Method for the control of excessive corrosion in phosphoric acid circuits
Assignee: JR Simplot Co
•
Filing: 1981-03-02
•
Granted: 1983-01-04
•
Expires: 2001-03-02
Abstract
Abstract Methods for control of excessive corrosion in wet process phosphoric circuits are effected by oxidation of reduced ion species in the acid with maintenance of EMF value of the acid above about 190 millivolts (S.C.E. reference) through the digestion circuit. Supplementary monitoring is by a ceric red-ox titration procedure. In one embodied form, the present invention is utilized to control corrosion in a phosphoric acid plant digestion system (and subsequent processing equipment) operating by a dihydrate (gypsum) process even when such a process employs a calcined western U.S. phosphate ore feed from a relatively highly carbonaceous ore. The invention is also applicable for treating wet process phosphoric acid in phosphoric acid plants having a digester system operating by a hemihydrate process. In a presently preferred embodiment, additions of manganese dioxide to a primary digester in a sufficient amount effective to achieve an EMF value over about 190 millivolts will significantly control the occurrence of excessive corrosion in phosphoric acid circuits. In yet another preferred embodiment, an oxygen autoclave oxidation is used to oxidize the reduced ion species present in the acid to inhibit corrosion.
Inventors
- 👤 Gary L. Long
- 👤 Roger B. Humberger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 16:42
CPC Classifications
C; C01; C01B; C01B25/00; C01B25/16; C01B25/18; C01B25/22; C01B25/222; C01B25/223; C01B25/226; C01B25/225; C23; C23F; C23F11/00; C23F11/04
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
116 words
A method of controlling excessive corrosion in phosphoric acid circuits by oxidation of reduced ion species in wet process phosphoric acid slurry, comprising the steps of: measuring the total weight percent concentration of reduced ion species in the acid slurry; measuring the total weight percent concentration of oxidized ion species in the acid slurry; comparing the ratio of the total weight percent concentration of reduced ion species to the total weight percent concentration of oxidized ion species; and oxidizing a portion of the reduced ion species in the acid slurry when the value of said ratio is greater than or equal to about 4.0 to alter the value of said ratio to less than about 4.0.
Claim 2
Independent Claim
116 words
A method of controlling excessive corrosion in phosphoric acid circuits by oxidation of reduced ion species in wet process phosphoric acid slurry, comprising the steps of: measuring the total weight percent concentration of reduced ion species in the acid slurry; measuring the total weight percent concentration of oxidized ion species in the acid slurry; comparing the ratio of the total weight percent concentration of reduced ion species to the total weight percent concentration of oxidized ion species; and oxidizing a portion of the reduced ion species in the acid slurry when the value of said ratio is greater than or equal to about 4.0 to alter the value of said ratio to less than about 4.0.
Claim 3
Dependent Claim
29 words
The method of claim 1 wherein said oxidizing step comprises adding manganese dioxide in an amount sufficient to alter the value of said ratio to less than about 4.0.
Claim 4
Dependent Claim
19 words
The method of claim 1 wherein said oxidizing step comprises oxidizing the reduced ion species in an oxygen autoclave.
Claim 5
Dependent Claim
155 words
The method of claim 1 wherein the reduced ion species comprises iron and vanadium, and wherein said steps of measuring the total weight percent concentration of reduced ion species and the total weight percent concentration of oxidized ion species in the acid slurry comprises measuring the total weight percent concentration of iron in the acid slurry, performing a potentiometric titration of a portion of the acid slurry in about 65° C. ten percent H 2 SO 4 solution with dilute ceric bisulfate titrant to determine the amount of titrant to achieve a first end point and a second end point, and wherein said comparing step comprises comparing in normalized units the ratio of the amount of titrant to achieve the first end point to the total weight percent concentration of iron less twice the amount of titrant to achieve the first end point plus the total amount of titrant to achieve the second end point.
Claim 6
Dependent Claim
151 words
The method of claim 1 wherein the reduced ion species comprises iron and vanadium, and wherein said steps of measuring the total weight percent concentration of reduced ion species and the total weight percent concentration of oxidized ion species in the acid slurry comprises measuring the total weight percent concentration of iron in the acid slurry, measuring the total weight percent concentration of vanadium in the acid slurry, performing a potentiometric titration of a portion of the acid slurry in about 65° C. ten percent H 2 SO 4 solution with dilute ceric bisulfate titrant to determine the amount of titrant to achieve a first end point, and wherein said comparing step comprises comparing in normalized units the ratio of the amount of titrant to achieve the first end point to the total weight percent concentration of iron and vanadium less the amount of titrant to achieve the first end point.
Claim 7
Dependent Claim
48 words
The method of claim 5 wherein said step of measuring the total weight percent concentration of vanadium comprises the steps of determining the amount of titrant to achieve a second end point, and determining the difference between the amounts of titrant for the first and second end points.
References Cited (Backward Citations)
US2854497A
Cited
US3027236A
Cited
US3116178A
Cited
US3649167A
Cited
US3935298A
Cited
US4101638A
Cited
SU592746A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-01-03 | 1986-07-05 | 1987-01-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-01-03 | 1990-07-05 | 1991-01-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-01-03 | 1994-07-05 | 1995-01-04 | $7700.00 | Window Closed / Lapsed |