and R 1 is a divalent aliphatic hydrocarbon group having at least one carbon atom, Y is selected from the group consisting of hydrogen, R'NH 2 and R'OH where R' is a divalent alkylene radical having from 1 to 6 carbon atoms, with an amide forming derivative of a polymeric fat acid; (B) a thermoplastic copolyester made from the polyesterification reaction between terephthalic acid, cyclohexanedimethanol, a diol in addition to cyclohexanedimethanol and a dibasic acid in addition to terephthalic acid; or (C) a polyester-polyamide formed by heating a mixture of about 50 to about 99% by weight of component (A) with about 1 to about 50% by weight of component (B) at a temperature above the melting points of components (A) and (B) for a sufficient period to effect ester-interchange.
Claim 3
Dependent Claim
54 words
The composition of claim 1 wherein said another component is component (A), said polyurethane being present in said composition in the range of about 10 to about 60% by weight of said composition, component (A) being present in said composition in the range of about 40 to about 90% by weight of said composition.
Claim 4
Dependent Claim
80 words
The composition of claim 1 wherein said another component is component (A), said component (A) being formed by the reaction of from about 30 to about 70% by mole of a polymeric fat acid having a dimeric fat acid content of at least about 65% by weight, from about 20 to about 40% by mole of azelaic acid, from about 20 to about 40% by mole of ethylene diamine and from about 20 to about 80% by mole of piperazine.
Claim 5
Dependent Claim
54 words
The composition of claim 1 wherein said another component is component (B), said polyurethane being present in said composition in the range of about 10 to about 25% by weight of said composition, component (B) being present in said composition in the range of about 25 to about 90% by weight of said composition.
Claim 6
Dependent Claim
24 words
The composition of claim 4 including component (A) which is present at a level of up to about 50% by weight of said composition.
Claim 7
Dependent Claim
72 words
The composition of claim 1 with about 10 to about 25% by weight of said polyurethane, and said another component consists of a mixture of components (A) and (B), component (A) being present in said composition at a level of up to about 50% by weight of said composition and component (B) being present in said composition at a level of from about 25% to about 90% by weight of said composition.
Claim 8
Dependent Claim
33 words
The composition of claim 1 wherein said another component is component (C), said component (C) being present in said composition at a level of up to about 75% by weight of said composition.
Claim 9
Dependent Claim
21 words
The composition of claim 2 with about 13% by weight of said polyurethane and about 87% by weight of component (A).
Claim 10
Dependent Claim
28 words
The composition of claim 1 with about 25% by weight of said polyurethane, about 25% by weight of component (A) and about 50% by weight of component (B).
Claim 11
Dependent Claim
76 words
The composition of claim 1 wherein said another component consists of a mixture of components (A) and (C), said polyurethane being present in said composition at a level of about 10 to about 60% by weight of said composition, component (A) being present at a level of up to about 90% by weight of said composition, component (C) being present in said composition at a level of up to about 75% by weight of said composition.
Claim 12
Dependent Claim
21 words
The composition of claim 1 wherein said polyurethane is the reaction product of polytetraethylene ether glycol and methylene di-para phenylene isocyanate.
Claim 13
Dependent Claim
183 words
The composition of claim 1 wherein said component (A) is formed by the amidification at a temperature in the range of about 200° F. to about 575° F. of (i) about 30% to about 70% by mole of a polymeric fat acid having a dimeric fat acid content of at least about 65% by weight, (ii) from about 20% to about 80% by mole of said compound of the formula YN<Z>NH, (iii) from about 20% to about 40% by mole of a compound of the formula R 2 OOC--COOR 2 or R 2 OOCR 3 COOR 2 where R 2 is selected from the group consisting of hydrogen, alkyl and aryl groups containing from 1 to 8 carbon atoms and R 3 is a divalent, aliphatic, cycloaliphatic or aromatic hydrocarbon radical having from 1 to 20 carbon atoms, and (iv) from about 20% to about 40% by mole of a diamine of the formula H 2 NR 4 NH 2 where R 4 is selected from the group consisting of aliphatic, cycloaliphatic and aromatic hydrocarbon radicals having from 2 to 20 carbon atoms.
Claim 14
Dependent Claim
32 words
The composition of claim 1 wherein said component (B) is formed from the polyesterification of terephthalic acid, cyclohexanedimethanol, an aliphatic, cycloaliphatic or aromatic diol and an aliphatic, cycloaliphatic or aromatic dicarboxylic acid.
Claim 15
Dependent Claim
32 words
The composition of claim 13 wherein said diol for component (B) is selected from the group consisting of ethylene glycol, 1,6 hexane diol, or a mixture of ethylene glycol and 1,6 hexanediol.
Claim 16
Dependent Claim
15 words
The composition of claim 13 wherein said dicarboxylic acid for component (B) is azelaic acid.
Claim 17
Dependent Claim
39 words
The composition of claim 1 wherein component (C) is formed by heating a mixture of components (A) and (B) at a temperature in the range of from the melting point of components (A) and (B) to about 600° F.
Claim 18
Dependent Claim
19 words
The composition of claim 16 wherein components (A) and (B) are heated at a temperature of about 500° F.
Claim 19
Dependent Claim
26 words
The composition of claim 1 wherein component (C) is formed by heating a mixture of components (A) and (B) in the presence of an ester-interchange catalyst.
Claim 20
Independent Claim
17 words
A method of forming a thermoplastic adhesive comprising extruding the composition of any one of claims 1-18.
Claim 21
Dependent Claim
24 words
The method of claim 19 wherein said composition is extruded at a temperature in the range of about 300° F. to about 425° F.
Claim 22
Dependent Claim
32 words
The method of claim 19 wherein the temperature of said composition is raised to a temperature of over about 300° F. and then said composition is subjected to high shear extrusion conditions.
Claim 23
Independent Claim
21 words
A method of making a composite product comprising extruding the composition of any one of claims 1-18 on to a substrate.
Claim 24
Dependent Claim
13 words
The method of claim 22 wherein said substrate and said composition are co-extruded.
Claim 25
Independent Claim
70 words
A method of making a composite structure comprising extruding the composition of any one of claims 1-18, applying the extruded composition to at least a portion of a first component of said composite structure as said extruded composition is extruded, placing a second component of said composite structure in contact with said extruded composition, and applying pressure to said second component to bond said second component to said first component.
Claim 26
Dependent Claim
42 words
The method of claim 24 with the step of cooling said extruded composition prior to placing said second component in contact with said extruded composition, and then applying heat to said extruded composition to bond said second component to said first component.
Claim 27
Dependent Claim
13 words
A hot melt adhesive comprising the composition of any one of claims 1-18.
Claim 28
Dependent Claim
40 words
The method of claim 24 wherein said first and said second components are made from the same or different materials, the material of each component being selected from the group consisting of polyurethane, polyolefin, polyurethane-polyolefin blend, polyvinylchloride, polyester or nylon.
Claim 29
Dependent Claim
25 words
The method of claim 27 wherein said first component is coextruded with said composition and said second component is a smooth, porous or woven structure.
References Cited (Backward Citations)
US2506486A
Cited
US2744882A
Cited
US2852492A
Cited
US2954364A
Cited
US3372148A
Cited
US3377303A
Cited
US3663513A
Cited
US3887755A
Cited
US4279801A
Cited
US4156064A
Cited
US4135033A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-05-16 | 1986-11-15 | 1987-05-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-05-16 | 1990-11-15 | 1991-05-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-05-16 | 1994-11-15 | 1995-05-17 | $7700.00 | Window Closed / Lapsed |