Method for manufacturing a Nb3 Sn superconductor and method for manufacturing hollow superconducting magnet
Assignee: Fujikura Ltd
•
Filing: 1981-02-20
•
Granted: 1983-03-29
•
Expires: 2001-02-20
Abstract
Abstract A method for manufacturing a Nb 3 Sn superconductor comprising the steps of preparing a composite conductor element which is composed of Cu-Sn alloy matrix and one or more Nb cores inserted and disposed in said matrix, if necessary sheathing the outer surface of the Cu-Sn alloy matrix with copper, subjecting the composite conductor element to a diameter reducing working until the predetermined diameter is reached, then forming an Sn-plating layer on the outer surface of the reduced diameter composite conductor element and thereafter subjecting the Sn-plated composite conductor element to diffusion heat treatment so that an intermetallic compound of Nb 3 Sn is formed, and a method for manufacturing hollow superconducting magnet off an intermetallic compound type comprising the steps of extending a plurality of multicore superconductors together with thin tapes of a low temperature melting metal along grooves of a hollow conductor carrier, winding the superconductor assembly around a magnet reel and then heating up the superconducting magnet assembly to melt the thin tape of low temperature melting metal so that the multicore superconductors are secured to the hollow conductor carrier.
Inventors
- 👤 Koh Agatsuma
- 👤 Kenichi Koyama
- 👤 Itaru Todoriki
- 👤 Osamu Kohno
- 👤 Takashi Saito
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 09:31
CPC Classifications
H; H01; H01F; H01F27/00; H01F27/28; H01F27/2804; H01F27/2819; H01F41/00; H01F41/02; H01F41/04; H01F41/048; H01F6/00; H01F6/06; H10; H10N; H10N60/00; H10N60/01; H10N60/0184; Y; Y10; Y10S; Y10S505/00; Y10S505/825; Y10S505/917; Y10S505/918; Y10S505/919; Y10S505/921; Y10S505/924; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49014; Y10T29/4902; Y10T29/49071
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
202 words
A method of manufacturing a hollow superconducting magnet of an intermetallic compound type, comprising the steps of: (a) preparing an elongated hollow conductor carrier made of an excellent conducting material, said carrier having (i) a passage formed therethrough for flowing a cooling medium and (ii) a groove having a bottom wall and an opening formed on an outer surface thereof and extending in a longitudinal direction; (b) inserting a multicore superconductor in said groove, said superconductor extending along said groove with said superconductor having an upper surface and a lower surface with the lower surface being adjacent said bottom wall of said groove and the upper surface extending within the opening of said groove; (c) extending a tape of low temperature melting metal along at least one of the upper surface and lower surface of said superconductor; (d) wrapping an insulating tape about the carrier thereby forming a superconductor assembly; (e) winding said superconductor assembly around a magnet reel to form a magnet assembly; (f) subsequent to step (e) heating said magnet assembly to melt said low temperature melting metal tape; and (g) cooling said magnet assembly to solidify said metal tape, thereby securing said multicore superconductor to said hollow conductor carrier.
Claim 2
Independent Claim
202 words
A method of manufacturing a hollow superconducting magnet of an intermetallic compound type, comprising the steps of: (a) preparing an elongated hollow conductor carrier made of an excellent conducting material, said carrier having (i) a passage formed therethrough for flowing a cooling medium and (ii) a groove having a bottom wall and an opening formed on an outer surface thereof and extending in a longitudinal direction; (b) inserting a multicore superconductor in said groove, said superconductor extending along said groove with said superconductor having an upper surface and a lower surface with the lower surface being adjacent said bottom wall of said groove and the upper surface extending within the opening of said groove; (c) extending a tape of low temperature melting metal along at least one of the upper surface and lower surface of said superconductor; (d) wrapping an insulating tape about the carrier thereby forming a superconductor assembly; (e) winding said superconductor assembly around a magnet reel to form a magnet assembly; (f) subsequent to step (e) heating said magnet assembly to melt said low temperature melting metal tape; and (g) cooling said magnet assembly to solidify said metal tape, thereby securing said multicore superconductor to said hollow conductor carrier.
Claim 3
Dependent Claim
31 words
A method according to claim 1, wherein said low temperature melting metal is selected from the group consisting of an Sn-Ag alloy, Sn, an Sn-Pb alloy, In and an In alloy.
