Process for preparing polyarylates

Claim 2

A process for preparing polyarylate having a reduced viscosity of from about 0.5 to greater than 1.0 dl/gm, which process comprises reacting, at a temperature of from about 260 to about 350° C: (a) at least one diester derivative of a dihydric phenol having the following formula: ##STR6## wherein R is independently selected from an alkyl radical having from 1 to about 6 carbon atoms or cycloalkyl having from 4 to about 7 carbon atoms, y is independently selected from alkyl groups of 1 to 4 carbon atoms, chlorine, or bromine, z independently has a value of from 0 to 4, inclusive, and R' is independently selected from a divalent saturated aliphatic hydrocarbon radical having 1 to 8 carbon atoms, a cycloalkylene or cycloalkylidene readical having up to and including 9 carbon atoms, O, S, SO, SO 2 , CO, x is 0 or 1; with (b) at least one aromatic dicarboxylic acid, in the presence of from about 10 to about 60 weight percent, based on the polyarylate produced, of at least one halogenated and/or etherated substituted aromatic or heteroaromatic compound, said reaction being conducted in the absence of a catalyst, and wherein the halogenated and/or etherated substitued aromatic or hereroaromatic compound is of the following formulae: ##STR7## wherein X is independently Cl, Br, F, or OR 2 , a is an integer of 1 to 5, R 1 is independently alkyl of 1 to 16 carbon atoms, cycloalkyl of 6 to 18 atoms, aryl of 6 to 18 carbon atoms, or aralkyl or alkaryl of 7 to 18 carbon atoms, R 2 is independently alkyl of 1 to 16 carbon atoms or cycloalkyl of 6 to 18 carbon atoms, A is O, S, or --CH═N--, b is an integer of 0, 1, or 2, c is an integer of 0 to (8-a), d is an integer of 1 to 4, f is an integer of 0 to (4-d), with the proviso that the halogenated and/or etherified substitued aromatic compounds are free from benzylic and/or tertiary hydrogen atoms.

Claim 3

A process as defined in claim 1 wherein the diester derivative of the dihydric phenol has the following formula: ##STR8##

Claim 4

A process as defined in claim 2 wherein each z in 0.

Claim 5

A process as defined in claim 1 wherein the aromatic dicarboxylic acid is a mixture of isophthalic acid and terephthalic acid.

Claim 6

A process as defined in claim 4 wherein the isophthalic acid to terephthalic acid ratio in the mixture is about 25:80 to about 100:0.

Claim 7

A process as defined in claim 1 wherein the temperature is between about 275° C. and about 295° C.

Claim 8

A process as defined in claim 1 wherein the aromatic compound is selected from 1,2,4-trichlorobenzene, 1,4-dimethoxybenzene, o-dichlorobenzene, or anisole.

Claim 9

A process as defined in claim 1 wherein the polyarylate has a reduced viscosity of from about 0.6 to about 0.8.

Claim 10

A process as defined in claim 1 wherein the halogenated and/or etherated substituted aromatic or heteroaromatic compound is present in an amount of from about 25 to about 60 weight percent.

Claim 11

A process for preparing a polyarylate having a reduced viscosity of from about 0.5 to greater than 1.0 dl/gm which process comprises reacting at a temperature of from about 260° to about 350° C.: (a) an acid anhydride based on an acid containing from 2 to 8 carbon atoms; (b) at least one dihydric phenol having the following formula; ##STR9## wherein y is independently selected from alkyl groups of 1 to 4 carbon atoms, chlorine or bromine, z independently has a value of from 0 to 4, inclusive, R' is independently selected from a divalent saturated hydrocarbon radical having 1 to 8 carbon atoms, a cycloalkylene or cycloalkylidene radical having up to and including 9 carbon atoms, 0, S, SO 2 , CO, x is 0 to 1; and (c) at least one aromatic dicarboxylic acid, in the presence of from about 10 to 60 weight percent, based on the polyarylate produced, of at least one halogenated and/or etherated substituted aromatic or neteroaromatic compound, said reaction being conducted in the absence of a catalyst for the dihydric phenol and aromatic dicarboxylic acid, and wherein the halogenated and/or etherated substituted aromatic or heteraromatic compound is of the following formulae: ##STR10## wherein X is independently Cl, LBr, F, or OR 2 , a is an integer of 1 to 5, R 1 is independently alkyl of 1 to 16 carbon atoms, cycloalkyl of 6 to 18 carbon atoms, aryl of 6 to 18 carbon atoms, or aralkyl or alkyaryl of 7 to 18 carbon atoms, R 2 is independently alkyl of 1 to 16 carbon atoms or cycloalkyl of 6 to 18 carbon atoms, A is O, S, or --CH═N--, of 0, 1, or 2, c is an integer of 0 to (8-a), d is an integer of 1 to 4, f is an integer of 0 to (4-d), with the proviso that the halogenated and/or etherified substitued aromatic compounds are free from benzylic and/or tertiary hydrogen atoms.

