Method for producing compacts and cladding from glassy metallic alloy filaments by warm extrusion
Assignee: General Electric Co
•
Filing: 1980-08-25
•
Granted: 1983-03-22
•
Expires: 2000-08-25
Abstract
Abstract Filaments of glassy metallic alloys prepared by chill block melt-spinning are consolidated under heat and pressure by an extrusion process. Products obtainable by the process include discrete bodies of glassy metallic alloys of substantially uniform composition and articles having one or more layers of glassy metallic alloy clad onto one or more non-glassy metallic alloy substrates.
Inventors
- 👤 Howard H. Liebermann
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 21:56
CPC Classifications
B; B22; B22F; B22F9/00; B22F9/002; B22F9/008; B22F3/00; B22F3/006; B22F3/12; B22F3/1208; B22F3/20; B22F7/00; B22F7/06; H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/12; H01F1/14; H01F1/147; H01F1/153; H01F1/15358; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12424
Claims Analysis
Total Claims: 36
Claim 1
Independent Claim
205 words
The method for consolidating glassy metallic alloy in filamentary form comprising the steps of: (a) preparing an assembly of at least an outer metallic container having one end open and a preselected amount of intertwined filamentary glassy metallic alloy disposed substantially uniformly therein and packed to a density of from about 50% to about 60% of theoretical; (b) closing said open end by inserting a plunger into said open end forming thereby an extrusion billet; (c) heating said extrusion billet to a substantially uniform temperature throughout, said temperature being in the range between the plastic transition temperature and the crystallization temperature of said alloy; (d) extruding said billet to reduce the cross section thereof by an extrusion ratio of at least about 3.5 to 1 while maintaining the temperature of said billet at a substantially uniform value throughout in the range between the plastic transition temperature and the crystallization temperature of said alloy; and (e) recovering an extruded product of reduced cross section in which the contiguous surface areas of said intertwined filamentary glassy metallic alloy have been metallurgically bonded together by the application of inter-filament shearing forces to form a solid dense glassy metallic alloy body surrounded by and metallurgically bonded to said container.
Claim 2
Independent Claim
205 words
The method for consolidating glassy metallic alloy in filamentary form comprising the steps of: (a) preparing an assembly of at least an outer metallic container having one end open and a preselected amount of intertwined filamentary glassy metallic alloy disposed substantially uniformly therein and packed to a density of from about 50% to about 60% of theoretical; (b) closing said open end by inserting a plunger into said open end forming thereby an extrusion billet; (c) heating said extrusion billet to a substantially uniform temperature throughout, said temperature being in the range between the plastic transition temperature and the crystallization temperature of said alloy; (d) extruding said billet to reduce the cross section thereof by an extrusion ratio of at least about 3.5 to 1 while maintaining the temperature of said billet at a substantially uniform value throughout in the range between the plastic transition temperature and the crystallization temperature of said alloy; and (e) recovering an extruded product of reduced cross section in which the contiguous surface areas of said intertwined filamentary glassy metallic alloy have been metallurgically bonded together by the application of inter-filament shearing forces to form a solid dense glassy metallic alloy body surrounded by and metallurgically bonded to said container.
Claim 3
Dependent Claim
46 words
The method of claim 1 wherein said outer metallic container is a composite of a first metal surrounding a second metal, said second metal being harder and stronger than said first metal and being interposed between said first metal and said intertwined filamentary glassy metallic alloy.
Claim 4
Dependent Claim
43 words
The method of claim 2 wherein said first metal is an alloy of copper and nickel and said second metal is steel, said nickel being present in said alloy in the range of from about 10 weight percent to about 30 weight percent.
Claim 5
Dependent Claim
23 words
The method of claim 1 further including the step of removing said outer metallic container from said extruded product by a metalworking process.
Claim 6
Dependent Claim
28 words
A consolidated dense discrete metallic body that is at least 50% glassy with any remainder crystalline, said body being prepared in accordance with the method of claim 4.
Claim 7
Dependent Claim
11 words
The body of claim 5 wherein said body is totally glassy.
Claim 8
Dependent Claim
13 words
The body of claim 5 wherein said body is at least 80% dense.
Claim 9
Dependent Claim
79 words
The method of claim 1 in which said preselected amount of substantially intertwined filamentary glassy metallic alloy is disposed in said metallic container by repeatedly partially filling said container with a portion of said preselected amount of said alloy and partially compacting said portion of said filamentary alloy to a substantially uniform packing density of about at least 50% to no more than about 60% of theoretical until said container is filled with said preselected amount of said alloy.
