Thermoplastic polyurethane resin having isocyanate end groups and containing ethylenic side groups
Assignee: NATIONALE DESPOUDRES ET EXPLOSIFS Ste
•
Filing: 1981-04-30
•
Granted: 1983-01-04
•
Expires: 2001-04-30
Abstract
Abstract The invention relates to new crosslinkable thermoplastic polyurethane resins having isocyanate end groups and containing ethylenic side groups. According to the invention, the polyurethane resins result from the reaction of: (a) an organic diisocyanate, (b) a saturated diol and (c) an unsaturated diol of the formula: <IMAGE> in which R3=Me or H and n is an integer between 1 and 4. 2,3-Dihydroxypropyl acrylate will preferably be used. Application to glues, in particular for lamination with the aid of a two-step glueing process which consists, in a first step, in crosslinking the acrylic bonds in order to increase the tack of the film, and then in crosslinking the NCO groups.
Inventors
- 👤 Patrice M. Le Roy
- 👤 Sabine M. Journeau
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 11:22
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/67; C08G18/675; C09; C09J; C09J175/00; C09J175/04; C09J175/14
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
138 words
Thermoplastic polyurethane resin having isocyanate end groups and containing internal ethylenic side groups, useful as an adhesive, which comprises the product resulting from the reaction of: (a) an organic diisocyanate, (b) a saturated diol having a molecular weight of between 450 and 4,000 and (c) an unsaturated diol consisting of the acrylic or methacrylic acid ester of a trihydric alcohol, of the formula: ##STR4## in which R 1 and R 2 , which are identical or different, are hydrogen, a lower alkyl group, an aryl group or a halogen, R 3 is hydrogen, a lower alkyl, aryl or cycloalkyl group or a halogen and n is 1, 2, 3 or 4, the diisocyanate compound (a) being present in a ratio NCO:OH of more than 1.1 and the molar ratio diol (b):unsaturated diol (c) being between 0 and 3.
Claim 2
Dependent Claim
138 words
Thermoplastic polyurethane resin having isocyanate end groups and containing internal ethylenic side groups, useful as an adhesive, which comprises the product resulting from the reaction of: (a) an organic diisocyanate, (b) a saturated diol having a molecular weight of between 450 and 4,000 and (c) an unsaturated diol consisting of the acrylic or methacrylic acid ester of a trihydric alcohol, of the formula: ##STR4## in which R 1 and R 2 , which are identical or different, are hydrogen, a lower alkyl group, an aryl group or a halogen, R 3 is hydrogen, a lower alkyl, aryl or cycloalkyl group or a halogen and n is 1, 2, 3 or 4, the diisocyanate compound (a) being present in a ratio NCO:OH of more than 1.1 and the molar ratio diol (b):unsaturated diol (c) being between 0 and 3.
Claim 3
Dependent Claim
27 words
Polyurethane resin according to claim 1, wherein the unsaturated diol (c) has the formula: ##STR5## R 3 and n having the same meaning as in claim 1.
Claim 4
Dependent Claim
16 words
Polyurethane resin according to claim 2, wherein the unsaturated diol (c) is 2,3-dihydroxypropyl acrylate or methacrylate.
Claim 5
Dependent Claim
13 words
Polyurethane resin according to claim 1, wherein the ratio NCO:OH is about 2.
Claim 6
Dependent Claim
53 words
Crosslinkable adhesive composition, which is formed by a mixture of: A. a polyurethane resin according to one of the preceding claims and B. a reactive solvent which is a member selected from the group consisting of vinyl and acrylic monomers, the weight ratio polyurethane resin A:reactive solvent B being between 95/5 and 40/60.
Claim 7
Dependent Claim
39 words
Crosslinkable adhesive composition according to claim 5, wherein a prepolymer, having isocyanate end groups, of a saturated long-chain diol is also added, the proportion by weight of the said prepolymer to the polyurethane resin being between 0.25 and 4.
Claim 8
Dependent Claim
27 words
Crosslinkable adhesive composition according to claim 6, wherein the saturated long-chain diol of the prepolymer is the same as the long-chain diol (b) of the polyurethane resin.
Claim 9
Dependent Claim
77 words
Process for causing two substrates to adhere to one another, wherein in the first step, the first substrate is covered with a resin according to claim 1 or composition according to claim 5; the resin or composition is then crosslinked in accordance with a means of free-radical polymerisation; the second substrate is then applied; and the final product is then left for the time required for the crosslinking of the free NCO groups in the polyurethane resin.
Claim 10
Dependent Claim
18 words
The resin according to claim 1, wherein the saturated diol (b) has molecular weight between 500 and 2,500.
Claim 11
Dependent Claim
24 words
The composition according to claim 5, wherein the weight ratio of said polyurethane resin A to reactive solvent B is between 90/10 and 70/30.
Claim 12
Dependent Claim
17 words
The resin according to claim 1, wherein the diisocyanate has a molecular weight of less than 300.
Claim 13
Dependent Claim
24 words
The resin according to claim 1, wherein the diisocyanate compound (a) is present in a ratio of NCO:OH greater than or equal to 1.2.
Claim 14
Dependent Claim
22 words
The resin according to claim 1, wherein the ratio of long-chain diol (b) to the unsaturated diol is between 0.5 and 2.5.
Claim 15
Dependent Claim
51 words
The resin according to claim 1, wherein part of the unsaturated diol is replaced by a saturated chain extender, which is a member selected from the group consisting of short-chain diols, alkanolamines and diamines and the molar ratio of said chain extender to said unsaturated diol is between 0 and 10.
References Cited (Backward Citations)
FR1211430A
Cited
US3061574A
Cited
FR1366079A
Cited
FR1418816A
Cited
GB1061773A
Cited
US4195146A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-01-03 | 1986-07-05 | 1987-01-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-01-03 | 1990-07-05 | 1991-01-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-01-03 | 1994-07-05 | 1995-01-04 | $7700.00 | Window Closed / Lapsed |