High flow rate polyolefin extrusion coating compositions
Assignee: Huntsman Corp
•
Filing: 1981-09-14
•
Granted: 1983-03-29
•
Expires: 2001-09-14
Abstract
Abstract This invention relates to novel blends containing degraded crystalline polypropylene or propylene containing copolymer useful as extrusion coating compositions which provide coatings having good coatability and good heat sealability. These coated substrates then can be used in fabricating bags and other packaging applications. Particularly, these coatings are a blend of a degraded crystalline polypropylene, or propylene containing copolymer, and low density polyethylene.
Inventors
- 👤 Ray Edwards
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 22:13
CPC Classifications
C; C09; C09D; C09D123/00; C09D123/02; C09D123/10
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
113 words
An extrusion coating composition having a flow rate of 5 to 55 dg/min. at 230° C. which provides coatings of less than 1 mil which have heat seal strengths of at least 10 pounds per linear inch comprising a blend of: (1) about 75 to 95 percent, by weight, of at least one degraded crystalline polypropylene or propylene containing copolymer having a melt flow rate of 5 to 55 dg/min. at 230° C., and (2) about 5 to 25 percent, by weight, of at least one polyethylene having a density of 0.916 to 0.925, a melt index at 190° C. of 0.5 to 4.5, and a melt index recovery of greater than 40.
Claim 2
Dependent Claim
113 words
An extrusion coating composition having a flow rate of 5 to 55 dg/min. at 230° C. which provides coatings of less than 1 mil which have heat seal strengths of at least 10 pounds per linear inch comprising a blend of: (1) about 75 to 95 percent, by weight, of at least one degraded crystalline polypropylene or propylene containing copolymer having a melt flow rate of 5 to 55 dg/min. at 230° C., and (2) about 5 to 25 percent, by weight, of at least one polyethylene having a density of 0.916 to 0.925, a melt index at 190° C. of 0.5 to 4.5, and a melt index recovery of greater than 40.
Claim 3
Dependent Claim
20 words
An extrusion coating composition according to claim 1 wherein said degraded crystalline polypropylene or propylene containing copolymer is crystalline polypropylene.
Claim 4
Dependent Claim
23 words
An extrusion coating composition according to claim 2 wherein said degraded crystalline polypropylene has a melt flow rate of 35 at 230° C.
Claim 5
Dependent Claim
34 words
An extrusion coating composition according to claim 2 wherein said low density polyethylene has a melt index of 3.5 dg/min. at 190° C., a density of 0.917 g/cc, and a 70 melt index recovery.
Claim 6
Dependent Claim
28 words
An extrusion coating composition according to claim 1 wherein said degraded crystalline polypropylene or propylene containing copolymer is crystalline ethylene/propylene copolymer containing less than 5 weight percent ethylene.
Claim 7
Dependent Claim
24 words
An extrusion coating composition according to claim 5 wherein said degraded crystalline ethylene/propylene copolymer has a melt flow rate of 30 at 230° C.
Claim 8
Dependent Claim
34 words
An extrusion coating composition according to claim 5 wherein said low density polyethylene has a melt index of 3.5 dg/min. at 190° C., a density of 0.917 g/cc, and a 70 melt index recovery.
Claim 9
Dependent Claim
116 words
An extrusion coating composition having a melt flow rate of 5 to 55 dg/min. at 230° C. which provides coatings of less than 1 mil which have heat seal strengths of at least 10 pounds per linear inch comprising a blend of: (1) about 80 to 90 percent, by weight, of at least one degraded crystalline polypropylene or propylene containing copolymer having a melt flow rate of 5 to 55 dg/min. at 230° C., and (2) about 10 to 20 percent, by weight, of at least one polyethylene having a density of about 0.916 to about 0.925, a melt index at 190° C. of 0.5 to 4.5, and a melt index recovery of greater than 40.
