Method of producing clad steel articles
Assignee: Kawasaki Motors Ltd
•
Filing: 1980-08-14
•
Granted: 1983-01-11
•
Expires: 2000-08-14
Abstract
Abstract An inner stainless-steel tube having an outer frustoconical faying surface is fitted into an outer carbon-steel tube having a matching inner frustoconical faying surface, and these tubes are friction welded over their entire faying surfaces by pressing the tubes together in their axial direction to obtain a high contact pressure due to a wedge action and, at the same time, imparting rotation thereto relative to each other thereby to obtain an integrally bonded, laminated, tubular blank, which is then extended by a suitable process such as rolling into a clad steel tube. The tubular blank can also be slit in its axial direction and flattened into a laminated flat blank, which can be rolled into a clad steel plate. The inner tube may be replaced by a solid core metal. In this case, an integrally bonded blank made up of the inner core metal and the outer tube is extended into a clad steel tube or into a clad steel shape.
Inventors
- 👤 Toshio Yoshida
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 01:52
CPC Classifications
B; B23; B23K; B23K20/00; B23K20/12; B23K20/129; Y; Y10; Y10S; Y10S72/00; Y10S72/70
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
129 words
An improved method of producing clad steel articles which comprises placing a dissimilar metal material in a laminated state against a steel material, having mutual contact along respective frustoconical faying surfaces, and friction welding the metal materials by relative rotation at their faying surfaces to cause bonding of said metal materials together, the improvement comprising the steps of: forming one of the metal materials to be friction welded as an outer tube, having an inner wall surface finished to be the frustoconical faying surface thereof, forming the other metal material as an inner tube having an outer surface finished to mate with said frustoconical faying surface, producing by said friction welding a bonded metal blank an subjecting said metal blank to plastic working to produce a clad steel article.
Claim 2
Dependent Claim
129 words
An improved method of producing clad steel articles which comprises placing a dissimilar metal material in a laminated state against a steel material, having mutual contact along respective frustoconical faying surfaces, and friction welding the metal materials by relative rotation at their faying surfaces to cause bonding of said metal materials together, the improvement comprising the steps of: forming one of the metal materials to be friction welded as an outer tube, having an inner wall surface finished to be the frustoconical faying surface thereof, forming the other metal material as an inner tube having an outer surface finished to mate with said frustoconical faying surface, producing by said friction welding a bonded metal blank an subjecting said metal blank to plastic working to produce a clad steel article.
Claim 3
Dependent Claim
130 words
An improved method of producing clad steel articles which comprises, placing a dissimilar metal material in a laminated state against a steel material with mutual contact along respective frustoconical faying surfaces, and friction welding the metal materials by relative rotation at their faying surfaces to bond said materials together, the improvement comprising the steps of: forming one of the metal materials to be friction welded to the other in the form of an outer tube having an inner wall surface finished as the frusto conical faying surface thereof, forming the other metal material as a solid core having an outer surface finished to mate with said frustoconical faying surface, and producing by friction welding, a bonded metal blank and subjecting it to plastic working for producing a clad steel article.
Claim 4
Dependent Claim
130 words
An improved method of producing clad steel articles which comprises, placing a dissimilar metal material in a laminated state against a steel material with mutual contact along respective frustoconical faying surfaces, and friction welding the metal materials by relative rotation at their faying surfaces to bond said materials together, the improvement comprising the steps of: forming one of the metal materials to be friction welded to the other in the form of an outer tube having an inner wall surface finished as the frusto conical faying surface thereof, forming the other metal material as a solid core having an outer surface finished to mate with said frustoconical faying surface, and producing by friction welding, a bonded metal blank and subjecting it to plastic working for producing a clad steel article.
Claim 5
Dependent Claim
44 words
An improved method according to claim 1, comprising the steps of: forming the outer tube of the steel material, forming the inner tube of the dissimilar metal material and forming said bonded metal blank into an internally clad steel tube by the plastic working.
Claim 6
Dependent Claim
48 words
An improved method according to claim 2, comprising the steps of: forming the outer tube of the steel material, forming the solid core of the dissimilar metal material, and plastically extending the bonded metal blank by a die and a coacting mandrel into an internally clad steel tube.
Claim 7
Dependent Claim
45 words
An improved method according to either of claims 3 or 4, comprising the steps of: slitting the internally clad steel tube through its wall in the axial direction and opening same into a flat blank, and plastically extending said blank into a flat laminated plate.
Claim 8
Dependent Claim
42 words
An improved method according to claim 2, comprising the steps of: forming the outer tube of the dissimilar metal material, forming the solid core of the steel material and plastically shaping and extending the bonded metal blank into a clad steel shape.
References Cited (Backward Citations)
US3126625A
Cited
US2107943A
Cited
GB607205A
Cited
US3134278A
Cited
US3504425A
Cited
GB1234586A
Cited
US3664012A
Cited
JPS496026A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-01-10 | 1986-07-12 | 1987-01-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-01-10 | 1990-07-12 | 1991-01-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-01-10 | 1994-07-12 | 1995-01-11 | $7700.00 | Window Closed / Lapsed |