Method of making a non-linear voltage-dependent resistor
Assignee: Meidensha Corp
•
Filing: 1981-03-18
•
Granted: 1983-02-15
•
Expires: 2001-03-18
Abstract
Abstract There is provided a method of making a non-linear voltage-dependent resistor containing a ZnO element including zinc oxide as its major component by forming or coating a layer of high insulation material on the element. The layer is formed due to a vapor-solid reaction in the atmosphere of a vaporizable molecular compound containing Sb 2 O 3 , Bi 2 O 4 or SiO 2 at a sintering temperature. Preferably, the layer is formed due to a vapor-solid reaction in the atmosphere of a vaporization retarding compound containing ZnO, or SiO 2 in addition to the vaporizable molecular compound at a sintering temperature within a sintering vessel.
Inventors
- 👤 Nobuyuki Yoshioka
- 👤 Tsutai Suzuki
- 👤 Masanori Haba
- 👤 Hideo Koyama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 20:30
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C04B41/45; C04B41/50; C04B41/5025; C04B41/80; C04B41/81; C04B41/85; C04B41/87; H; H01; H01C; H01C7/00; H01C7/10; H01C7/102; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49082
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
57 words
A method of making a non-linear voltage-dependent resistor containing a ZnO element including zinc oxide as its major component wherein the improvement comprises the step of forming a layer comprised of high insulating material due to a vapor-solid reaction in an atmosphere of a vaporizable molecular compound which reacts with the zinc oxide at a sintering temperature.
Claim 2
Independent Claim
57 words
A method of making a non-linear voltage-dependent resistor containing a ZnO element including zinc oxide as its major component wherein the improvement comprises the step of forming a layer comprised of high insulating material due to a vapor-solid reaction in an atmosphere of a vaporizable molecular compound which reacts with the zinc oxide at a sintering temperature.
Claim 3
Dependent Claim
22 words
A method of making a non-linear voltage-dependent resistor as defined in claim 1, wherein said vaporizable molecular compound contains an antimony oxide.
Claim 4
Dependent Claim
26 words
A method of making a non-linear voltage-dependent resistor as defined in claim 1, wherein said vaporizable molecular compound contains an antimony oxide and a bismuth oxide.
Claim 5
Dependent Claim
29 words
A method of making a non-linear voltage-dependent resistor as defined in claim 1, wherein said vaporizable molecular compound contains an antimony oxide, a bismuth oxide, and a silicon oxide.
Claim 6
Independent Claim
69 words
A method of making a non-linear voltage-dependent resistor containing a ZnO element including zinc oxide as its major component the improvement wherein; the method comprises the steps of arranging a vaporisable molecular compound which reacts with said zinc oxide at a sintering temperature within a sintering vessel, and forming a layer comprised of high insulation material due to a vapor-solid reaction in an atmosphere of said vaporizable molecular compound.
Claim 7
Independent Claim
69 words
A method of making a non-linear voltage-dependent resistor containing a ZnO element including zinc oxide as its major component the improvement wherein; the method comprises the steps of arranging a vaporisable molecular compound which reacts with said zinc oxide at a sintering temperature within a sintering vessel, and forming a layer comprised of high insulation material due to a vapor-solid reaction in an atmosphere of said vaporizable molecular compound.
Claim 8
Independent Claim
84 words
A method of making a non-linear voltage dependent resistor containing a ZnO element including zinc oxide as its major component the improvement wherein; the method comprises the steps of mounting the ZnO element within a sintering vessel in which a vaporizable molecular compound is formed, maintaining the temperature within said sintering vessel at a predetermined range to produce an atmosphere of the antimony oxide, and sintering the ZnO element in the atmosphere of said vaporizable molecular compound thereby to form an electrically insulating layer.
Claim 9
Independent Claim
84 words
A method of making a non-linear voltage dependent resistor containing a ZnO element including zinc oxide as its major component the improvement wherein; the method comprises the steps of mounting the ZnO element within a sintering vessel in which a vaporizable molecular compound is formed, maintaining the temperature within said sintering vessel at a predetermined range to produce an atmosphere of the antimony oxide, and sintering the ZnO element in the atmosphere of said vaporizable molecular compound thereby to form an electrically insulating layer.
Claim 10
Dependent Claim
22 words
A method of making a non-linear voltage-dependent resistor as defined in claim 6, wherein said vaporizable molecular compound contains an antimony oxide.
Claim 11
Dependent Claim
26 words
A method of making a non-linear voltage-dependent resistor as defined in claim 6, wherein said vaporizable molecular compound contains an antimony oxide and a bismuth oxide.
Claim 12
Dependent Claim
29 words
A method of making a non-linear voltage-dependent resistor as defined in claim 6, wherein said vaporizable molecular compound contains an antimony oxide, a bismuth oxide, and a silicon oxide.
Claim 13
Independent Claim
85 words
A method of making a non-linear voltage-dependent resistor containing a ZnO element including zinc oxide as its major component the improvement wherein; the method comprises the steps of (a) arranging a vaporizable molecular compound which reacts with the zinc oxide and a vaporization retarding compound for retarding a vaporization of said vaporizable molecular compound at a sintering temperature within a sintering vessel, and (b) forming a layer comprised of high insulation meterial due to a vapor-solid reaction in an atmosphere of said vaporizable molecular compound.
Claim 14
Independent Claim
85 words
A method of making a non-linear voltage-dependent resistor containing a ZnO element including zinc oxide as its major component the improvement wherein; the method comprises the steps of (a) arranging a vaporizable molecular compound which reacts with the zinc oxide and a vaporization retarding compound for retarding a vaporization of said vaporizable molecular compound at a sintering temperature within a sintering vessel, and (b) forming a layer comprised of high insulation meterial due to a vapor-solid reaction in an atmosphere of said vaporizable molecular compound.
Claim 15
Dependent Claim
23 words
A method of making a non-linear voltage dependent resistor as defined in claim 10, wherein said vaporization retarding compound contains a zinc oxide.
Claim 16
Dependent Claim
27 words
A method of making a non-linear voltage dependent resistor as defined in claim 10, wherein said vaporization retarding compound contains a zinc oxide and a silicon oxide.
Claim 17
Independent Claim
98 words
A method of making a non-linear voltage dependent resistor formed of a bulk element comprising zinc oxide as its major part and as additives at least one of an antimony oxide, a bismuth oxide, and a silicon oxide, the improvement wherein the method comprises the steps of: (a) placing the bulk in an atmosphere of a gaseous molecular compound comprising an antimony oxide, and (b) forming an electrical insulating layer on the side surface of the bulk due to a chemical reaction between the gaseous phase of said molecular compound and a solid phase of the bulk element.
Claim 18
Independent Claim
98 words
A method of making a non-linear voltage dependent resistor formed of a bulk element comprising zinc oxide as its major part and as additives at least one of an antimony oxide, a bismuth oxide, and a silicon oxide, the improvement wherein the method comprises the steps of: (a) placing the bulk in an atmosphere of a gaseous molecular compound comprising an antimony oxide, and (b) forming an electrical insulating layer on the side surface of the bulk due to a chemical reaction between the gaseous phase of said molecular compound and a solid phase of the bulk element.
Claim 19
Dependent Claim
33 words
A method of making a non-linear voltage dependent resistor as defined in claim 13, further comprising the step of heating said molecular compound of an antimony oxide to a temperature above 1,000° C.
Claim 20
Dependent Claim
44 words
A method of making a non-linear voltage dependent resistor as defined in claim 13 wherein said bulk is formed by pressing a mixture consisting of a powdered zinc oxide and at least one of an antimony oxide, a bismuth oxide, and a silicon oxide.
Claim 21
Dependent Claim
34 words
A method of making a non-linear voltage dependent resistor as defined in claim 13 wherein said forming step comprises the step of sintering said bulk element in the atmosphere of said gaseous molecular compound.
Claim 22
Dependent Claim
45 words
A method of making a non-linear voltage dependent resistor as defined in claim 16 wherein said placing step further comprises the step of placing said bulk element in a sintering vessel having a support for said bulk element formed of a mixture including zinc oxide.
Claim 23
Dependent Claim
40 words
A method of making a non-linear voltage dependent resistor as defined in claim 17 wherein said support formed of a zinc oxide mixture comprises a granulated powder disposed between said bulk element and a base member of said sintering vessel.
Claim 24
Independent Claim
44 words
A method of making a non-linear voltage dependent resistor as defined in claims 17 or 18 wherein said sintering vessel includes a seating member formed of zinc oxide for preventing the formation of an insulating coating on a top surface of said bulk element.
Claim 25
Dependent Claim
120 words
A method of making a non-linear voltage dependent resistor as defined in claim 13 wherein said placing step comprises the steps of placing said bulk element in a sintering vessel having a support for said bulk element in an inner surface disposed therein and spaced apart from the side surface of said bulk element, coating at least a portion of said inner surface within said sintering vessel with a coating agent comprising at least one of antimony oxide, bismuth oxide, and silicon oxide for forming the side surface insulating layer, and heating said sintering vessel and said bulk element to a predetermined temperature range for forming said atmosphere of at least one of antimony oxide, bismuth oxide and silica oxide.
Claim 26
Dependent Claim
56 words
A method of making a non-linear voltage dependent resistor as defined in claim 20 wherein said placing step further comprises the step of placing a detachable auxiliary member, having said inner surface coated by said coating agent formed as a part thereof, in said sintering vessel thereby protecting said sintering vessel from deterioration and heat deformation.
Claim 27
Dependent Claim
93 words
A method of making a non-linear voltage dependent resistor as defined in claim 20 wherein said heating step comprises the steps of: sintering said bulk element by heating the bulk element to a temperature selected to be below a predetermined temperature at which said reaction between the gaseous phase of said molecular compound and a solid phase of the bulk elements starts, thereby shrinking said bulk element, and thereafter heating the bulk element at the predetermined temperature and for a time sufficient to maintain the vapor and solid phase reaction in said atmosphere.
Claim 28
Dependent Claim
38 words
A method of making a non-linear voltage dependent resister as defined in claim 13 wherein said forming step comprises the step of reacting the gaseous phase of said molecular compound with a solid phase of said bulk element.
References Cited (Backward Citations)
US4031498A
Cited
US4060661A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-02-14 | 1986-08-16 | 1987-02-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-02-14 | 1990-08-16 | 1991-02-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-02-14 | 1994-08-16 | 1995-02-15 | $7700.00 | Window Closed / Lapsed |