Preparation of polyurethane foams modified with melamine-formaldehyde precondensates
Assignee: BASF SE
•
Filing: 1981-05-22
•
Granted: 1983-01-04
•
Expires: 2001-05-22
Abstract
Abstract A process for the preparation of polyurethane foams modified with melamine-formaldehyde precondensates, in which the precondensates employed are storage-stable, aqueous 40-85% strength by weight resin solutions which are obtained by condensing melamine with formaldehyde in a molar ratio of 1:1.1-1.75 in aqueous solution at a pH which, at least periodically, is above 8, and at from 60 to 130° C., until one part by volume of resin solution can be diluted with from 0.5 to 4 parts by volume of water at 20° C. without causing a persisting cloudiness.
Inventors
- 👤 Klaus Hahn
- 👤 Peter Horn
- 👤 Matthias Marx
- 👤 Heinz Weber
- 👤 Wolfram Weiss
- 👤 Rolf Wurmb
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 19:51
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/54; C08G18/544; C08G12/00; C08G12/02; C08G12/26; C08G12/30; C08G12/32
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
91 words
A process for the preparation of polyurethane foams by reacting organic polyisocyanates, polyols and melamine-formaldehyde precondensates in the presence of catalysts and blowing agents and in the presence or absence of chain extenders or crosslinking agents, auxiliaries and additives, wherein the melamine-formaldehyde precondensates used are aqueous resin solutions which have a melamine-formaldehyde precondensate content of 40-85% by weight, based on total weight, and which are obtained by condensing melamine with formaldehyde, in a molar ratio of 1:1.1-1.75, in aqueous solution, until the water-dilutability of the product, at 20° C., is 1:0.5-4.
Claim 2
Dependent Claim
91 words
A process for the preparation of polyurethane foams by reacting organic polyisocyanates, polyols and melamine-formaldehyde precondensates in the presence of catalysts and blowing agents and in the presence or absence of chain extenders or crosslinking agents, auxiliaries and additives, wherein the melamine-formaldehyde precondensates used are aqueous resin solutions which have a melamine-formaldehyde precondensate content of 40-85% by weight, based on total weight, and which are obtained by condensing melamine with formaldehyde, in a molar ratio of 1:1.1-1.75, in aqueous solution, until the water-dilutability of the product, at 20° C., is 1:0.5-4.
Claim 3
Dependent Claim
29 words
The process of claim 1, wherein the melamine and formaldehyde are condensed at a pH which is, at least periodically, above 8, and at from 60° to 130° C.
Claim 4
Dependent Claim
31 words
The process of claim 1, wherein a stabilizer to improve the shelf line of the melamine-formaldehyde precondensate is added before, during or after the condensation of the melamine with the formaldehyde.
Claim 5
Dependent Claim
12 words
The process of claim 1, wherein the melamine:formaldehyde molar ratio is 1:1.5-1.65.
Claim 6
Dependent Claim
13 words
The process of claim 1, wherein the organic polyisocyanates used are aromatic polyisocyanates.
Claim 7
Dependent Claim
34 words
The process of claim 1, wherein the organic polyisocyanates used are prepolymers, containing isocyanate groups, which are obtained from polyols and aromatic polyisocyanates and having NCO contents of from 3 to 35% by weight.
Claim 8
Dependent Claim
50 words
The process of claim 5, wherein the aromatic polyisocyanates used are 2,4- and 2,6-toluylene diisocyanate or a corresponding isomer mixture, 2,2'-, 2,4'- and 4,4'-diphenylmethane diisocyanate or a corresponding isomer mixture, a mixture of 2,2'-, 2,4'- and 4,4'-diphenylmethane diisocyanate and polyphenyl-polymethylene polyisocyanates or a mixture of all the aromatic polyisocyanates mentioned.
Claim 9
Dependent Claim
32 words
The process of claim 1, wherein from 1 to 50 parts by weight of polyol are used per 100 parts by weight of the aqueous 40-85% strength by weight melamine-formaldehyde precondensate solution.
Claim 10
Dependent Claim
14 words
The process of claim 1, wherein water is used as the sole blowing agent.
Claim 11
Dependent Claim
74 words
The process of claim 1, wherein the starting materials are reacted by the two-component process, using a storage-stable A-component which contains melamine-formaldehyde precondensates, water, one or more basic polyurethane catalysts, if appropriate polyols, acid condensation catalysts, physical blowing agents, chain extenders or crosslinking agents, auxiliaries and additives and which has a pH of above 7, and a B-component which contains polyisocyanates or prepolymers containing isocyanate groups, if appropriate physical blowing agents, auxiliaries and additives.
References Cited (Backward Citations)
US3135707A
Cited
US3523093A
Cited
US4122049A
Cited
US4139501A
Cited
US4246361A
Cited
US4096101A
Cited
US4130697A
Cited
US4176217A
Cited
US4260530A
Cited
US4160075A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-01-03 | 1986-07-05 | 1987-01-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-01-03 | 1990-07-05 | 1991-01-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-01-03 | 1994-07-05 | 1995-01-04 | $7700.00 | Window Closed / Lapsed |