Process and composition for use in recycling of old asphalt pavements

Claim 2

An asphalt base stock for use in recycling old asphalt pavements into new pavements, said asphalt base stock having the following physical properties. (1) a penetration in the range of from about 10 to about 50 measured at 77° F., (2) a softening point below about 160° F., (3) a ductility in excess of three times the penetration, in centimeters at 77° F. when pulled at the rate of 5 centimeter per minute, wherein said asphalt base stock comprises, (1) an asphalt pitch having a penetration of less than about 25 and a softening point in the approximate range of 185° F. minus three times the penetration and (2) an asphalt cement having a penetration between about 60 and about 300.

Claim 3

An asphalt base stock in accordance with claim 1, wherein the asphalt pitch has a penetration of less than about 10 and a ductility less than about 10.

Claim 4

An asphalt base stock in accordance with claim 1, wherein the amount of asphalt pitch is in the range of from about 5% to about 40% by weight of said asphalt base stock.

Claim 5

An asphalt base stock in accordance with claim 1 wherein said asphalt base stock has a softening point in the range of from about 130° F. to about 160° F.

Claim 6

An emulsion comprising the asphalt base stock of claim 1 and water, wherein the water is in the continuous phase.

Claim 7

The emulsion in accordance with claim 5 wherein the water content is a minimum of about 35% by weight of the weight of the emulsion.

Claim 8

A pavement material comprising the emulsion of claim 5 and crushed old asphaltic pavement.

Claim 9

Pavement material in accordance with claim 7, wherein the amount of emulsion to said old pavement is in the range of from about 2.5% to about 15% by weight.

Claim 10

Pavement material in accordance with claim 7 wherein the amount of asphalt base stock is in the range of from about 1.5% to about 10% by weight of said old pavement.

Claim 11

Process for the recycling of old asphalt pavements into new pavements comprising the steps of, (1) admixing an asphalt pitch and an asphalt cement to form an asphalt base stock having (a) a penetration in the range of from about 10 to about 50 measured at 77° F., and (b) a softening point of less than about 160° F. and (c) a ductility in centimeters in excess of three times the penetration in centimeters at 77° F. when pulled at the rate of 5 centimeter per minute (2) emulsifying said asphalt base stock with water to form an asphalt emulsion (3) admixing the asphalt emulsion with an aggregate type of material comprising crushed old asphaltic pavement to form a pavement material (4) laying and compacting said pavement material of step 3 as a pavement course.

Claim 12

Process for the recycling of old asphalt pavements into new pavements comprising the steps of, (1) admixing an asphalt pitch and an asphalt cement to form an asphalt base stock having (a) a penetration in the range of from about 10 to about 50 measured at 77° F., and (b) a softening point of less than about 160° F. and (c) a ductility in centimeters in excess of three times the penetration in centimeters at 77° F. when pulled at the rate of 5 centimeter per minute (2) emulsifying said asphalt base stock with water to form an asphalt emulsion (3) admixing the asphalt emulsion with an aggregate type of material comprising crushed old asphaltic pavement to form a pavement material (4) laying and compacting said pavement material of step 3 as a pavement course.

Claim 13

Process in accordance with claim 10 comprising the additional step of, (5) allowing the water to leave said pavement course thereby binding said asphalt base stock and said aggregate type of material.

Claim 14

Process in accordance with claim 10, wherein the asphalt pitch has a penetration of less than about 25 and a softening point in the approximate range of 185° F. minus three times the penetration.

Claim 15

Process in accordance with claim 10, wherein the asphalt pitch has a penetration of less than about 10 and a ductility less than about 10.

Claim 16

Process in accordance with claim 10, wherein the amount of asphalt pitch is in the range of from about 5% to about 40% by weight of said asphalt base stock.

Claim 17

Process in accordance with claim 10, wherein the asphalt base stock has a softening point in the range of from about 130° F. to about 160° F.

