Ultrasonic transducer and process to obtain high acoustic attenuation in the backing
Assignee: General Electric Co
•
Filing: 1981-04-27
•
Granted: 1983-05-03
•
Expires: 2001-04-27
Abstract
Abstract A high frequency ultrasonic transducer is improved by fabricating the tungsten-polyvinyl chloride composite, which backs the elements, in a specific manner. Small particle size tungsten powder and PVC powder are placed into a high pressure die. Standard processing of the powder mixture includes degasing followed by heating and compressing. To maximize the acoustic attenuation, the pressure applied to the mixture is maintained until it has cooled down. The composite is in a state of elastic compression and spontaneously expands when removed from the die, giving rise to the high levels of acoustic attenuation.
Inventors
- 👤 Casmir R. Trzaskos
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 01:42
CPC Classifications
G; G10; G10K; G10K11/00; G10K11/16; G10K11/162; G10K11/165; G10K11/002
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
143 words
A process for enhancing the acoustic attenuation of a tungsten-polyvinyl chloride ultrasonic transducer backing material comprising: placing a mixture of tungsten powder and polyvinyl chloride powder into the chamber of a high pressure die, said tungsten powder having a particle size less than 10 microns and the volume ratio of tungsten to polyvinyl chloride being selected to yield a specific acoustic impedance; evacuating the die chamber to degas said powders; heating said powder mixture for a limited time and applying a pressure that is increased to a high pressure sufficient to compress said powders into a dense, compact composite; continuing to apply said high pressure until said composite cools down to below 50° C. and is in a state of elastic compression; and removing said cooled composite from the die so that said composite spontaneously expands and acquires high levels of acoustic attenuation.
Claim 2
Dependent Claim
143 words
A process for enhancing the acoustic attenuation of a tungsten-polyvinyl chloride ultrasonic transducer backing material comprising: placing a mixture of tungsten powder and polyvinyl chloride powder into the chamber of a high pressure die, said tungsten powder having a particle size less than 10 microns and the volume ratio of tungsten to polyvinyl chloride being selected to yield a specific acoustic impedance; evacuating the die chamber to degas said powders; heating said powder mixture for a limited time and applying a pressure that is increased to a high pressure sufficient to compress said powders into a dense, compact composite; continuing to apply said high pressure until said composite cools down to below 50° C. and is in a state of elastic compression; and removing said cooled composite from the die so that said composite spontaneously expands and acquires high levels of acoustic attenuation.
Claim 3
Dependent Claim
25 words
The process of claim 1 wherein said powder mixture is heated to 100°-120° C. and said high pressure is 40,000 to 48,000 pounds/in 2 .
Claim 4
Dependent Claim
25 words
The process of claim 1 wherein said powder mixture has a volume ratio of about 55 parts 4 micron tungsten to 45 parts polyvinyl chloride.
Claim 5
Dependent Claim
24 words
The process of claim 3 wherein said powder mixture is heated to 115-120° C. and said high pressure is about 45,000 pounds/in 2 .
Claim 6
Dependent Claim
72 words
An improved 4.5 megahertz or higher ultrasonic transducer comprising: at least one piezoelectric transducer element having a front and a back surface and metallic electrodes on both surfaces; a cover layer on the front surface of said element; and a tungsten-polyvinyl chloride composite backing on the back surface of said element which absorbs almost all the acoustic energy emitted from said back surface and is fabricated by the process of claim 1.
References Cited (Backward Citations)
US2881336A
Cited
US3376438A
Cited
US3631271A
Cited
US3794866A
Cited
US4205686A
Cited
US4240003A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-05-02 | 1986-11-01 | 1987-05-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-05-02 | 1990-11-01 | 1991-05-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-05-02 | 1994-11-01 | 1995-05-03 | $7700.00 | Window Closed / Lapsed |