Assignee: Tokyo Ohka Kogyo Co Ltd
•
Filing: 1981-09-14
•
Granted: 1983-05-17
•
Expires: 2001-09-14
Abstract
Abstract A process for producing novel resinous gravure printing plates comprises coating on a printing substrate such as a cylinder a radiation-curable resin coating composition containing in a specific ratio a soluble polyamide resin and a radiation-polymerizable monomer or the like dissolved in a solvent, curing the coated film by irradiation with actinic rays, and engraving the resulting cured film. As a result, a novel resinous gravure printing plate having excellent engraving property, printing durability, and solvent resistance is produced.
Inventors
- 👤 Toshimi Aoyama
- 👤 Bonpei Kato
- 👤 Hiroyuki Tohda
- 👤 Eiichi Tachibana
- 👤 Shinichi Hikosaka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 06:44
CPC Classifications
B; B41; B41N; B41N1/00; B41N1/12
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
93 words
A process for producing resinous gravure printing plates which comprises coating a printing substrate with a film of a radiation-curable coating composition comprising 100 parts by weight of a soluble polyamide resin, 50 to 100 parts by weight of a radiation-polymerizable monomeric compound, and a solvent in a quantity sufficient to cause the viscosity of the coating composition to be suitable for coating, curing the coated film by irradiation with actinic rays, and engraving the resulting cured coated film, said radiation-polymerizable monomeric compound being a nitrogen-containing compound having at least three ethylenic unsaturations.
Claim 2
Dependent Claim
93 words
A process for producing resinous gravure printing plates which comprises coating a printing substrate with a film of a radiation-curable coating composition comprising 100 parts by weight of a soluble polyamide resin, 50 to 100 parts by weight of a radiation-polymerizable monomeric compound, and a solvent in a quantity sufficient to cause the viscosity of the coating composition to be suitable for coating, curing the coated film by irradiation with actinic rays, and engraving the resulting cured coated film, said radiation-polymerizable monomeric compound being a nitrogen-containing compound having at least three ethylenic unsaturations.
Claim 3
Dependent Claim
52 words
The process according to claim 1, in which: the coating composition further comprises a photopolymerization initiator in a quantity of 0.01 to 10% by weight with respect to the total quantity of the polyamide resin and the radiation-polymerizable monomeric compound; the coating composition is photocurable; and the actinic rays are ultraviolet rays.
Claim 4
Dependent Claim
26 words
The process according to claim 1, in which the coating composition has a viscosity of 10 to 400 cps when it is coated on the substrate.
Claim 5
Dependent Claim
16 words
The process according to claim 1, in which the printing substrate is of a cylindrical shape.
Claim 6
Dependent Claim
30 words
The process according to claim 8, in which the coating composition is spirally applied as successively overlaid layers on the surface of the cylindrical substrate, as the substrate is rotated.
Claim 7
Dependent Claim
71 words
The process according to claim 5, in which the spiral application of the coating composition is carried out by supplying the coating composition into a sump formed between the substrate and a coating composition retainer disposed along and adjacent to the substrate and by causing the coating composition to flow from within the sump onto the surface of the substrate while causing the coating composition retainer to gradually leave the substrate.
Claim 8
Dependent Claim
17 words
The process according to claim 1, in which the coated film is dried prior to the irradiation.
Claim 9
Dependent Claim
17 words
The process according to claim 1, in which the engraving is carried out by an electronic engraver.
Claim 10
Dependent Claim
42 words
The process according to claim 1, in which the coated film is irradiated for a time sufficient to produce a coated cured film having an ultimate tensile elongation of 100% or less and a tensile strength of 100 Kg/cm 2 or more.
References Cited (Backward Citations)
US1182982A
Cited
US3551148A
Cited
US3512971A
Cited
US3764501A
Cited
US3656999A
Cited
US3985953A
Cited
US4007680A
Cited
US4339472A
Cited
US4269930A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-05-16 | 1986-11-15 | 1987-05-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-05-16 | 1990-11-15 | 1991-05-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-05-16 | 1994-11-15 | 1995-05-17 | $7700.00 | Window Closed / Lapsed |