Recovery of gadolinium and gallium oxides

Assignee: Honeywell International Inc
•
Filing: 1981-12-28
•
Granted: 1983-03-01
•
Expires: 2001-12-28
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract Gd2O3 and Ga2O3 are currently used for the fabrication of Gd3Ga5O12 (GGG) wafers which are employed as substrates for bubble domain memory devices. In the processing, in the order of 25% of the starting material ends up as process "saw kerf" contaminated with variable amounts of iron, nickel, magnesium, aluminum, zirconium, iridium and silicon. A process is described whereby the "saw kerf" can be reprocessed in sufficient purity to be re-used in the process, thereby improving the economics of production of GGG wafers significantly. Gadolinium and gallium oxides are recovered and separated from transition metal impurities introduced during fabrication of GGG wafers. The process "saw kerf" produced from slicing the crystal boule is dissolved in HCl, treated with H2SO4, and the resulting sulfates separated. Metathesis with (NH4)2C2O4 results in conversion of the sulfates to the ammonium oxalates which were calcined at 850 DEG C. to form Ga2O3 and Gd2O3 of purity >99.99%. The process can be extended to include purification and re-use of by-products generated in other grinding and polishing operations which may result in the recycling of the order of 80% of the generated by-products.

Inventors

  • 👤 David Nalewajek
  • 👤 Eugene B. Recla
  • 👤 Robert A. Wiles
  • 👤 Richard E. Eibeck

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-11-09 03:52
CPC Classifications
C; C01; C01G; C01G15/00; C01F; C01F17/00; C01F17/20; C01F17/206; C01F17/224; C01F17/282; C01F17/30; C01P; C01P2004/00; C01P2004/60; C01P2004/61; C01P2006/00; C01P2006/80

Claims Analysis

Total Claims: 4
Claim 1
Independent Claim 199 words
A method for recovering gadolinium and gallium oxides from by product material which contains both of these oxides and various impurities comprising the steps of: (a) dissolving the gadolinium and gallium oxide in a strong mineral acid selected from the group consisting of hydrochloric and nitric acids, (b) isolating the filtrate and precipitating gadolinium sulfate from said filtrate by adding thereto sulfuric acid, (c) separating washing and drying the precipitated gadolinium sulfate, (d) converting the gadolinium sulfate salt from step (c) to ammonium gadolinium sulfate by dissolving the sulfate salt and precipitating with ammonium oxalate and calcining the recovered ammonium gadolinium oxalate to yield gadolinium oxide, (e) distilling the filtrate from step (b) to reduce the volume and thereby precipitate therefrom gallium sulfate, (f) separating and dissolving the precipitate from step (e) in water and precipitating the gallium sulfate from the aqueous solution with excess ethanol, (g) washing and drying the gallium sulfate obtained in step (f), dissolving this salt in water, treating the solution with ammonium oxalate and precipitating from said solution, by the addition of ammonium hydroxide, ammonium gallium oxalate and gallium hydroxide and (h) isolating, drying and calcining precipitate from step (g) to form gallium oxide.
Claim 2
Independent Claim 199 words
A method for recovering gadolinium and gallium oxides from by product material which contains both of these oxides and various impurities comprising the steps of: (a) dissolving the gadolinium and gallium oxide in a strong mineral acid selected from the group consisting of hydrochloric and nitric acids, (b) isolating the filtrate and precipitating gadolinium sulfate from said filtrate by adding thereto sulfuric acid, (c) separating washing and drying the precipitated gadolinium sulfate, (d) converting the gadolinium sulfate salt from step (c) to ammonium gadolinium sulfate by dissolving the sulfate salt and precipitating with ammonium oxalate and calcining the recovered ammonium gadolinium oxalate to yield gadolinium oxide, (e) distilling the filtrate from step (b) to reduce the volume and thereby precipitate therefrom gallium sulfate, (f) separating and dissolving the precipitate from step (e) in water and precipitating the gallium sulfate from the aqueous solution with excess ethanol, (g) washing and drying the gallium sulfate obtained in step (f), dissolving this salt in water, treating the solution with ammonium oxalate and precipitating from said solution, by the addition of ammonium hydroxide, ammonium gallium oxalate and gallium hydroxide and (h) isolating, drying and calcining precipitate from step (g) to form gallium oxide.
Claim 3
Dependent Claim 90 words
The method of claim 1 wherein the gadolinium sulfate from step (c) and the gallium sulfate from step (f) are dissolved in water and co-precipitated by excess ethanol and washed, whereby the gadolinium is separated from the gallium by dissolving the mixture in strongly acidic aqueous nitric acid solution, adding a stoichiometric amount of ammonium oxalate to precipitate the gadolinium salt adjusting the separated filtrate to a pH in the range of 7-9 with ammonium hydroxide and washing, drying and calcining the resulting ammonium gallium oxalate and gallium hydroxide precipitates.
Claim 4
Dependent Claim 21 words
The method of claim 1 wherein the gadolinium and gallium oxide dissolved in step (a) is preheated to remove organic impurities.

References Cited (Backward Citations)

US4198231A Cited
EP0021990A1 Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1986-02-28 1986-08-30 1987-03-01 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1990-02-28 1990-08-30 1991-03-01 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1994-02-28 1994-08-30 1995-03-01 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag