Hot corrosion resistant coatings
Assignee: RTX Corp
•
Filing: 1982-02-01
•
Granted: 1983-02-01
•
Expires: 2002-02-01
Abstract
Abstract A coated article and method for producing the coated article are described. The article is provided with a coating system which provides protection against hot corrosion at moderate temperatures (1200-1700° F.). An overlay coating based on a metal selected from the group consisting of iron, nickel or cobalt or mixtures thereof and containing chromium and optionally aluminum, yttrium and/or hafnium is applied to the article to be protected. A silicon rich surface zone is produced at the surface of the overlay coating. Methods including pack cementation and physical vapor deposition are described for producing the coating.
Inventors
- 👤 Joseph A. Goebel
- 👤 Richard H. Barkalow
- 👤 Nicholas E. Ulion
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 21:14
CPC Classifications
F; F02; F02C; F02C7/00; F02C7/30; C; C23; C23C; C23C28/00; C23C28/02; C23C28/023
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
93 words
A method for providing a superalloy article with enhanced resistance to hot corrosion including the steps of: a. providing the article with an overlay coating of a material selected from the group consisting of MCr, MCrAl, MCrAlY and MCrAlHf, where "M" is selected from the group consisting of Fe, Ni, Co, and mixtures thereof: b. diffusing silicon into the overlay coating surface to produce a silicon rich surface zone having a thickness of from about 10 to about 40% of the total coating thickness which contains from about 20 to about 40% Si.
Claim 2
Independent Claim
93 words
A method for providing a superalloy article with enhanced resistance to hot corrosion including the steps of: a. providing the article with an overlay coating of a material selected from the group consisting of MCr, MCrAl, MCrAlY and MCrAlHf, where "M" is selected from the group consisting of Fe, Ni, Co, and mixtures thereof: b. diffusing silicon into the overlay coating surface to produce a silicon rich surface zone having a thickness of from about 10 to about 40% of the total coating thickness which contains from about 20 to about 40% Si.
Claim 3
Dependent Claim
17 words
A method as in claim 1 wherein the silicon rich surface layer is produced by pack cementation.
Claim 4
Dependent Claim
18 words
A method as in claim 1 wherein the silicon rich surface layer is produced by physical vapor deposition.
Claim 5
Independent Claim
123 words
A method for providing a superalloy article with enhanced resistance to hot corrosion including the steps of: a. providing the article with an overlay coating of material selected from the group consisting of MCr, MCrAl, MCrAlY and MCrAlHf, where "M" is selected from the group consisting of Fe, Ni, Co and mixtures thereof: b. applying a second overlay coating over the first overlay coating, with the second overlay coating having a thickness of from about 10 to about 40% of the total coating thickness, with the second overlay coating containing from greater than 10 to about 50% Si, with the balance of the overlay composition being similar to a material selected from the group consisting of the MCr, MCrAl, MCrAlY and MCrAlHf coatings.
Claim 6
Independent Claim
123 words
A method for providing a superalloy article with enhanced resistance to hot corrosion including the steps of: a. providing the article with an overlay coating of material selected from the group consisting of MCr, MCrAl, MCrAlY and MCrAlHf, where "M" is selected from the group consisting of Fe, Ni, Co and mixtures thereof: b. applying a second overlay coating over the first overlay coating, with the second overlay coating having a thickness of from about 10 to about 40% of the total coating thickness, with the second overlay coating containing from greater than 10 to about 50% Si, with the balance of the overlay composition being similar to a material selected from the group consisting of the MCr, MCrAl, MCrAlY and MCrAlHf coatings.
References Cited (Backward Citations)
EP0007675A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-01-31 | 1986-08-02 | 1987-02-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-01-31 | 1990-08-02 | 1991-02-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-01-31 | 1994-08-02 | 1995-02-01 | $7700.00 | Window Closed / Lapsed |