Method of making Schottky barrier diode by selective beam-crystallized polycrystalline/amorphous layer
Assignee: Fujitsu Ltd
•
Filing: 1981-04-01
•
Granted: 1983-03-22
•
Expires: 2001-04-01
Abstract
Abstract Generally, a complicated process is required in manufacturing a semiconductor device containing a Schottky barrier diode and a polycrystalline silicon layer which prevents excessive reaction of the aluminum electrode and silicon material involved. Because of the inability of the aluminum electrode to provide a good Schottky barrier by its contact with the polycrystalline silicon layer, it is required to directly contact the electrode with a monocrystalline silicon semiconductor layer or substrate. According to the present invention, this process is simplified by monocrystallizing the polycrystalline silicon layer at least in the region in which a Schottky barrier diode is to be formed by annealing the silicon layer in said region by laser beam irradiation and applying an aluminum electrode thereto.
Inventors
- 👤 Hiroshi Goto
- 👤 Kenji Sugishima
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 17:43
CPC Classifications
H; H10; H10P; H10P95/00; H10P95/90; H10D; H10D48/00; H10D48/30; H10D48/32; H10D48/34; H10D48/345; H10D64/00; H10D64/01; H10D64/012; H10D64/0121; H10P34/00; H10P34/40; H10P34/42; Y; Y10; Y10S; Y10S117/00; Y10S117/903; Y10S117/904; Y10S148/00; Y10S148/046; Y10S148/092; Y10S148/093
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
177 words
A method of manufacturing a semiconductor device comprising the steps of: forming an insulating layer on a semiconductor substrate; selectively removing the insulating layer until the top surface of the semiconductor substrate is exposed to open a plurality of windows, including a window in which to form a Schottky barrier diode and windows in which to form electrodes; forming a polycrystalline or amorphous semiconductor layer covering the exposed surface of the semiconductor substrate and the remaining insulating layer; applying an energy beam to the polycrystalline or amorphous semiconductor layer at least in the window in which to form the Schottky barrier diode to convert the polycrystalline or amorphous semiconductor layer ito a single-crystal semiconductor layer; depositing a Schottky barrier diode forming metal layer on the single-crystal semiconductor layer to form a Schottky barrier contact between the metal layer and the single-crystal semiconductor layer; and depositing an electrode forming metal layer on the semiconductor layer in each of the windows in which to form electrodes to form an ohmic contact between the metal layer and the semiconductor layer.
Claim 2
Independent Claim
177 words
A method of manufacturing a semiconductor device comprising the steps of: forming an insulating layer on a semiconductor substrate; selectively removing the insulating layer until the top surface of the semiconductor substrate is exposed to open a plurality of windows, including a window in which to form a Schottky barrier diode and windows in which to form electrodes; forming a polycrystalline or amorphous semiconductor layer covering the exposed surface of the semiconductor substrate and the remaining insulating layer; applying an energy beam to the polycrystalline or amorphous semiconductor layer at least in the window in which to form the Schottky barrier diode to convert the polycrystalline or amorphous semiconductor layer ito a single-crystal semiconductor layer; depositing a Schottky barrier diode forming metal layer on the single-crystal semiconductor layer to form a Schottky barrier contact between the metal layer and the single-crystal semiconductor layer; and depositing an electrode forming metal layer on the semiconductor layer in each of the windows in which to form electrodes to form an ohmic contact between the metal layer and the semiconductor layer.
Claim 3
Dependent Claim
26 words
The method of claim 1 wherein said energy beam is selected from the group consisting of a photon beam, an electron beam and an ion beam.
Claim 4
Dependent Claim
25 words
The method of claim 1 wherein the step of selectively removing the insulating layer comprises patterning the insulating layer using a single photoresist masking layer.
Claim 5
Dependent Claim
15 words
The method of claim 3 wherein the photoresist masking layer is of a positive type.
Claim 6
Dependent Claim
31 words
The method of claim 3 wherein the step of selectively removing the insulating layer further comprises removing the single photoresist masking layer prior to forming the polycrystalline or amorphous semiconductor layer.
Claim 7
Dependent Claim
42 words
The method of claim 1, 2, 3 or 4 wherein in the step of applying an energy beam, only the portion of the polycrystalline or amorphous layer around the window in which the Schottky barrier diode is to be formed is monocrystallized.
Claim 8
Dependent Claim
38 words
The method of claim 5 wherein in the step of applying an energy beam, only the portion of the polycrystalline or amorphous layer around the window in which the Schottky barrier diode is to be formed is monocrystallized.
References Cited (Backward Citations)
US3771026A
Cited
US4059461A
Cited
US4187126A
Cited
US4267011A
Cited
US4292091A
Cited
US4269631A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-03-21 | 1986-09-20 | 1987-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-03-21 | 1990-09-20 | 1991-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-03-21 | 1994-09-20 | 1995-03-22 | $7700.00 | Window Closed / Lapsed |