Claim 10
Dependent Claim
47 words
The method of claim 1 wherein the closing step is accomplished in a vacuum chamber, said vacuum chamber having been evacuated to a reduced pressure of at least less than 10 -4 Torr and maintained thereat for at least one hour prior to insertion of said plunger.
Claim 11
Dependent Claim
24 words
The method of claim 9 wherein said vacuum chamber is maintained at a substantially constant elevated temperature below the crystallization temperature of said alloy.
Claim 12
Dependent Claim
17 words
The method of claim 1 further including the step of tack welding said plunger to said container.
Claim 13
Dependent Claim
17 words
The method of claim 9 further including the step of seal welding said plunger to said container.
Claim 14
Dependent Claim
15 words
The method of claim 12 wherein said seal weld is effected by an electron beam.
Claim 15
Dependent Claim
19 words
The method of claim 1 wherein said heating step is carried out rapidly by means of induction heating apparatus.
Claim 16
Dependent Claim
42 words
The method of claim 1 wherein said assembly comprises a solid crystalline metallic core centrally disposed within said outer metallic container with said preselected amount of intertwined filamentary glassy metallic alloy being disposed within the region between said core and said container.
Claim 17
Dependent Claim
88 words
A composite body produced by the method of claim 15 in which the contiguous surface areas of said intertwined filamentary glassy metallic alloy have been metallurgically bonded together to form a consolidated dense region by the application of inter-filament shearing forces and in which the surface areas of said intertwined filamentary glassy metallic alloy contiguous with said core and said container have been metallurgically clad to said core and said container by said shearing forces, said consolidated dense region being at least 50% glassy with any remainder crystalline.
Claim 18
Dependent Claim
13 words
The composite body of claim 16 wherein said dense region is totally glassy.
Claim 19
Dependent Claim
15 words
The composite body of claim 16 wherein said dense region is at least 80% dense.
Claim 20
Dependent Claim
58 words
The method of claim 1 wherein said assembly comprises a hollow crystalline metallic core centrally disposed within said outer metallic container with a first preselected amount of intertwined filamentary glassy metallic alloy disposed within said hollow core and a second preselected amount of intertwined filamentary glassy metallic alloy disposed within the region between said core and said container.
Claim 21
Dependent Claim
30 words
The method of claim 19 wherein said first preselected amount of glassy alloy has substantially the same chemical composition and physical properties as said second preselected amount of glassy alloy.
Claim 22
Dependent Claim
134 words
A composite body produced by the method of claim 19 in which the contiguous surface areas of said intertwined filamentary glassy metallic alloy in said core have been metallurgically bonded together to form a first consolidated dense region by the application of inter-filament shearing forces, the contiguous surface areas of said intertwined filamentary glassy metallic alloy in said region between said core and said container have been metallurgically bonded together to form a second consolidated dense region by the application of inter-filament shearing forces, and in which the surface areas of said intertwined filamentary glassy metallic alloys contiguous with said core and said container have been metallurgically clad to said core and said container by said shearing forces, said first and second consolidated dense region being at least 50% glassy with any remainder crystalline.
Claim 23
Dependent Claim
13 words
The composite body of claim 21 wherein said first region is totally glassy.
Claim 24
Dependent Claim
13 words
The composite body of claim 21 wherein said second region is totally glassy.
Claim 25
Dependent Claim
15 words
The composite body of claim 21 wherein said first region is at least 80% dense.
Claim 26
Dependent Claim
15 words
The composite body of claim 21 wherein said second region is at least 80% dense.
