Process for the thermal stabilization of acrylic fibers
Assignee: SUBJECT TO AGREEMENT RECITED SEE DOCUMENT FOR DETAILS
•
Filing: 1981-05-18
•
Granted: 1983-01-25
•
Expires: 2001-05-18
Abstract
Abstract An improved process is provided whereby acrylic fibers are thermally stabilized (i.e., rendered black in appearance and non-burning when subjected to an ordinary match flame). The acrylic fibrous material, while present in an oxygen-containing atmosphere, is subjected to the intermittent irradiation of a laser beam which surprisingly has been found to expedite the desired thermal stabilization when compared to commonly employed processes which transfer heat to the acrylic fibers primarily by the convective flow of a heated gas (e.g., air) while the acrylic fibers are suspended in a hot gas oven. In a preferred embodiment the laser beam is produced by the use of a CO 2 infrared laser.
Inventors
- 👤 Shu M. Lee
- 👤 Donald M. Gezovich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 20:03
CPC Classifications
D; D01; D01F; D01F9/00; D01F9/08; D01F9/12; D01F9/14; D01F9/20; D01F9/21; D01F9/22; D01F9/225
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
114 words
In a process for the thermal stabilization of an acrylic fibrous material selected from the group consisting of an acrylonitrile homopolymer and an acrylonitrile copolymer containing at least 85 mole percent acrylonitrile units and up to 15 mole percent of one or more monovinyl units copolymerized therewith wherein said acrylic fibrous material is heated in an oxygen-containing atmosphere while retaining the original fibrous configuration substantially intact and said acrylic fibrous material is rendered black in appearance and non-burning when subjected to an ordinary match flame; the improvement of accomplishing at least a portion of the heating of said acrylic fibrous material by the intermittent irradiation of said acrylic fibrous material with a laser beam.
Claim 2
Dependent Claim
114 words
In a process for the thermal stabilization of an acrylic fibrous material selected from the group consisting of an acrylonitrile homopolymer and an acrylonitrile copolymer containing at least 85 mole percent acrylonitrile units and up to 15 mole percent of one or more monovinyl units copolymerized therewith wherein said acrylic fibrous material is heated in an oxygen-containing atmosphere while retaining the original fibrous configuration substantially intact and said acrylic fibrous material is rendered black in appearance and non-burning when subjected to an ordinary match flame; the improvement of accomplishing at least a portion of the heating of said acrylic fibrous material by the intermittent irradiation of said acrylic fibrous material with a laser beam.
Claim 3
Dependent Claim
57 words
A process for the thermal stabilization of an acrylic fibrous material according to claim 1 wherein said acrylic fibrous material is selected from the group consisting of an acrylonitrile homopolymer and an acrylonitrile copolymer containing at least 95 mole percent of acrylonitrile units and up to 5 mole percent of one or more monovinyl units copolymerized therewith.
Claim 4
Dependent Claim
29 words
A process for the thermal stabilization of an acrylic fibrous material according to claim 1 wherein said acrylic fibrous material is provided as a continuous length of multifilamentary material.
Claim 5
Dependent Claim
45 words
A process for the thermal stabilization of an acrylic fibrous material according to claim 1 wherein said acrylic fibrous material is heated to a time average temperature determined by optical pyrometry of approximately 200° to 250° C. while being intermittently irradiated with said laser beam.
Claim 6
Dependent Claim
31 words
A process for the thermal stabilization of an acrylic fibrous material according to claim 1 wherein said intermittent irradiation with a laser beam is produced by a CO 2 infrared laser.
Claim 7
Dependent Claim
26 words
A process for the thermal stabilization of an acrylic fibrous material according to claim 1 wherein said intermittent irradiation is produced by pulsing said laser beam.
Claim 8
Dependent Claim
34 words
A process for the thermal stabilization of an acrylic fibrous material according to claim 1 wherein said intermittent irradiation is produced by the relative movement of said laser beam and said acrylic fibrous material.
Claim 9
Dependent Claim
36 words
A process for the thermal stabilization of an acrylic fibrous material according to claim 1 wherein said heating of said acrylic fibrous material above ambient temperature is accomplished solely by intermittent irradiation with a laser beam.
Claim 10
Dependent Claim
134 words
In a process for the thermal stabilization of an acrylic fibrous material selected from the group consisting of an acrylonitrile homopolymer and an acrylonitrile copolymer containing at least 95 mole percent acrylonitrile units and up to 5 mole percent of one or more monovinyl units copolymerized therewith wherein said acrylic fibrous material is heated in an oxygen-containing atmosphere while retaining the original fibrous configuration substantially intact and said acrylic fibrous material is rendered black in appearance and non-burning when subjected to an ordinary match flame; the improvement of accomplishing the heating of said acrylic fibrous material by the intermittent irradiation of said acrylic fibrous material with a CO 2 infrared laser beam whereby said acrylic fibrous material is heated to a time average temperature determined by optical pyrometry of approximately 200° to 250° C.
