Manufacture of articles by drawing and blow-moulding
Assignee: Rexam AB
•
Filing: 1980-05-30
•
Granted: 1983-04-26
•
Expires: 2000-05-30
Abstract
Abstract A process for the manufacture of articles from a thermoplastic of polyester or polyamide type, preferably of polyethylene terephthalate, the element consisting of an edge part which surrounds a body in an arrangement in which the latter is sunk relative to the edge part. The element is formed from a blank of mainly amorphous material or from a material having a crystallinity of less than 10%. The blank consists, for example, of a flat plate, a blank shell or the like. The body or parts thereof are shaped by stretching the blank until that material flows which is located within the material sections of the blank, which form the edge part in the element, the material stretched up to flowing in the body assuming a crystallinity of between 10% and 25%, while the crystallinity in the material in the edge part and in the unstretched parts retains its original value of less than 10%. At least the body of the element is expanded against warm mould walls until the final shape of the particular article is obtained. Optionally, the expansion is preceded by a number of drawing steps with an axial elongation of the body coupled with a simultaneous reduction in its dimensions at right angles thereto.
Inventors
- 👤 Kjell M. Jakobsen
- 👤 Claes T. Nilsson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 10:53
CPC Classifications
B; B29; B29C; B29C51/00; B29C51/26; B29C51/261; B29C51/262; B29C51/002; B29C51/04; B65; B65D; B65D1/00; B65D1/22; B65D1/26; Y; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1397
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
331 words
A process for the manufacture of an article from polyethylene terephthlate or similar materials comprising providing a substantially flat blank of amorphous, polyethylene terephthlate having a crystallinity of less than 10%, clamping said blank between clamping devices to form at least one inner zone completely surrounded by a closed, band-like, clamped section of material, applying a press element against said inner zone over a region smaller than the total area of said inner zone, whereby a second closed, band-like zone is formed between said clamped band-like section and said inner zone to which the press element is applied, relatively displacing said press element and said clamping devices with the thermoplastic material at a temperature below the glass transition temperature (Tg) while maintaining said press element in contact with said inner zone, the second band-like zone being substantially greater than the thickness of the blank whereby the material in said second band-like zone is freely stretched by drawing in a drawing region between the outer surface of the press element and the inner surface of the clamping devices without contact of the drawn material with the surfaces of the clamping devices, the material in said drawing region forming a transition zone at which flow takes place in the material reducing the original thickness of the blank by a factor of about 3 to effect crystallization thereof and monoaxial orientation whereby a drawn element is formed which comprises an edge part composed of said clamped section and a body which is drawn relative to said edge part and includes material drawn until it flows to form the monoaxially oriented crystallized material, the crystallinity of said material of said body being between 10% and 25%, while the crystallinity of the material in said edge part and in any undrawn part of the body retains its original value of less than 10%, and reshaping said body at a temperature above the glass transition temperature (Tg) by blow-moulding to achieve the shape of the final product.
Claim 2
Dependent Claim
331 words
A process for the manufacture of an article from polyethylene terephthlate or similar materials comprising providing a substantially flat blank of amorphous, polyethylene terephthlate having a crystallinity of less than 10%, clamping said blank between clamping devices to form at least one inner zone completely surrounded by a closed, band-like, clamped section of material, applying a press element against said inner zone over a region smaller than the total area of said inner zone, whereby a second closed, band-like zone is formed between said clamped band-like section and said inner zone to which the press element is applied, relatively displacing said press element and said clamping devices with the thermoplastic material at a temperature below the glass transition temperature (Tg) while maintaining said press element in contact with said inner zone, the second band-like zone being substantially greater than the thickness of the blank whereby the material in said second band-like zone is freely stretched by drawing in a drawing region between the outer surface of the press element and the inner surface of the clamping devices without contact of the drawn material with the surfaces of the clamping devices, the material in said drawing region forming a transition zone at which flow takes place in the material reducing the original thickness of the blank by a factor of about 3 to effect crystallization thereof and monoaxial orientation whereby a drawn element is formed which comprises an edge part composed of said clamped section and a body which is drawn relative to said edge part and includes material drawn until it flows to form the monoaxially oriented crystallized material, the crystallinity of said material of said body being between 10% and 25%, while the crystallinity of the material in said edge part and in any undrawn part of the body retains its original value of less than 10%, and reshaping said body at a temperature above the glass transition temperature (Tg) by blow-moulding to achieve the shape of the final product.
Claim 3
Dependent Claim
17 words
A process as claimed in claim 1, wherein the crystallinity of said blank is less than 5%.
Claim 4
Dependent Claim
19 words
A process as claimed in claim 2, wherein the crystallinity of the drawn material is between 12 and 20%.
Claim 5
Dependent Claim
13 words
A process as claimed in claim 1 comprising heating the body during blow-moulding.
Claim 6
Dependent Claim
41 words
A process as claimed in claim 1 comprising elongating said body in the axial direction before blow-moulding by a number of repeated drawing steps to retain reduced dimensions at right angles thereto, the thickness of the drawn material being substantially unchanged.
Claim 7
Dependent Claim
52 words
A process as claimed in claim 1, wherein the drawing step for causing the material to flow is continued until approximately all of the material in the inner zone has undergone flow, as a result of which approximately all of the material in the body consists of material which has undergone flow.
Claim 8
Dependent Claim
47 words
A process as claimed in claim 1, wherein the contact surface of the press element with said inner zone is such that it is completely surrounded by said closed, band-like, clamped section, in order to cause the flow of the material to start at the press element.
Claim 9
Dependent Claim
36 words
A process as claimed in claim 7, wherein the width of the clamped material is selected so that flow of the material at the end of the drawing step extends to said material and ends thereat.
Claim 10
Dependent Claim
18 words
A process as claimed in claim 8, wherein the temperature of the material before drawing is room temperature.
Claim 11
Dependent Claim
24 words
A process as claimed in claim 8 comprising subjecting the material, at least during the drawing step, to accelerated cooling in the flow region.
Claim 12
Dependent Claim
27 words
A process as claimed in claim 10 comprising cooling the press element such that, on drawing the material, the regions in which the material flows are cooled.
Claim 13
Dependent Claim
23 words
A process as claimed in claim 1 further comprising severing said body from said edge part prior to said reshaping of said body.
References Cited (Backward Citations)
US3184524A
Cited
US3420930A
Cited
US3496143A
Cited
US3757718A
Cited
US3733309A
Cited
US3733309B1
Cited
US3814784A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-04-25 | 1986-10-25 | 1987-04-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-04-25 | 1990-10-25 | 1991-04-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-04-25 | 1994-10-25 | 1995-04-26 | $7700.00 | Window Closed / Lapsed |