Claim 10
Dependent Claim
116 words
An extrusion coating composition having a melt flow rate of 5 to 55 dg/min. at 230° C. which provides coatings of less than 1 mil which have heat seal strengths of at least 10 pounds per linear inch comprising a blend of: (1) about 80 to 90 percent, by weight, of at least one degraded crystalline polypropylene or propylene containing copolymer having a melt flow rate of 5 to 55 dg/min. at 230° C., and (2) about 10 to 20 percent, by weight, of at least one polyethylene having a density of about 0.916 to about 0.925, a melt index at 190° C. of 0.5 to 4.5, and a melt index recovery of greater than 40.
Claim 11
Dependent Claim
20 words
An extrusion coating composition according to claim 8 wherein said degraded crystalline polypropylene or propylene containing copolymer is crystalline polypropylene.
Claim 12
Dependent Claim
23 words
An extrusion coating composition according to claim 9 wherein said degraded crystalline polypropylene has a melt flow rate of 35 at 230° C.
Claim 13
Dependent Claim
34 words
An extrusion coating composition according to claim 9 wherein said low density polyethylene has a melt index of 3.5 dg/min. at 190° C., a density of 0.917 g/cc, and a 70 melt index recovery.
Claim 14
Dependent Claim
26 words
An extrusion coating composition according to claim 8 wherein said degraded crystalline propylene containing copolymer is crystalline ethylene/propylene copolymer containing less than 5 weight percent ethylene.
Claim 15
Dependent Claim
24 words
An extrusion coating composition according to claim 12 wherein said degraded crystalline ethylene/propylene copolymer has a melt flow rate of 30 at 230° C.
Claim 16
Dependent Claim
34 words
An extrusion coating composition according to claim 12 wherein said low density polyethylene has a melt index of 3.5 dg/min. at 190° C., a density of 0.917 g/cc, and a 70 melt index recovery.
Claim 17
Dependent Claim
103 words
An extrusion coating composition having a melt flow rate of 30 dg/min. at 230° C. which provides coatings of less than 1 mil which have heat seal strengths of at least 10 pounds per linear inch comprising a blend of: (1) about 90 percent, by weight, of at least one degraded crystalline polypropylene or propylene containing copolymer having a melt flow rate of 30 to 35 dg/min. at 230° C., and (2) about 10 percent, by weight, of at least one polyethylene having a density of about 0.917, a melt index at 190° C. of 3.5, and a melt index recovery of 70.
Claim 18
Dependent Claim
103 words
An extrusion coating composition having a melt flow rate of 30 dg/min. at 230° C. which provides coatings of less than 1 mil which have heat seal strengths of at least 10 pounds per linear inch comprising a blend of: (1) about 90 percent, by weight, of at least one degraded crystalline polypropylene or propylene containing copolymer having a melt flow rate of 30 to 35 dg/min. at 230° C., and (2) about 10 percent, by weight, of at least one polyethylene having a density of about 0.917, a melt index at 190° C. of 3.5, and a melt index recovery of 70.
Claim 19
Dependent Claim
20 words
An extrusion coating composition according to claim 15 wherein said degraded crystalline polypropylene or propylene containing copolymer is crystalline polypropylene.
Claim 20
Dependent Claim
23 words
An extrusion coating composition according to claim 16 wherein said degraded crystalline polypropylene has a melt flow rate of 35 at 230° C.
Claim 21
Dependent Claim
34 words
An extrusion coating composition according to claim 17 wherein said low density polyethylene has a melt index of 3.5 dg/min. at 190° C., a density of 0.917 g/cc, and a 70 melt index recovery.
Claim 22
Dependent Claim
26 words
An extrusion coating composition according to claim 15 wherein said degraded crystalline propylene containing copolymer is crystalline ethylene/propylene copolymer containing less than 5 weight percent ethylene.
Claim 23
Dependent Claim
24 words
An extrusion coating composition according to claim 19 wherein said degraded crystalline ethylene/propylene copolymer has a melt flow rate of 30 at 230° C.
Claim 24
Dependent Claim
34 words
An extrusion coating composition according to claim 20 wherein said low density polyethylene has a melt index of 3.5 dg/min. at 190° C., a density of 0.917 g/cc, and a 70 melt index recovery.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-03-28 | 1986-09-27 | 1987-03-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-03-28 | 1990-09-27 | 1991-03-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-03-28 | 1994-09-27 | 1995-03-29 | $7700.00 | Window Closed / Lapsed |