Claim 27
Independent Claim
295 words
The method for consolidating magnetically soft glassy metallic alloy in filamentary form while substantially maintaining the soft magnetic properties of the alloy comprising the steps of: (a) preparing an assembly comprising at least an outer metallic container having one end open and a preselected amount of magnetically soft intertwined filamentary glassy metallic alloy disposed loosely and substantially uniformly therein by preheating said alloy to a temperature in the range between the plastic transition temperature and the crystallization temperature of said alloy and disposing said alloy in said container without causing heterogeneous plastic flow of said alloy, said container being maintained at a substantially uniform temperature throughout in the range between the plastic transition temperature and the crystallization temperature of said alloy; (b) closing said open end by inserting a plunger preheated to a temperature in the range between the plastic transition temperature and the crystallization temperature of said alloy into said open end without compressing said magnetically soft filamentary alloy disposed therein to form an extrusion billet; (c) extruding said heated billet to reduce the cross section thereof by an extrusion ratio of at least about 3.5 to 1 while maintaining the temperature of said billet at a substantially uniform value throughout in the range between the plastic transition temperature and the crystallization temperature of said alloy; and (d) recovering an extruded product of reduced cross section in which the contiguous surface areas of said interwined filamentary magnetically soft glassy metallic alloy have been metallurgically bonded together by the application of inter-filament shearing forces to form a solid dense magnetically soft glassy metallic alloy body and in which the surface areas of said intertwined filamentary magnetically soft glassy metallic alloy contiguous with said container have been metallurgically bonded to said container by said shearing forces.
Claim 28
Independent Claim
295 words
The method for consolidating magnetically soft glassy metallic alloy in filamentary form while substantially maintaining the soft magnetic properties of the alloy comprising the steps of: (a) preparing an assembly comprising at least an outer metallic container having one end open and a preselected amount of magnetically soft intertwined filamentary glassy metallic alloy disposed loosely and substantially uniformly therein by preheating said alloy to a temperature in the range between the plastic transition temperature and the crystallization temperature of said alloy and disposing said alloy in said container without causing heterogeneous plastic flow of said alloy, said container being maintained at a substantially uniform temperature throughout in the range between the plastic transition temperature and the crystallization temperature of said alloy; (b) closing said open end by inserting a plunger preheated to a temperature in the range between the plastic transition temperature and the crystallization temperature of said alloy into said open end without compressing said magnetically soft filamentary alloy disposed therein to form an extrusion billet; (c) extruding said heated billet to reduce the cross section thereof by an extrusion ratio of at least about 3.5 to 1 while maintaining the temperature of said billet at a substantially uniform value throughout in the range between the plastic transition temperature and the crystallization temperature of said alloy; and (d) recovering an extruded product of reduced cross section in which the contiguous surface areas of said interwined filamentary magnetically soft glassy metallic alloy have been metallurgically bonded together by the application of inter-filament shearing forces to form a solid dense magnetically soft glassy metallic alloy body and in which the surface areas of said intertwined filamentary magnetically soft glassy metallic alloy contiguous with said container have been metallurgically bonded to said container by said shearing forces.
Claim 29
Dependent Claim
23 words
The method of claim 26 further including the step of removing said outer metallic container from said extruded product by a metalworking process.
Claim 30
Dependent Claim
30 words
A consolidated dense discrete magnetically soft metallic body that is at least 50% glassy with any remainder crystalline, said body being prepared in accordance with the method of claim 27.
Claim 31
Dependent Claim
11 words
The body of claim 28 wherein said body is totally glassy.
Claim 32
Dependent Claim
13 words
The body of claim 28 wherein said body is at least 80% dense.
Claim 33
Dependent Claim
48 words
The method of claim 26 wherein said outer metallic container is a composite of a first metal surrounding a second metal, said second metal being harder and stronger than said first metal and being interposed between said first metal and said magnetically soft intertwined filamentary glassy metallic alloy.
Claim 34
Dependent Claim
43 words
The method of claim 31 wherein said first metal is an alloy of copper and nickel and said second metal is steel, said nickel being present in said alloy in the range of from about 10 weight percent to about 30 weight percent.
Claim 35
Dependent Claim
47 words
The method of claim 26 wherein the closing step is accomplished in a vacuum chamber, said vacuum chamber having been evacuated to a reduced pressure of at least less than 10 -4 Torr and maintained thereat for at least one hour prior to insertion of said plunger.
Claim 36
Dependent Claim
24 words
The method of claim 33 wherein said vacuum chamber is maintained at a substantially constant elevated temperature below the crystallization temperature of said alloy.
References Cited (Backward Citations)
US3824097A
Cited
US4079430A
Cited
US4038073A
Cited
US4197146A
Cited
US4201837A
Cited
US4267626A
Cited
US4298382A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-03-21 | 1986-09-20 | 1987-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-03-21 | 1990-09-20 | 1991-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-03-21 | 1994-09-20 | 1995-03-22 | $7700.00 | Window Closed / Lapsed |