Claim 18

Process in accordance with claim 10, wherein the amount of emulsion to said old asphaltic pavement is in the range of from about 2.5% to about 15% by weight.

Claim 19

Process in accordance with claim 10, wherein the amount of asphalt base stock is the range of from about 1.5% to about 10% by weight of said old asphaltic pavement.

Claim 20

Process for recycling old asphalt pavements into new pavements comprising the steps of, (a) crushing said old asphalt pavement to form an aggregate comprising asphalt and mineral matter, (b) emulsifying an asphalt base stock with water to form an emulsion wherein said asphalt base stock has the following physical properties, (1) a penetration in the range of from about 10 to about 50 measured at 77° F., (2) a softening point below about 160° F., and (3) a ductility in excess of three times the penetration, in centimeters when pulled at the rate of 5 centimeters per minute, (c) admixing the aggregate of step (a) with the emulsion of step (b) to form a pavement material, and (d) laying and compacting said pavement material of step (c) as a pavement course.

Claim 21

Process for recycling old asphalt pavements into new pavements comprising the steps of, (a) crushing said old asphalt pavement to form an aggregate comprising asphalt and mineral matter, (b) emulsifying an asphalt base stock with water to form an emulsion wherein said asphalt base stock has the following physical properties, (1) a penetration in the range of from about 10 to about 50 measured at 77° F., (2) a softening point below about 160° F., and (3) a ductility in excess of three times the penetration, in centimeters when pulled at the rate of 5 centimeters per minute, (c) admixing the aggregate of step (a) with the emulsion of step (b) to form a pavement material, and (d) laying and compacting said pavement material of step (c) as a pavement course.

Claim 22

Process in accordance with claim 18 comprising the additional step of, (e) allowing the water to leave said pavement course thereby binding said asphalt base stock and said aggregate.

Claim 23

Process in accordance with claim 18 wherein new mineral aggregate material is added prior to step (d).

Claim 24

Process for recycling old asphalt pavements comprising the steps of, (a) crushing said old asphalt pavement to form an aggregate comprising asphalt and mineral matter, (b) emulsifying an asphalt base stock with water to form an emulsion which said asphalt base stock has the following physical properties, (1) a penetration in the range of from about 10 to about 50 measured at 77° F., (2) a softening point below about 160° F., and (3) a ductility in excess of three times the penetration, in centimeters when pulled at the rate of 5 centimeters per minute, and (c) admixing the aggregate of step (a) with the emulsion of step (b) to form a pavement material, (d) laying and compacting said pavement material of step (c) as a pavement course wherein said new asphalt base stock substantially unalters the physical characteristics of the asphalt in said aggregate.

Claim 25

Process for recycling old asphalt pavements comprising the steps of, (a) crushing said old asphalt pavement to form an aggregate comprising asphalt and mineral matter, (b) emulsifying an asphalt base stock with water to form an emulsion which said asphalt base stock has the following physical properties, (1) a penetration in the range of from about 10 to about 50 measured at 77° F., (2) a softening point below about 160° F., and (3) a ductility in excess of three times the penetration, in centimeters when pulled at the rate of 5 centimeters per minute, and (c) admixing the aggregate of step (a) with the emulsion of step (b) to form a pavement material, (d) laying and compacting said pavement material of step (c) as a pavement course wherein said new asphalt base stock substantially unalters the physical characteristics of the asphalt in said aggregate.

Claim 26

Process in accordance with claim 21 wherein new mineral aggregate material is added prior to step (d).

Claim 27

Process in accordance with claim 21 comprising the additional step of (e) allowing the water to leave said pavement course thereby binding said asphalt base stock and said aggregate.

Claim 28

Process in accordance with claim 21 wherein the penetration of the asphalt in step (b) is selected to a degree of hardness within the range of penetration between about 10 and about 50, measured at 77° F., to obtain the effect of substantially unaltering the physical characteristics of the old asphalt in said aggregate.