Claim 4
Dependent Claim
25 words
A method according to claim 2, further comprising the step of preforming said multicore superconductor so as to fit in said groove of said carrier.
Claim 5
Dependent Claim
55 words
A method according to claim 3, wherein said preforming step comprises braiding a plurality of composite conductor elements to form a braided conductor element assembly, working said braided conductor element assembly to fit in said groove, and thereafter subjecting said worked conductor element assembly to a diffusion heat treatment, whereby said multicore superconductor is formed.
Claim 6
Dependent Claim
72 words
A method according to claim 3 wherein the construction of said multicore superconductor comprises: (a) inserting a plurality of Nb cores into a Cu-Sn matrix, containing less than 10% Sn by weight, to form a composite conductor element; (b) reducing the diameter of said element to a predetermined value; (c) electrodepositing a layer of tin on the surface of said reduced diameter element; and (f) diffusion heat treating said tin electroplated element.
Claim 7
Dependent Claim
87 words
A method according to claim 3 wherein the construction of said multicore superconductor comprises: (a) inserting a plurality of Nb cores into a Cu-Sn matrix, containing 2-15% Sn by weight, to form a composite conductor element; (b) sheathing the surface of said element with a copper layer to form a copper-sheathed element assembly; (c) reducing the diameter of said assembly to a predetermined value; (d) electrodepositing a layer of tin on the surface of said reduced diameter sheathed assembly; and (e) diffusion heat treating said tin-electroplated assembly.
Claim 8
Dependent Claim
169 words
A method according to claim 2 wherein the construction of said multicore superconductor comprises: (a) providing a first hollow pipe composed of an alloy of copper and one constituent of an intermetallic compound selected from the group consisting of Nb 3 Sn, V 3 Ga, Nb 3 Ge, Nb 3 Ga, Nb 3 Si, Nb 3 Al and Nb 3 (Al 0 .8 Ge 0 .2); (b) inserting into said pipe a plurality of cores composed of the other constituent of said intermetallic compound to form a composite conductor element; (c) reducing the diameter of said element to a predetermined value; (d) assembling a plurality of said reduced diameter elements to form a bundle; (e) inserting said bundle into a second hollow pipe of the same composition as said first hollow pipe to form an assembly; (f) reducing the diameter of said assembly to a predetermined value; (g) working said reduced diameter assembly to fit into the groove of said carrier; and (h) diffusion heat treating said worked assembly.
Claim 9
Dependent Claim
163 words
A method according to claim 2 wherein the construction of said multicore superconductor comprises: (a) providing a first hollow copper pipe; (b) inserting into said pipe a plurality of cores composed of one constituent of an intermetallic compound selected from the group consisting of Nb 3 Sn, V 3 Ga, Nb 3 Ge, Nb 3 Ga, Nb 3 Si, Nb 3 Al and Nb 3 (Al 0 .8 Ge 0 .2), to form a composite conductor element; (c) reducing the diameter of said element to a predetermined value; (d) assembling a plurality of said reduced diameter elements to form a bundle; (e) inserting said bundle into a second hollow copper pipe to form an assembly; (f) reducing the diameter of said assembly to a predetermined value; (g) electrodepositing on said reduced diameter assembly a layer of the other constituent of said intermetallic compound; (h) working said electroplated assembly to fit into the groove of said carrier; and (i) diffusion heat treating said assembly.
Claim 10
Dependent Claim
23 words
A method as set forth in claim 1, wherein said hollow conductor carrier is constructed of copper and has a substantially rectangular cross-section.
Claim 11
Dependent Claim
31 words
A method as set forth in claim 2, wherein said metal tape is heated and molten in a non-oxidizing atmosphere at a temperature higher than the melting point of said metal.
Claim 12
Dependent Claim
18 words
A method as set forth in claim 2, wherein said metal tape is heated and molten under vacuum.
References Cited (Backward Citations)
US3046509A
Cited
US3728165A
Cited
US3731374A
Cited
US3905839A
Cited
US3836404A
Cited
US3996661A
Cited
US3954572A
Cited
US4084989A
Cited
US4053976A
Cited
US4043028A
Cited
US4254299A
Cited
US4161062A
Cited
US4195199A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-03-28 | 1986-09-27 | 1987-03-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-03-28 | 1990-09-27 | 1991-03-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-03-28 | 1994-09-27 | 1995-03-29 | $7700.00 | Window Closed / Lapsed |