US4380595A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Encapsulating sealant compositions for friable insulation materials
Assignee: HOLLYBROOK CREDIT Corp A NEW JERSEY CORPORATION
•
Filing: 1980-10-14
•
Granted: 1983-04-19
•
Expires: 2000-10-14
Abstract
Abstract A penetrating sealant composition useful for encapsulating a friable material which is designed to be stored in two parts, one of said parts comprising an aqueous silicate solution comprising a water soluble alkali metal silicate such as potassium silicate or a mixture of potassium silicate and sodium silicate and a cationic or nonionic surfactant and the other part comprising an acrylic polymer dispersion component comprising an acrylic polymer latex and a reagent that reacts with alkali metal silicate. The two parts are mixed to provide a blended composition having a solids content between 20 and 65 weight percent. The sealant composition is particularly useful for friable asbestos-containing materials and the cured sealant provides a physically tough flexible barrier.
Inventors
- 👤 John Arpin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 21:38
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/34; C09; C09J; C09J133/00; C09J133/04; C09J133/06; C08L; C08L2666/00; C08L2666/54; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
205 words
A penetrating sealant composition useful for encapsulating a friable material comprising a blend of: Part I an aqueous silicate solution component comprising: (a) 20 to 40 weight percent of an aqueous alkali metal silicate selected from potassium silicate or a mixture of potassium silicate and sodium silicate; (b) 0.01 to 10 weight percent of a cationic or nonionic surfactant; (c) 60 to 80 weight percent water; and Part II an acrylic polymer dispersion component comprising: (a) 45 to 65 weight percent of an acrylic polymer latex having a solids content of 40 to 65 weight percent, said acrylic polymer selected from the group consisting of homopolymers and copolymers of lower alkyl esters of acrylic acid or lower alkyl esters of an alpha-lower alkyl acid or mixtures thereof; (b) 0.01 to 10 weight percent of a reagent that reacts with said alkali silicate; said reagent being selected from the group consisting of the borate, halide, nitrate and phosphate salts of aluminum, antimony, barium, beryllium, cadmium, calcium, chromium, cobalt, copper, lead, magnesium, mercury, silver and zinc, and (c) 35 to 55 weight percent water, wherein the ratio of Part I to Part II provides a blended composition having a solids content between 20 and 65 weight percent.
Claim 2
Dependent Claim
205 words
A penetrating sealant composition useful for encapsulating a friable material comprising a blend of: Part I an aqueous silicate solution component comprising: (a) 20 to 40 weight percent of an aqueous alkali metal silicate selected from potassium silicate or a mixture of potassium silicate and sodium silicate; (b) 0.01 to 10 weight percent of a cationic or nonionic surfactant; (c) 60 to 80 weight percent water; and Part II an acrylic polymer dispersion component comprising: (a) 45 to 65 weight percent of an acrylic polymer latex having a solids content of 40 to 65 weight percent, said acrylic polymer selected from the group consisting of homopolymers and copolymers of lower alkyl esters of acrylic acid or lower alkyl esters of an alpha-lower alkyl acid or mixtures thereof; (b) 0.01 to 10 weight percent of a reagent that reacts with said alkali silicate; said reagent being selected from the group consisting of the borate, halide, nitrate and phosphate salts of aluminum, antimony, barium, beryllium, cadmium, calcium, chromium, cobalt, copper, lead, magnesium, mercury, silver and zinc, and (c) 35 to 55 weight percent water, wherein the ratio of Part I to Part II provides a blended composition having a solids content between 20 and 65 weight percent.
Claim 3
Dependent Claim
18 words
The composition according to claim 1 wherein said reagent is potassium silicofluoride, zinc silicofluoride and hydrated sodium borate.
Claim 4
Dependent Claim
200 words
In a method for enhancing the adhesion and appearance of friable materials, the improvement comprising applying to the friable material a penetrating sealant composition for encapsulating the friable material comprising a blend of: Part I an aqueous silicate solution component comprising: (a) 20 to 40 weight percent of an aqueous alkali metal silicate selected from potassium silicate or a mixture of potassium silicate and sodium silicate; (b) 0.01 to 10 weight percent of a cationic or nonionic surfactant; (c) 60 to 80 weight percent water; and Part II an acrylic polymer dispersion component comprising: (a) 45 to 65 weight percent of an acrylic polymer latex having a solids contant of 40 to 65 weight percent, said acrylic polymer selected from the group consisting of nomopolymers and copolymers of lower alkyl esters of acrylic acid or lower alkyl esters of an alpha-lower alkyl acid or mixtures thereof; (b) 0.01 to 10 weight percent of a reagent that reacts with said alkali silicate; and (c) 35 to 55 weight percent water, wherein the ratio of Part I to Part II provides a blended composition having a solids content between 20 and 65 weight percent, subsequently applying a conventional coating to said composition.
Claim 5
Dependent Claim
200 words
In a method for enhancing the adhesion and appearance of friable materials, the improvement comprising applying to the friable material a penetrating sealant composition for encapsulating the friable material comprising a blend of: Part I an aqueous silicate solution component comprising: (a) 20 to 40 weight percent of an aqueous alkali metal silicate selected from potassium silicate or a mixture of potassium silicate and sodium silicate; (b) 0.01 to 10 weight percent of a cationic or nonionic surfactant; (c) 60 to 80 weight percent water; and Part II an acrylic polymer dispersion component comprising: (a) 45 to 65 weight percent of an acrylic polymer latex having a solids contant of 40 to 65 weight percent, said acrylic polymer selected from the group consisting of nomopolymers and copolymers of lower alkyl esters of acrylic acid or lower alkyl esters of an alpha-lower alkyl acid or mixtures thereof; (b) 0.01 to 10 weight percent of a reagent that reacts with said alkali silicate; and (c) 35 to 55 weight percent water, wherein the ratio of Part I to Part II provides a blended composition having a solids content between 20 and 65 weight percent, subsequently applying a conventional coating to said composition.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-04-18 | 1986-10-18 | 1987-04-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-04-18 | 1990-10-18 | 1991-04-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-04-18 | 1994-10-18 | 1995-04-19 | $7700.00 | Window Closed / Lapsed |