Claim 11
Dependent Claim
134 words
In a process for the thermal stabilization of an acrylic fibrous material selected from the group consisting of an acrylonitrile homopolymer and an acrylonitrile copolymer containing at least 95 mole percent acrylonitrile units and up to 5 mole percent of one or more monovinyl units copolymerized therewith wherein said acrylic fibrous material is heated in an oxygen-containing atmosphere while retaining the original fibrous configuration substantially intact and said acrylic fibrous material is rendered black in appearance and non-burning when subjected to an ordinary match flame; the improvement of accomplishing the heating of said acrylic fibrous material by the intermittent irradiation of said acrylic fibrous material with a CO 2 infrared laser beam whereby said acrylic fibrous material is heated to a time average temperature determined by optical pyrometry of approximately 200° to 250° C.
Claim 12
Dependent Claim
29 words
A process for the thermal stabilization of an acrylic fibrous material according to claim 9 wherein said acrylic fibrous material is provided as a continuous length of multifilamentary material.
Claim 13
Dependent Claim
43 words
A process for the thermal stabilization of an acrylic fibrous material according to claim 9 wherein said continuous length of multifilamentary material is continuously passed in the direction of its length while under a constant tension through said CO 2 infrared laser beam.
Claim 14
Dependent Claim
59 words
A process for the thermal stabilization of an acrylic fibrous material according to claim 9 wherein said acrylic fibrous material possesses a denier per filament of approximately 0.5 to 1.6 prior to said thermal stabilization, and said acrylic fibrous material is subjected to said intermittent irradiation with said CO 2 infrared laser beam for approximately 5 to 20 minutes.
Claim 15
Dependent Claim
26 words
A process for the thermal stabilization of an acrylic fibrous material according to claim 9 wherein said intermittent irradiation is produced by pulsing said laser beam.
Claim 16
Dependent Claim
34 words
A process for the thermal stabilizaiton of an acrylic fibrous material according to claim 9 wherein said intermittent irradiation is produced by the relative movement of said laser beam and said acrylic fibrous material.
Claim 17
Dependent Claim
150 words
In a process for the thermal stabilization of an acrylic fibrous material having a denier per filament of approximately 0.5 to 1.6 selected from the group consisting of an acrylonitrile homopolymer and an acrylonitrile copolymer containing at least 95 mole percent acrylonitrile units and up to 5 mole percent of one or more monovinyl units copolymerized therewith wherein said acrylic fibrous material is heated in an oxygen-containing atmosphere while retaining the original fibrous configuration substantially intact and said acrylic fibrous material is rendered black in appearance and non-burning when subjected to an ordinary match flame; the improvement of accomplishing the heating of said acrylic fibrous material by the intermittent irradiation of said acrylic fibrous material for approximately 5 to 20 minutes with a CO 2 infrared laser beam whereby said acrylic fibrous material is heated to a time average temperature determined by optical pyrometry of approximately 200° to 250° C.
Claim 18
Dependent Claim
150 words
In a process for the thermal stabilization of an acrylic fibrous material having a denier per filament of approximately 0.5 to 1.6 selected from the group consisting of an acrylonitrile homopolymer and an acrylonitrile copolymer containing at least 95 mole percent acrylonitrile units and up to 5 mole percent of one or more monovinyl units copolymerized therewith wherein said acrylic fibrous material is heated in an oxygen-containing atmosphere while retaining the original fibrous configuration substantially intact and said acrylic fibrous material is rendered black in appearance and non-burning when subjected to an ordinary match flame; the improvement of accomplishing the heating of said acrylic fibrous material by the intermittent irradiation of said acrylic fibrous material for approximately 5 to 20 minutes with a CO 2 infrared laser beam whereby said acrylic fibrous material is heated to a time average temperature determined by optical pyrometry of approximately 200° to 250° C.
Claim 19
Dependent Claim
29 words
A process for the thermal stabilization of an acrylic fibrous material according to claim 15 wherein said acrylic fibrous material is provided as a continuous length of multifilamentary material.
Claim 20
Dependent Claim
40 words
A process for the thermal stabilization of an acrylic fibrous material according to claim 16 wherein said continuous length of multifilamentary material is continuously passed in the direction of its length while under a constant tension through said laser beam.
Claim 21
Dependent Claim
26 words
A process for the thermal stabilization of an acrylic fibrous material according to claim 15 wherein said intermittent irradiation is produced by pulsing said laser beam.
Claim 22
Dependent Claim
34 words
A process for the thermal stabilization of an acrylic fibrous material according to claim 15 wherein said intermittent irradiation is produced by the relative movement of said laser beam and said acrylic fibrous material.
Claim 23
Dependent Claim
32 words
A process for the thermal stabilization of an acrylic fibrous material according to claim 19 wherein said intermittent irradiation is produced by the movement of said laser beam in a Lissajous figure.
Claim 24
Dependent Claim
40 words
A process for the thermal stabilization of an acrylic fibrous material according to claim 17 wherein the resulting thermally stabilized acrylic fibrous material continuously is passed directly from the zone in which thermal stabilization is accomplished to a carbonization zone.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-01-24 | 1986-07-26 | 1987-01-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-01-24 | 1990-07-26 | 1991-01-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-01-24 | 1994-07-26 | 1995-01-25 | $7700.00 | Window Closed / Lapsed |