Claim 12

A process for preparing a polyarylate having a reduced viscosity of from about 0.5 to greater than 1.0 dl/gm which process comprises reacting at a temperature of from about 260° to about 350° C.: (a) an acid anhydride based on an acid containing from 2 to 8 carbon atoms; (b) at least one dihydric phenol having the following formula; ##STR9## wherein y is independently selected from alkyl groups of 1 to 4 carbon atoms, chlorine or bromine, z independently has a value of from 0 to 4, inclusive, R' is independently selected from a divalent saturated hydrocarbon radical having 1 to 8 carbon atoms, a cycloalkylene or cycloalkylidene radical having up to and including 9 carbon atoms, 0, S, SO 2 , CO, x is 0 to 1; and (c) at least one aromatic dicarboxylic acid, in the presence of from about 10 to 60 weight percent, based on the polyarylate produced, of at least one halogenated and/or etherated substituted aromatic or neteroaromatic compound, said reaction being conducted in the absence of a catalyst for the dihydric phenol and aromatic dicarboxylic acid, and wherein the halogenated and/or etherated substituted aromatic or heteraromatic compound is of the following formulae: ##STR10## wherein X is independently Cl, LBr, F, or OR 2 , a is an integer of 1 to 5, R 1 is independently alkyl of 1 to 16 carbon atoms, cycloalkyl of 6 to 18 carbon atoms, aryl of 6 to 18 carbon atoms, or aralkyl or alkyaryl of 7 to 18 carbon atoms, R 2 is independently alkyl of 1 to 16 carbon atoms or cycloalkyl of 6 to 18 carbon atoms, A is O, S, or --CH═N--, of 0, 1, or 2, c is an integer of 0 to (8-a), d is an integer of 1 to 4, f is an integer of 0 to (4-d), with the proviso that the halogenated and/or etherified substitued aromatic compounds are free from benzylic and/or tertiary hydrogen atoms.

Claim 13

A process for preparing a polyarylate having a reduced visocsity of from about 0.5 to greater than 1.0 dl/gm, which process comprises the following steps: I. forming a polyarylate prepolymer having a reduced visocosity of from about 0.4 dl/gm, by reacting: (a) at least one diester derivative of a dihydric phenol having the following formula: ##STR11## wherein R is independently an alkyl radical having form 1 to about 6 carbon atoms, or cycloalkyl having 4 to about 7 carbon atoms, y is independently selected fom alkyl groups of 1 to 4 carbon atoms, chlorine, or bromine, z independently has a value of from 0 to 4, inclusive, and R' is independently selected from a divalent saturated aliphatic hydrocarbon radical having 1 to 8 carbon atoms, a cycloaklylene, or cycloalkylidene radical having up to and including 9 carbon atoms, O, S, SO, SO 2 , CO, x is 0 or 1; with (b) at least one aromatic dicarboxylic acid, in the presence of from about 10 to about 60 weight percent, based on the polyarylate produced, of at least one halogenated and/or etherated substituted aromatic or heteroaromatic compound, said reaction being conducted in the absence of catalyst and wherein the halogenated and/or etherated substituted aromatic or neteroaromatic compound is of the following formulae: ##STR12## wherein X is independentyl Cl, Br, F, or OR 2 , a is an integer of 1 to 5, R 1 is independently alkyl of 1 to 16 carbon atoms, cyclolkyl of 6 to 18 carbon atoms, aryl of 6 to 18 carbon atoms, or araklyl or alkaryl of 7 to 18 carbon atoms, R 2 is independently alkyl of 1 to 16 carbon atoms or cycloalkyl of 6 to 18 carbon atoms, A is O, S, or --CH═N--, b is an integer of 0, 1, or 2, c is an integer of 0 to (8-a), d is an integer of 1 to 4, and f is an integer of 0 to (4-d), with the proviso that the halogenated and/or etherified substituted aromatic compounds are free from benzylic and/or tertiary hydrogen atoms; II. Heating the prepolymer so formed at a temperature of from about 300° to 350° C. for a period of time sufficient to form a polyarylate having a reduced viscosity of from about 0.5 to greater than 1.0 dl/g.

Claim 14

A process for preparing a polyarylate having a reduced visocsity of from about 0.5 to greater than 1.0 dl/gm, which process comprises the following steps: I. forming a polyarylate prepolymer having a reduced visocosity of from about 0.4 dl/gm, by reacting: (a) at least one diester derivative of a dihydric phenol having the following formula: ##STR11## wherein R is independently an alkyl radical having form 1 to about 6 carbon atoms, or cycloalkyl having 4 to about 7 carbon atoms, y is independently selected fom alkyl groups of 1 to 4 carbon atoms, chlorine, or bromine, z independently has a value of from 0 to 4, inclusive, and R' is independently selected from a divalent saturated aliphatic hydrocarbon radical having 1 to 8 carbon atoms, a cycloaklylene, or cycloalkylidene radical having up to and including 9 carbon atoms, O, S, SO, SO 2 , CO, x is 0 or 1; with (b) at least one aromatic dicarboxylic acid, in the presence of from about 10 to about 60 weight percent, based on the polyarylate produced, of at least one halogenated and/or etherated substituted aromatic or heteroaromatic compound, said reaction being conducted in the absence of catalyst and wherein the halogenated and/or etherated substituted aromatic or neteroaromatic compound is of the following formulae: ##STR12## wherein X is independentyl Cl, Br, F, or OR 2 , a is an integer of 1 to 5, R 1 is independently alkyl of 1 to 16 carbon atoms, cyclolkyl of 6 to 18 carbon atoms, aryl of 6 to 18 carbon atoms, or araklyl or alkaryl of 7 to 18 carbon atoms, R 2 is independently alkyl of 1 to 16 carbon atoms or cycloalkyl of 6 to 18 carbon atoms, A is O, S, or --CH═N--, b is an integer of 0, 1, or 2, c is an integer of 0 to (8-a), d is an integer of 1 to 4, and f is an integer of 0 to (4-d), with the proviso that the halogenated and/or etherified substituted aromatic compounds are free from benzylic and/or tertiary hydrogen atoms; II. Heating the prepolymer so formed at a temperature of from about 300° to 350° C. for a period of time sufficient to form a polyarylate having a reduced viscosity of from about 0.5 to greater than 1.0 dl/g.

Claim 15

A process as defined in claim 11 wherein the prepolymer is heated in step (II) in a vented extruder under vacuum.